In this study, gold nanoparticle samples were prepared by the chemical reduction method (seed-growth) with 4 ratios (10, 12, 15 and 18) ml of seed, and the growth was stationary at 40 ml. The optical and structural properties of these samples were studied. The 18 ml seed sample showed the highest absorbance. The X- ray diffraction (XRD) patterns of these samples showed clear peaks at (38.25^o, 44.5^o, 64.4^o, and 77.95^o). The UV-visible showed that the absorbance of all the samples was in the same range as the standard AuNPs. The field emission-scanning electron microscope (FE-SEM) showed the shape of AuNPs as nanorods and the particle size between 30-50 nm. Rhodamine-610 (RhB) was prepared at 10<

Background: to evaluate the effect of different dentifrices on the surface roughness of two composite resins (nanofilled-based and nanoceramic – based composite resins). Materials and methods: Forty specimens (diameter 12 mm and height of 2mm) prepared from different composite resin materials: Z350 (nanofilled composite, and Ceram-X (nanoceramic) .they were subjected to brushing simulation equivalent to the period of 1 year. The groups assessed were a control group brushed with distilled water (G1), Opalescence whitening toothpasteR (G2), Colgate sensitive pro-relief (G3) and Biomed Charcoal Toothpaste (G4). The initial and final roughness of each group was tested by surface roughness tester. The results were statistically analyzed using

In this paper two modifications on Kuznetsov model namely on growth rate law and fractional cell kill term are given. Laplace Adomian decomposition method is used to get the solution (volume of the tumor) as a function of time .Stability analysis is applied. For lung cancer the tumor will continue in growing in spite of the treatment.

Dengke Naniura is a traditional food from Sumatera Utara, Indonesia, that is produced through fermenting process, and this food is believed to contain high probiotics. The objective of the current research is to determine the potential of LAB as a probiotic that has been obtained from Dengke Naniura. Dengke Naniura was traditionally prepared from Cyprinus carpio. Four LABs have been successfully isolated from Dengke Naniura, such as D7DA3, D7B3, D7DBF and D7DN3. Those four LAB isolates were identified as Lactobacillus sp. This result has been confirmed by the non-spore forming bacterium, non-motile, and Gram-positive. Also, it has been supported by biochemical test, for the example Voges Proskauer, catalase test, Methyl

The use of deep learning.

Nano γ-Al₂O₃ support was prepared by co-precipitation method by using different calcination temperatures (550, 600, and 750) ^oC. Then nano NiMo/γ-Al₂O₃ catalyst was prepared by impregnation method were nickel carbonate (source of Ni) and ammonium paramolybdate (source of Mo) on the best prepared nano γ-Al₂O₃ support at calcination temperature 550 ^oC. Make the characterizations for prepared nano γ-Al₂O₃ support at different temperatures and for nano NiMo/γ-Al₂O₃ catalyst like X-ray diffraction, X-ray fluorescent, AFM, SEM, BET surface area, and pore volume.

The N

Zinc Oxide (ZnO) thin films of different thickness were prepared
on ultrasonically cleaned corning glass substrate, by pulsed laser
deposition technique (PLD) at room temperature. Since most
application of ZnO thin film are certainly related to its optical
properties, so the optical properties of ZnO thin film in the
wavelength range (300-1100) nm were studied, it was observed that
all ZnO films have high transmittance (˃ 80 %) in the wavelength
region (400-1100) nm and it increase as the film thickness increase,
using the optical transmittance to calculate optical energy gap (Eg
opt)
show that (Eg
opt) of a direct allowed transition and its value nearly
constant (~ 3.2 eV) for all film thickness (150