In this work, porous silicon gas sensor hs been fabricated on n-type crystalline silicon (c-Si) wafers of (100) orientation denoted by n-PS using electrochemical etching (ECE) process at etching time 10 min and etching current density 40 mA/cm2. Deposition of the catalyst (Cu) is done by immersing porous silicon (PS) layer in solution consists of 3ml from (Cu) chloride with 4ml (HF) and 12ml (ethanol) and 1 ml (H2O2). The structural, morphological and gas sensing behavior of porous silicon has been studied. The formation of nanostructured silicon is confirmed by using X-ray diffraction (XRD) measurement as well as it shows the formation of an oxide silicon layer due to chemical reaction. Atomic force microscope for PS illustrates that the pores have sphere-like shape and the porous layers have sponge-like appearance. Sensing behavior is studied for PS before and after fictionalization with copper at different operating temperatures and it is found that the maximum sensitivity is (64516.82%) after fictionalization with Cu at T=250 ºC.
The research aims to improve the effectiveness of internal control system according to a model COSO, by identifying the availability of system components according to the model and then improve the effectiveness of each component by focusing on areas for improvement in each component, as it was addressed to a model COSO and then Maamth with the environment, the current Iraqi by introducing some improvements on the form of some mechanisms of corporate governance of the Council of Directors, and senior management, the Audit Committee, Committee appointments, especially that supplies application available in the laws and legislation, the current Iraqi, taking into consideration to make some
... Show More
This study deals with the role of compensation system in improving the quality of educational services (University of Halabja as a Model) also our problem was the following question ; What is the role of compensation system in its different dimensions in improving the quality of educational services? And what is the relationship and impact of using the dimensions of the compensation system to improve the quality of educational services? The hypothesis of the research included the correlation and the impacts between the compensation system and its combined variables in the quality of educational services. This was proved through a field study and the distribution of questionn
... Show More
(1)
Mixed convection heat transfer in a vertical concentric annulus packed with a metallic porous media and heated at a constant heat flux is experimentally investigated with water as the working fluid. A series of experiments have been carried out with a Rayleigh number range from Ra=122418.92 to 372579.31 and Reynolds number that based on the particles diameter of Red=14.62, 19.48 and 24.36. Under steady state condition, the measured data were collected and analyzed. Results show that the wall surface temperatures are affected by the imposed heat flux variation and Reynolds number variation. The variation of the local heat transfer coefficient and the mean Nusselt number are presented and analyzed. An empirical
... Show More
(22)
(19)
(22)
(19)
Titanium alloy (Ti-6Al-4V) samples were nitrided in low pressure (1.3, 3 mbar) dc-glow discharge plasmas of nitrogen. The treating time was 5, 10 and 15 hour and the temperatures range of the samples during the nitriding process was close to 800oC. The obtained microstructures of the nitride layers were studied by x-ray diffraction and optical microscopy. The ε –Ti2N, ζ-Ti3N3-x and η-Ti3N2-x.phases were formed and addition to the solid solution of nitrogen in titanium, α (Ti,N). Micro hardness measurements exhibit an increment for the Ti-alloy specimens which nitrided at 800oC for 10 and 15h.Corrosion measurements were obtained for the Ti-6Al-4V alloy in Ringer solution after plasma nitriding. The clear improving in the corrosion r
... Show More
(7)
(4)
This study introduced the effect of using magnetic abrasive finishing method (MAF) for finishing flat surfaces. The results of experiment allow considering the MAF method as a perspective for finishing flat surfaces, forming optimum physical mechanical properties of surfaces layer, removing the defective layers and decreasing the height of micro irregularities. Study the characteristics which permit judgment parameters of surface quality after MAF method then comparative with grinding
In this search, Ep/SiO2 at (3, 6, 9, 12 %) composites is prepared by hand Lay-up method, to measure the change in the thermal conductivity and Impact Strength of epoxy resin before and after immersion in H2SO4 Solution with a 0.3N for 10 days. The results before immersion decreases with the increase of the weight ratios of the reinforcement material (SiO2), It changed from (82.6×10-2 to 38.7×10-2 W/m.°C) with change weight ratios from (3 to 12) % respectively, but after immersion time in the chemical solution where it was (65.6×10-2 W/m.°C) at the weight ratios (6 %) and became (46.6 × 10-2 W/m.°C) after immersion in sulfuric acid. The results of the Impact strength decreased by increasing the percentage weight ratio, it changed f
... Show More
Hydrogen and nanocarbon were produced by the catalytic decomposition of electrocracking gas obtained by the pyrolysis of liquid organic waste via electric arc discharge. The GIAP-16 (NiO-Al2O3) industrial catalyst was used to reduce the maximum decomposition temperature to 700 °C. In a fixed-bed reactor, under atmospheric pressure, reasonable amounts of high-purity hydrogen were produced, accompanied by deposits of nanocarbon by-product. The NiO-Al2O3 catalyst showed excellent catalytic activity. X-ray powder diffraction analysis of the NiO-Al2O3 composite revealed the presence of cubic NiO and rhombohedral Al2O3, which were chemically stable. However, above 500 °C, NiAl2O4 began to appear. The specific surface area of the catalyst was de
... Show More