CdSe alloy has been prepared successfully from its high purity elements. Thin films of this alloy with different thicknesses (300,700)nm have been grown on glass substrates at room temperature under very low pressure (10-5)Torr with rate of deposition (1.7)nm/sec by thermal evaporation technique, after that these thin films have been heat treated under low pressure (10-2)Torr at (473,673)K for one hour. X-ray patterns showed that both CdSe alloy and thin films are polycrystalline and have the hexagonal structure with preferential orientation in the [100] and [002] direction respectively. The optical measurements indicated that CdSe thin films have allowed direct optical energy band gap, and it increases from (1.77- 1.84) eV and from

Azo-Schiff base compounds (L1 and L2) have been synthesized from the reaction of m-hydroxy benzoic acid with 1,5-dimethyl-3-[2-(5-methyl-1H-indol-3-yl)-ethylimino]-2-phenyl-2,3- dihydro-1H-pyrazol-4-ylamine and with 3-[2-(1H-indol-3-yl)-ethylimino]-1,5-dimethyl-2-phenyl- 2,3-dihydro-1H-pyrazol-4-ylamine. The free ligands and their complexes were characterized based on elemental analysis, determination of metal, molar conductivity, (1H, 13C) NMR, UV–vis, FT-IR, mass spectra and thermal analysis (TGA). The molar conductance data revealed that all the complexes are non-electrolytes. The study of complex formation via molar ratio in DMF solution has been investigated and results were consistent to those found in the solid complexes with a rat

Background: Dental stone casts come into contact with impression materials and becomes susceptible to cross contamination from saliva and blood. This study was done to evaluate the physical and mechanical properties of dental stone type IV after treatments with various disinfecting agents and regimes (methods). Materials and Methods: Type IV dental stone and different types of disinfecting agents were used and divided into seven groups: G1: dental stone without disinfection (control group), G2: dental stone mixed with silver nitrate powder 0.5% , G3: dental stone mixed with silver nitrate powder 1%, G4: dental stone mixed with copper sulfate powder 0.5%, G5: dental stone mixed with copper sulfate powder 1% ,G6: dental stone immersed in prop

The present work initiated to eaIuate the efficiency of Al-Rustamivah sewage treatment plant
as reflected by the quality of final effluent that is thrown to Di ala river. Weekly samples of
wastewater and final effluent were collected between November 1994 and end of January
1995 and analyzed for different chemical and biological features. Results ha e inidicated that
Al-Rustamiyah sewage treatment plant could not be able efficiently to purify the raw sewage.
The mean values of suspended solids. BOD. COD Dichromate and Oil & grease effluents
were felt to pass standard limits (98.4. 92.8. 125.2 and 39.1 ppm. respectiel). The atherse
possible effects of pollution on Diuala equatic life hae been also discussed in res

In this work, the spectra for plasma glow produced by pulse
Nd:YAG laser (λ=532 and 1064nm) on Ag:Al alloy with same molar
ratio samples in distilled water were analyzed by studying the atomic
lines compared with aluminum and silver strong standard lines. The
effect of laser energies of the range 300 to 800 mJ on spectral lines,
produced by laser ablation, were investigated using optical
spectroscopy. The electron temperature was found to be increased
from 1.698 to 1.899 eV, while the electron density decreased from
2.247×1015 to 5.08×1014 cm-3 with increasing laser energy from 300
to 800 mJ with wavelength of 1064 nm. The values of electron
temperature using second harmonic frequency are greater than of<

Samples prepared by using carbon black as a filler material and phenolic resin as a binder. The samples were pressed in a (3) cm diameter cylindrical die to (250)MPa and treated thermally within temperature range of (600-1000)oC for two and three hours. Physical properties tests were performed, like density, porosity, and X-ray tests. Moreover vicker microhardness and electric resistivity tests were done. From the results, it can be concluded that density was increased while porosity was decreased gradually with increasing temperature and treating time. In microhardness test, it found that more temperature and treating time cause more hardness. Finally the resistivity was decreased in steps with temperature and treating time. It can be c

This study explains the effect of non-thermal (cold) plasma on wound of diabetic rats by (FE-DBD) system, 3cm probe diameter is used. The output power was ranged from (12-20) W. The effect of non-thermal plasma on wounds of a diabetic was observed with different exposure durations (20,30) sec., the plasma exposure duration decreases the sugar level in blood and the diameter of the wound. These results indicate the cold plasma can be used to enhance the insulin level (i.e., blood sugar) and wounds treatment.

The current study was conducted on goats in various parts of Wasit Province, Iraq, from November 2021 to April 2022. The study aims to find and identify intestinal parasites (IPs) in goats in Wasit province. The goat's fresh fecal specimens (n=180) include cysts, eggs, oocysts, trophozoites and larval stages. One hundred eighty sheep feces samples were collected, and more than one parasite was isolated from one sample (mixed infection). According to the data acquired, the overall prevalence of intestinal parasites in goats was 52.77 (95 samples). In the current investigation, eleven distinct (IPs) species with infection rates were identified, including Toxocara vitulorum (Goeze, 1782) (16.66 %), Cryptosporidium sp.( Tyzzer, 1907) (1

يسعى المجتمع من خلال الوحدات الإقتصادية إلى الوصول إلى تحقيق أفضل الإنجازات التي لا تتمثل بالسلع والخدمات حسب وإنما بما يتحقق من مردود لكافة الاطراف المعنية بالوحدات الإقتصادية على ان لايتم ذلك على حساب قيم المجتمع وأخلاقياته وآدابه العامة. وعليه تصبح الوحدات الإقتصادية مسرحاً لصراعات قوى متعددة كل منها له قيمه الأخلاقية سواء كان فرداً أومجموعة افراد أو وحدة إقتصادية أو أي جهة أُخرى، وبحكم مسؤولياته

In this report Silver doped Tin Sulfide (SnS) thin films with ratio of (0.03) were prepared using thermal evaporation with a vacuum of 4*10-6 mbar on glass with (400) nm thickness and the sample annealing with ( 573K ). The optical constants for the wavelengths in the range (300-900) nm and Hall effect for (SnS and SnS:3% Ag) films are investigated and calculated before and after annealing at 573 K. Transition metal doped SnS thin films the regular absorption 70% in the visible region, the doping level intensification the optical band gap values from 1.5- 2 eV. Silver doped tin sulfide (SnS) its direct optical band gap. Hall Effect results of (SnS and SnS:3% Ag) films show all films were (p-type) electrical conductivity with resistivity of