Hydrothermal process method using different dimensions reactors with volume 100 ml (homemade) was employed to prepare titanium sub-oxide Ti₆O₁₁, where  one gram of TiO₂ nanoparticles 30-50 nm and 3M (20 ml) of NaOH as suspension was used . The samples are characterized using X-ray diffraction, Raman spectroscopy, and Field Emission Scanning Electron Microscopy (FE-SEM). X-ray diffraction revealed the formation of sub- oxide titanium Ti₆O₁₁ of triclinic structure with Magneli phase, when the temperature applied was 363K for 9h.While FE-SEM showed uniform hierarchical structures with planar grass-like shapes. A novel phase has been found from rutile titanium.

Objectives: The study aims to evaluate the application of monitoring indicators for maternal, newborn and
child health through the evaluation of impact and coverage health indicators and to evaluate the usefulness of the
application of these indicators at sub primary health care centers in Baghdad City.
Methodology: A descriptive comparative design, which is using the evaluation approach, has been steered at
Sub Primary Health Centers of Baghdad City in order to evaluate the application; impact and coverage, and the
usefulness of monitoring indicators for maternal, newborn and child health from December 4th 2017 to April 29th
2018. A multistage, "non-probability" convenient, sample is selected for the present study. A t

     In this work, the mass attenuation coefficient, effective atomic number and half value layer parameters were calculated for silicate (SiO2) mixed with various levels of lead oxide and iron oxide as reinforced materials. SiO2 was used with different concentrations of PbO and Fe2O3 (25, 50 and 75 weight %). The glass system was prepared by the melt-quenching method. The attenuation parameters were calculated at photon energies varying from 1keV to 100MeV using the XCOM program (version 3.1). In addition, the mass attenuation coefficient and half value layer parameters for selected glass samples were experimentally determined at photon energies 0.662 and 1.28 MeV emitted from radioactive sources 137Cs and 22Na respe

In the present article, Nano crystalline SnS and SnS:3% Bi thin films were fabricated using thermal
evaporation with 400±20 nm thickness at room temperature at a rate deposition rate of 0.5 ±0.01nm
/sec then annealing for one hour at 573 K for photovoltaic application. The prepared samples were
characterized in order to investigate the structural, electrical, morphological, and optical properties
using diverse techniques. XRD and SEM were recorded to investigate the effect of doping and
annealing on structural and morphological possessions, respectively. XRD showed an SnS phase
with polycrystalline and appeared to form an orthorhombic structure, with the distinguish trend
along the (111) grade,

Cadmium Oxide and Bi doped Cadmium Oxide thin films are prepared by using the chemical spray pyrolysis technique a glass substrate at a temperature of (400?C) with volumetric concentration (2,4)%. The thickness of all prepared films is about (400±20) nm. Transmittance and Absorbance spectra are recorded in the wave length ranged (400-800) nm. The nature of electronic transitions is determined, it is found out that these films have directly allowed transition with an optical energy gap of (2.37( eV for CdO and ) 2.59, 2.62) eV for (2% ,4%) Bi doped CdO respectively. The optical constants have been evaluated before and after doping.

The concepts of higher Bi- homomorphism and Jordan higher Bi- homomorphism have been introduced and studied the relation between Jordan and ordinary higher Bi- homomorphism also the concepts of Co- higher Bi- homomorphism and  Co- Jordan higher Bi- homomorphism introduced  and the relation between them in Banach algebra have also been studied.

In this work the effect of annealing temperature on the structure and the electrical properties of Bi thin films was studied, the Bi films were deposited on glass substrates at room temperature by thermal evaporation technique with thickness (0.4 µm) and rate of deposition equal to 6.66Å/sec, all samples are annealed in a vacuum for one hour. The X-ray diffraction analysis shows that the prepared samples are polycrystalline and it exhibits hexagonal structure. The electrical properties of these films were studied with different annealing temperatures, the d.c conductivity for films decreases from 16.42 ? 10-2 at 343K to 10.11?10-2 (?.cm)-1 at 363K. The electrical activation energies Ea1 and Ea2 increase from 0.031 to 0.049eV and