Lithium–Manganese ferrites having the chemical formula (Li0.5-0.5x Mnx Fe2.5-0.5x O4), (0 ≤ x ≤ 1) were prepared by double sintering powder processing. The density of the ferrite increased with Mn content while the porosity was noticed to decrease. The dielectric constant was found to increase at high frequencies more rapidly than the low ones. The dielectric constant found to decrease with Mn content. The decrease in loss factor with frequency agreed with Deby’s type relaxation process. A maximum of dielectric loss factor was observed when the hopping frequency is equal to the external electric field frequency. Manganese substitution reduced the dielectric loss in ferrite. The variation of tanδ with frequency shows a similar na

The ratio of draft tube to reactor diameters is of decisive importance for the operation behavior of air lift loop reactors. The influence of draft tube geometry was investigated with respect to oxygen mass transfer and mixing time. The diameter ratio was varied between 0.33 and 0.80. The measurements were performed in two loop reactors with liquid capacities of 11.775 and 26.49 liters using aqueous with solutions of different coalescence behavior. The results show that there is no single diameter ratio which would produce most favorable conditions for the two process parameters. With respect to the more important requirements of aerobic cultures, i.e high oxygen mass transfer and efficient mixing, a diameter ratio between 0.5 and 0.6 is

يتضمن البحث دراسة لزوجة محاليل تحتوي على املاح كلوريد البوتاسيوم وبروميد البوتاسيوم في مزيج من الماء وداي مثيل سلفوكسايد 60% وزنا داي مثيل سلفوكسايد.وقد اجريت الدراسة بست درجات حرارية مختلفة ونوقشت امكانية في ضوء معادلة جونز- دول حيث اخذ بنظر الاعتبار الحجم الايوني والشحنة وشكل جزيئات المذاب.

In this paper, three types of epoxy-based coatings (Polyamide, pure Polyamine, and Polyamine reinforced by glass-flake) used as a lining for potable water tanks were studied using experimental and finite element methods. Tensile, impact, and fatigue tests were conducted on uncoated and coated AISI 316 stainless steel. The test results show that the applied epoxy based coating improves the mechanical properties, increases of fatigue crack resistance, and enhance the dynamic fracture toughness. The fatigue crack propagation is influenced by the compositions of epoxy coating, and the glass-flake improves the coating resistance to fatigue crack propagation compared to other types.

The aim of this study was to assess the nutritional status for samples at the age of 17-15 years. These samples were taken from secondary schools and universities in Baghdad area, 123 of them were male and 261 were female. Data on weight, height and body mass index (BMI) were determined in each individual. Smaller sample of 215 individuals (male and female) from the original sample was taken in order to record their nutritional behavior and daily food intake during the 24 hours prior to the visit through personal meeting using special questionnaire. The results showed that the weight and the height were within the range of the people of neighboring Arab countries, who are in the same age. Beside 44.4- 55.95% of these samples were within t

Polymer electrolyte films composed of PVP and PVP/glycerin with varying concentrations of CuCl2 (10, 20, and 30 wt.%) were synthesized using the solution casting method. The synthesized electrolyte films were characterized using FTIR, XRD, UV-Vis, DSC, and TGA techniques. FTIR spectroscopy revealed an O-H stretching vibration of PVP around 3300 cm(-1), which experienced broadening and a reduction in intensity upon the introduction of glycerin and CuCl2. XRD analysis displayed a characteristic peak at 2 theta similar to 20 degrees, with the peak shifting towards higher angles and a slight decrease in intensity as the CuCl2 concentration increased, indicating a disruption of the crystalline structure of the host matrix. UV-Vis analysis reveal

Removable dental prostheses remain a reliable treatment for edentulous patients. Conventional fabrication requires multiple steps, whereas computer-aided design and manufacturing (CAD-CAM), particularly 3D printing, offers faster and more cost-effective alternatives. This in vitro study aimed to evaluate the effect of sandblasting on surface roughness and shear bond strength of silicone soft liner bonded to 3D-printed and heat-cured acrylic denture base materials. Eighty specimens were divided into four groups: heat-cured control, 3D-printed control, heat-cured sandblasted, and 3D-printed sandblasted. Surface roughness was measured using a profilometer, while shear bond strength was tested with a universal testing machine. D