The Silver¹Indium¹Selenide (AgInSe₂) (AIS) thin¹films of (300¹Â±20) nm thickness  have been¹prepared²from the compound alloys²using thermal evaporation² technique onto the glass²substrate at room temperature, with a deposition rate²(3±0.1) nm²sec^-1.

The²structural, optical and electrical³properties have been studied³at different annealing³temperatures (Ta=450, 550 and 650) K.

The amount³or (concentration) of the elements³(Ag, In, Se) in the  prepared alloy³was verified using  an

  The study focused on the results of first paleostress from thrust fault slip data on Tertiary age of Hemrin North Structure, North of Iraq. The stress inversion was performed for fault slip data using an improved right dihedral model, and then followed by rotational optimization (Georient Software). The trend of the principal stress axes (σ1, σ2 and σ3) and the ratio of the principal stress differences (R) show the main paleostress field is NE-SW compression regime. As well as using Lisle graph and Mohr diagram to determine the magnitudes of palestress.  The values paleostress of the study area were σ1=1430 bars, σ2=632 bars and σ3=166 bar. The large magnitudes of the primary stress axes could be attributed to active tecto

Tin Oxide (SnO2) films have been deposited by spray pyrolysis technique at different substrate temperatures. The effects of substrate temperature on the structural, optical and electrical properties of SnO2 films have been investigated. The XRD result shows a polycrystalline structure for SnO2 films at substrate temperature of 673K. The thickness of the deposited film was of the order of 200 nm measured by Toulansky method. The energy gap increases from 2.58eV to 3.59 eV when substrate temperature increases from 473K to 673K .Electrical conductivity is 4.8*10-7(.cm)-1 for sample deposited at 473K while it increases to 8.7*10-3 when the film is deposited at 673K

Fe3O4:Ce thin films were deposited on glass and Si substrates by Pulse Laser Deposition Technique (PLD). Polycrystalline nature of the cubic structure with the preferred orientation of (311) are proved by X-ray diffraction. The nano size of the prepared films are revealed by SEM measurement. Undoped Iron oxide and doped with different concentration of Ce films have direct allowed transition band gap with 2.15±0.1 eV which is confirmed by PL Photoluminescence measurements. The PL spectra consist of the emission band located at two sets of peaks, set (A) at 579±2 nm , and set (B) at 650 nm, respectively when it is excited at an excitation wavelength of 280 nm at room temperature. I-V characteristics have been studied in the dark and under v

The vortex rate sensor is a fluidic gyroscope with no moving parts and can be used in very difficult conditions like radiation, high temperature and noise with minimum cost of manufacturing and maintenance. A vortex rate sensor made of wood has been designed and manufactured to study theoretically and experimentally its static performance .A rig has been built to carry out the study,
the test carried out with three different air flow rates (100, 150, and 200 l/min).The results show that the relation between the differential pressure taken from the sensor pickoff points and the angular velocity of the sensor was linear.The present work involved theoretical and experimental study of vortex rate sensor static characteristics .Vortex rat

Corrosion inhibiting admixtures are unique among other methods to protect reinforced concrete from corrosion damage. In this study, the effect of furfural on the fresh and hardened properties of concrete mixes of 35 and 45 MPa compressive strengths as well as the corrosion inhibition of furfural was evaluated. Furfural was added at different dosages (1, 2 and 3% by weight of cement) with and without superplasticizer (HRWR). Different electrochemical measurements were performed (Half-cell potential, Tafel plot and linear polarization resistance). Electrochemical measurements confirmed that furfural dramatically reduces the rate of corrosion; the inhibition efficiencies were 62.7 and 63.8 % due to 3% furfural addition to 35 and 45MPa-concr

The   electrical     properties   of   thin   film    interdigital    metal­

phthalocyanine - metal devices have been studied with regard to purity and electrode material . Devices utilising phthalocyanines ( H2 Pc ,

NiPc and CuPc) films with Au, Ag , Cu ' In and AI electrodes have been prepared with Pc layers fabricated  from  both as - supplied  Pc powder and entrainer - subeimed  material . The results indicate that

sublimed phthalocyanine with gold electrodes offers the best material

combination with regard to linearity , reversibility and reproducibility. Measurements  of  current &nbs