This study was carried out to evaluate the hepato-protective property of (Arachis hypogea L.) peanut skin extracts in CCl4 induced hepatotoxicity in mice. The antioxidant activity was measured utilizing 2, 2-diphenyl-1-1 picrylhydrazyl (DPPH) radical scavenging capacity. The results showed that the methanolic extract was the highest free radical scavenging activity than the aqueous extract with values (92.34 ± 0.45 and 87.62 ± 0.44) respectively in 12 mg/mL compared to 89.61 ± 0.34 for Butylated hydroxytoluene (BHT) and 93.25 ± 0.06 for vitamin C, which means that the methanolic extract of peanut skin is superior to BHT. Furthermore, the total phenolic content was analyzed by using Folin-Ciocalteu method, the amount of total phenol in aqueous extract was15.32 ± 0.45, 39.29 ± 0.64 and 56.63 ± 1.03 mg/g in 2, 6 and 10 mg/ml respectively, while the methanolic extract was 47.08 ± 0.56, 68.40 ± 1.18 and 85.35 ± 0.62 mg/g respectively in the same concentrations. The hepato-protective effect of peanut skin extract was evaluated in CCl4 induced hepato-toxicity. The experiment was conducted in two methods: pre-treatment groups and post-treatment groups. Mice were treated with 50 and 100 mg/kg of aqueous and methanolic peanut skin extracts for 35 days before being damaged by CCl4 (pre-treatment group), and the other groups (post-treatment groups) which the mice were injected with CCl4 and received 50 and 100 mg/kg of aqueous and methanolic peanut skin extracts for 35 days. Biochemical studies show that there is decrease in the levels of serum ALT, AST, ALP, MDA and increases in the levels of SOD with significant differences (p <0.01) when compared with the CCl4 treated group. The histo pathological examination of liver obtained from mice with administrated intraperitoneally 3 ml/kg CCl4 showed histopathological changes in the liver represented in fatty changes of excessive hepatocyte accumulation of fatty material, while when treated with 100 mg/kg of peanut extract revealed look like normal structure appearance of hepatic tissue and normal structure appearance but with few apoptotic cells.
The investigation of the effect of tempering on thermal analysis of
Al-Ti-Si alloy and its composites with MgO and SiC particles was
performed. Thermal analysis was performed before and after
tempering by DSC scan. Optical microscopy was used to identify the
phases and precipitations that may be formed in base alloy and
composites. X-ray diffraction test indicated that the Al3Ti is the main
phase in Al-Ti-Si alloy in addition to form Al5Ti7Si12 phase. Some
chemical reactions can be occurred between reinforcements and
matrix such as MgO.Al2O3 in Al-Ti/MgO, and Al4C3 and Al(OH)3 in
Al-Ti/SiC composite. X-ray florescence technique is used to
investigate the chemical composition of the fabricated specimens.
H
(1)
Abstract: This study aims to investigate the effects of solvents of various polarities on the electronic absorption and fluorescence spectra of RhB and Rh6G. The singlet‐state excited dipole moments (me) and ground state dipole moments (mg) were estimated from the equations of Bakshiev -Kawski and Chamma‐ Viallet using the variation of Stokes shift along with the solvent’s dielectric constant (e) and refractive indexes (n). The observed singlet‐state excited dipole moments were found to be larger than the ground‐state ones. Moreover, the obtained fluorescence quantum yield values were influenced by the environment of the fluorescing molecule. Consequently, the concentration of the dye solution, excited singlet state absorption and
... Show MorePVA, Starch/PVA, and Starch/PVA/sugar samples of different
concentrations (10, 20, 30 and 40 % wt/wt) were prepared by casting
method. DSC analysis was carried; the results showed only one glass
transition temperature (Tg) for the samples involved, which suggest
that starch/PVA and starch/PVA/sugar blends are miscible. The
miscibility is attributed to the hydrogen bonds between PVA and
starch. This is in a good agreement with (FTIR) results. Tg and Tm
decrease with starch and sugar content compared with that for
(PVA). Systematic decrease in ultimate strength, due to starch and
sugar ratio increase, is attributed to (PVA), which has more hydroxyl
groups that made its ultimate strength higher than that for
(1)
Superconducting thin films of Bi1.6Pb0.4Sr2Ca2Cu2.2Zn0.8O10 system were prepared by depositing the film onto silicon (111) substrate by pulsed laser deposition. Annealing treatment and superconducting properties were investigated by XRD and four probe resistivity measurement. The analysis reveals the evolution of the minor phase of the films 2212 phase to 2223 phase, when the film was annealed at 820 °C. Also the films have superconducting behavior with transition temperature ≥90K.
Poly vinyl alcohol has been studied for its ability to form crystallites by using annealing method. Semicrystalline films of poly vinyl alcohol (PVA) were prepared by casting 11.5 wt. % and 13 wt. % PVA aqueous solution onto glass slides at annealing temperature range 90 -120°C and duration time 15- 60 minute. This allowed the macromolecules to form crystallites, small regions of folded and compacted chains separated by amorphous regions where single PVA chain may pass through several of these crystallites. Degree of crystallinity of PVA films (hydrogels) was determined by method of density; on the other hand the swelling behavior was conducted by the determination of water uptake, wet degree of crystallinity, gel fraction and solubilit
... Show MoreCdS and CdTe thin films were thermally deposited onto glass substrate. The CdCl2 layer was deposited onto CdS surface. These followed by annealing for different duration times to modify the surface and interface of the junction. The diffraction patterns showed that the intensity of the peaks increased with the CdCl2/annealed treatment, and the grain sizes are increased after CdCl2/annealed treatment
Thin films samples of Bismuth sulfide Bi2S3 had deposited on
glass substrate using thermal evaporation method by chemical
method under vacuum of 10-5 Toor. XRD and AFM were used to
check the structure and morphology of the Bi2S3 thin films. The
results showed that the films with law thickness <700 nm were free
from any diffraction peaks refer to amorphous structure while films
with thickness≥700 nm was polycrystalline. The roughness decreases
while average grain size increases with the increase of thickness. The
A.C conductivity as function of frequency had studied in the
frequency range (50 to 5x106 Hz). The dielectric constant,
polarizability showed significant dependence upon the variation of
thic
(1)
been taken at room temperature down to liquid nitrogen temperature (77K). Polar and nonpolar solvents have been used to study the solvent effect on the absorption and fluorescence spectra of solute molecules. Some of the spectroscopic parameters have been determined as functions of solvent polarity and temperature. The results indicate that the band width FWHM increases with increasing the solvent polarity and temperature, while the peak emission cross section decreases with increasing of solvent polarity and decreases with increasing the temperatures. Clear vibrational structure spectra of benzoanthracene molecules have been observed in Nonane and Hexane solvents at 77K.