The structural, optical and electrical properties of ZnS films prepared by vacuum evaporation technique on glass substrate at room temperature and treated at different annealing temperatures (323, 373, 423)K of thickness (0.5)µm have been studied. The structure of these films is determined by X-ray diffraction (XRD). The X-ray diffraction studies show that the structure is polycrystalline with cubic structure, and there are strong peaks at the direction (111). The optical properties investigated which include the absorbance and transmittance spectra, energy band gab, absorption coefficient, and other optical constants. The results showed that films have direct optical transition. The optical band gab was found to be in the range t

A Laced Reinforced Concrete (LRC) structural element comprises continuously inclined shear reinforcement in the form of lacing that connects the longitudinal reinforcements on both faces of the structural element. This study conducted a theoretical investigation of LRC deep beams to predict their behavior after exposure to fire and high temperatures. Four simply supported reinforced concrete beams of 1500 mm, 200 mm, and 240 mm length, width, and depth, respectively, were considered. The specimens were identical in terms of compressive strength (  40 MPa) and steel reinforcement details. The same laced steel reinforcement ratio of 0.0035 was used. Three specimens were burned at variable durations and steady-state temperatures (one

The ceramic compound Mg1-xSixAl2O4 (x= 0, 0.1, 0.2, 0.3, 0.4) was prepared from nano powder of Al2O3 and MgO doped with Nano powder of SiO2 at different molar ratios. The specimens were prepared by standard chemical solid reaction technique and sintered at 1450 oC. Structure of the specimens was analyzed by using X-ray diffraction (XRD). The X-ray patterns of the specimens showed the formation of pure simple cubic spinel structure MgAl2O4 phase with space group of ̅ . The average grain size and surface topology were studied by atomic force microscopy. The results showed that the average grain size was about 73-90 nm. The DC electrical properties of the specimen were measured. The apparent density was found to increase and the porosity a

     This work compares the changes in optical and structural properties of cerium oxide (CeO2) when doped with different concentrations (3%,5%,7%, and 9%) of two oxides, In2O3 and Eu2O3. X-ray diffraction and spectrophotometry were employed in the visible, ultraviolet, and near-infrared regions. The findings demonstrated that CeO2 doped with In2O3 and Eu2O3 thin films were polycrystalline and had a cubic structure. The crystal size increased from 20.5 to 32.15 when Eu2O3 doping ratio increased from 0% to 7% and then decreased to 28.46 nm at 9%. While the crystal size showed an increase from 20.5 to 21.42 nm with the increase of the In2O3 doping ratio, while the lattice constant measured for cubic CeO2 changed opposite to that

Exposure of reinforced concrete buildings to an accidental fire may result in cracking and loss in the bearing capacity of their major components, columns, beams, and slabs. It is a challenge for structural engineers to develop efficient retrofitting techniques that enable RC slabs to restore their structural integrity, after being exposed to intense fires for a long period of time. Experimental
investigation was carried out on twenty one slab specimens made of self compacting concrete, eighteen of them are retrofitted with CFRP sheets after burning and loading till failure while three of them (which represent control specimens) are retrofitted with CFRP sheet after loading till failure without burning. All slabs had been tested in a

Complex-valued regular functions that are normalized in the open unit disk are vastly studied. The current study introduces a new fractional integrodifferential (non-linear) operator. Based on the pre-Schwarzian derivative, certain appropriate stipulations on the parameters included in this con-structed operator to be univalent and bounded are investigated and determined.

The compounds 3-[4̄-(4˭-methoxybenzoyloxy) benzylideneamino]-2-thioxo-imidazolidine-4-one(3)aand 4-(1-(5-oxo- 2-thioxoimidazolidin-1-ylimino)ethyl)phenyl acetate(3)b were prepared from the reaction of aromatic aldehyde or ketone(1)a,bwith thiosemicarbazide to give aryl thiosemicarbazones(2)a,b ,followed by cyclization with ethylchloroacetate in the presence of fused sodium acetate. Treatment the compounds(3)a,bwith 4- hydroxybenzenediazoniumchloride yielded the correspondings4-((4-((4-hydroxyphenyl)diazenyl)-5-oxo-2- thioxoimidazolidin-1-ylimino)methyl)phenyl 4-methoxybenzoate(4)aand4-(1-(4-((4-hydroxyphenyl)diazenyl)-5-oxo-2- thioxoimidazolidin-1-ylimino)ethyl)phenyl acetate(4)b.The new 2-thioxo-imidazolidin-4-one with esters (5-7)a,b sy

The compounds 3-[4̄-(4˭-methoxybenzoyloxy) benzylideneamino]-2-thioxo-imidazolidine-4-one(3)aand 4-(1-(5-oxo- 2-thioxoimidazolidin-1-ylimino)ethyl)phenyl acetate(3)b were prepared from the reaction of aromatic aldehyde or ketone(1)a,bwith thiosemicarbazide to give aryl thiosemicarbazones(2)a,b ,followed by cyclization with ethylchloroacetate in the presence of fused sodium acetate. Treatment the compounds(3)a,bwith 4- hydroxybenzenediazoniumchloride yielded the correspondings4-((4-((4-hydroxyphenyl)diazenyl)-5-oxo-2- thioxoimidazolidin-1-ylimino)methyl)phenyl 4-methoxybenzoate(4)aand4-(1-(4-((4-hydroxyphenyl)diazenyl)-5-oxo-2- thioxoimidazolidin-1-ylimino)ethyl)phenyl acetate(4)b.The new 2-thioxo-imidazolidin-4-one with esters (5-7)a,b sy