The influence of pre- shot peening and welding parameters on mechanical and metallurgical properties of dissimilar and similar aluminum alloys AA2024-T3 and AA6061-T6 joints using friction stir welding have been studied. In this work, numbers of plates were equipped from sheet alloys in dimensions (150*50*6) mm then some of them were exposed to shot peening process before friction stir welding using steel ball having diameter 1.25 mm for period of 15 minutes. FSW joints were manufactured from plates at three welding speeds (28, 40, 56 mm/min) and welding speed 40mm/min was chosen at a rotating speed of 1400 rpm for welding the dissimilar pre- shot plates. Tow joints were made at rotational speed of 1000 rpm and welding speed of 40m/min f

This work aims to investigate the tensile and compression strengths of heat- cured acrylic resin denture base material by adding styrene-butadiene (S- B) to polymethyl methacrylate (PMMA). The most well- known issue in prosthodontic practice is fracture of a denture base. All samples were a blend of (90%, 80%) PMMA and (10%, 20%) S- B powder melted in Oxolane (Tetra hydro furan). These samples were chopped down into specimens of dimensions 100x10x2.5mm to carry out the requirements of tensile tests. The compression strength test specimens were shaped into a cylinder with dimensions of 12.7mm in diameter and 20mm in length. The experimental results show a significant increase in both tensile and compression strengths when compared to cont

In this work, nanostructure zinc sulfide (ZnS) thin films at temperature of substrate 450 oC and thickness (120) nm have been produced by chemical spray pyrolysis method. The X-Ray Diffraction (XRD) measurements of the film showed that they have a polycrystalline structure and possessed a hexagonal phase with strong crystalline orientation of (103). The grain size was measured using scanning electron microscope (SEM) which was approximately equal to 80 nm. The linear optical measurements showed that ZnS nanostructure has direct energy gap. Nonlinear optical properties experiments were performed using Q-switched 532 nm Nd:YAG laser Z-scan system. The nonlinear refractive index (n2) and nonlinear absorption coefficient (β) estimated for Z

This study was aime to investigate the effect of addition different concentration of celery leaves to white soft cheese ,Treated cheese between 2018-2019, ,The finely Celery (Apium graveolens) leaves were adding to crude white cheese after texturizing in three leveles included (A,B,C) in addition of control antimicrobial activity of celery treated cheese against total account bacteria and coliform bacteria was estimated during (0, 5, 10, 15, 20) days. The results were shown that the higher concentration of celery in treated cheese, had a lower concentration of protein, lipid and ash content ( 16.81,15.13 and 4.30% respectively, but it had a higher moisture content 59.50%.also the total bacteria counts were decreasing significantly (0.05 P)w

In this work 2-hydrazino pyrimidine (1) was prepared from 2-mercapto pyrimidine with hydrazine hydrate. Treatment of (1) with active methylene compounds gave 2-(3,5-dimethyl -1 H – Pyrazole-1-yl) pyrimidine , whereas the reaction of (1) with carboxylic anhydride namely maleic anhydride or 1,2,3,6-tetra hydro phthalic anhydride yielded 1-Pyrimidine-2-yl-1,2-dihydro pyridazine-3,6-dione (3) and 2 – Pyrimidin -2-yl -2,3,4 a ,5,8 a – hexahydro phthalazine 1,4 – dione (4) . Reaction of (1) with phenyl isothiocyanate and ethyl chloro acetate afforded 3-Phenyl-1,3-thiazolidine-2,4-dione-2( pyrimidine -2- yl hydrazone (6) Azomethine (7-10) were prepared through condensation of (1) with aromatic aldehydes or ketones, then comp

In this work the production of activated carbon (AC) from Imperata is done by microwave assisted Potassium hydroxide (KOH) activation and using this activated carbon for the purpose of the uptake of amoxicillin (AMX) by adsorption process from aqueous solution. The effects for irradiation power (450-800W), irradiation time (6-12min) as well as impregnation ratio (0.5-1 g/g) on the AMX uptake and yield AMX uptake at an initial concentration of AMX (150 mg/g). The optimum conditions were 700 W irradiation power, 10 min time of irradiation, as well as 0.8 g/g impregnation ratio with 14.821% yield and 12.456 mg/g AMX uptake. Total volume of hole and the area of the surface (BET) are 0.3027 m³/g, and 552.7638 m²/g respectively. The properti

Between October and December 2018, 27wounds and burn swab specimens were collected by laboratories at Al-Yarmook hospital, and cultured on Mannitol salt agar. the isolate was subjected to Nd: YAG laser in different power (400mJ, 500mJ, 800mJ and 900mJ). In general the laser showed effect on bacterial growth that reach to complete killing, the statistical analysis showed that there is weak correlation between laser at 400mJ with killed percentage. While in 500mJ its exhibit complete correlation with killing percentage, this correlation was decreased with increasing in power to 800mJ and 900Mj.