Corrosion inhibitor of carbon steel in 3.5%NaCl solution with Schiff base compounds
...Show More Authors

In this work, synthesized N4,N4`-bis(2, 3, 4 nitro benzylidene) biphenyi-4-4`-diamine(B1-B3) , was tested as an inhibitors in controlling the corrosion of carbon steel in NaCl 3.5% solution by using open circuit potential (OCP),at four different temperatures (293, 303, 313 and 323 K). Furthermore, the surface morphology was investigated using the Atomic force microscopy (AFM). The effect of using different Schiff bases and temperature was also investigated. Schiff bases was synthesized and characterized via using. Fourier Transform Infrared Spectroscopy (FT-IR)and Atomic Force Microscope (AFM) characterized . The experimental results shown that Schiff bases can consider as an excellent corrosion inhibitors for carbon steel in NaCl 3.5% solution, by presence of Schiff bases the corrosion of carbon steel was significantly suppressed. The inhibition efficiency is decreased with the increases of temperature. Kinetic and thermodynamic activation parameters (Ea, A, ΔH*, ΔS* and ΔG*) were calculated.

Crossref
View Publication
Publication Date
Fri Jul 21 2023
Journal Name
Journal Of Engineering
CATHODIC PROTECTION OF CARBON STEEL IN 0.1N NaCl SOLUTION UNDER FLOW CONDITIONS USING ROTATING CYLINDER ELECTRODE
...Show More Authors

The effect of applied current on protection of carbon steel in 0.1N NaCl solution (pH=7) was investigated under flow conditions (0-0.262 m/s) for a range of temperatures (35-55°C) using rotating cylinder electrode. Various values of currents were applied to protect steel from corrosion, these were Iapp.=Icorr., Iapp.=2Icorr. and Iapp.=2.4Icorr. under stationary and flow conditions. Corrosion current was measured by weight loss method. The variation of protection potential with time and rotation velocity at various applied currents was assessed. It is found that the corrosion rate of carbon steel increases with rotation velocity and
has unstable trend with temperature. The protection current required varies with temperature and it inc

... Show More
View Publication Preview PDF
Crossref (2)
Crossref
Publication Date
Thu Jul 01 2021
Journal Name
Chemical Methodologies
Novel Synthesis of Some N-Hydroxy Phthalimide Derivatives with Investigation of Its Corrosion Inhibition for Carbon Steel in HCl Solution
...Show More Authors

In the current study, new derivatives were synthesized by reaction of N-hydroxyphthalimide with chloro acetyl chloride in the presence of Et3N as a base to form 1,3-dioxoisoindolin-2-yl 2-chloroacetate (B1), which in turn enters several reactions with different amines where it interacts with primary amines to give 1,3-dioxoisoindolin-2-yl acetate derivatives (B2-B4) in basic medium, in the same way it interacts with these amines but with adding KNCS to form thiourea derivatives (B5-B7). It also reacts with diamines to give bis(azanediyl) derivatives (compounds B8-B10). The prepared derivatives were diagnosed using infrared FTIR and 1HNMR,13CNMR for some derivatives. Compounds B4, B5 and B9 were measured as corrosion inhibitors the inhibitio

... Show More
View Publication Preview PDF
Clarivate
Publication Date
Mon Dec 30 2002
Journal Name
Iraqi Journal Of Chemical And Petroleum Engineering
The Optimal Corrosion Inhibition of Aluminum in 0.1M NaCl Solution
...Show More Authors

View Publication Preview PDF
Publication Date
Thu Mar 01 2018
Journal Name
International Journal Of Science And Nature
EXPERIMENTAL AND THEORETICAL STUDY OF 3-BENZYL -2- MERCAPTOQUINOIZOLINE-4(3H)-ONE (BMQ) AS AN INHIBITOR OF CARBON STEEL CORROSION IN ACIDIC MEDIA
...Show More Authors

The inhibition of 3-Benzyl -2-mercaptoquinoizoline -4 (3H)-one (BMQ) on the corrosion of carbon steel in 0.5 M HCl studied by potentionstat polarization methods at 303–333 K. Results obtained show that BMQ act as inhibitor for carbon steel in HCl solution. The inhibition efficiency increase with increase in BMQ concentration. Activation parameters and Gibbs free energy for the adsorption process using Statistical Physics calculated and discussed. Quantum chemical calculations using DFT at the B3LYP/6-31G level of theory were used to calculate some electronic properties of the molecule to verify any correlation between the inhibitive effect and molecular structure of BMQ. The quantum calculations were proceeded to get data around correlati

... Show More
View Publication Preview PDF
Publication Date
Mon Sep 18 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Effects of Thiourea on the Corrosion of Low Carbon Steel in Hydrochloric Acid Solution
...Show More Authors

The c.orrosion rate of  low carbon  steel  in 4M  hydrochlwic acid with and without  presence of thiourea has b.een studied  by gravimetric ahd gasometric methods  over the temperature range 303-333 K.

 

The percentage protection of steel increases  vvith the decrease of thimuea concentrations at  various  temperature range  303-333 K and

approaching highest  protection  (86.82%) at 303K  by using  I X 1 o-4 M

of thiourea. The high concentration .of thiourea  ( lxlo-3 M), enl1ances.

the  corrosion rates and  act  as dcpolariser for  the hydrogen  evolution

reaction,&n

... Show More
View Publication Preview PDF
Publication Date
Tue Sep 30 2008
Journal Name
Iraqi Journal Of Chemical And Petroleum Engineering
EFFECT OF TEMPERATURE ON CORROSION OF CARBON STEEL BOILER TUBES IN DILUTE SODUIM CHLORIDE SOLUTION
...Show More Authors

The corrosion behavior of carbon steel at different Temperatures and in water containing different sodium chloride
concentrations under 3 bar pressure has been investigated using weight loss method . The carbon steel specimens were
immersed in water containing (100,400,700,1000PPM) of NaCl solution and under temperature was increased from
(90-120ºC) under pressures of 3 bar. The results of this investigation indicated that corrosion rate increased with NaCl
concentrations and Temperature.

View Publication Preview PDF
Publication Date
Sun May 30 2021
Journal Name
Iraqi Journal Of Science
Theoretical study of a new oxazolidine -5- one derivative as a corrosion inhibitor for carbon steel surface
...Show More Authors

A newly derivative of oxazolidin-5- one namely [2-(2-biphenyl-4-yl-imidazo [1,2-a] pyridine-3-yl)-3-(4-nitro-phenyl)-oxazolidin-5-one (BIPNO5)] was examined as an corrosion inhibitor for carbon steel surface. Quantum mechanical method of Density Functional Theory (DFT) with (B3LYP (6-311++G (2d, 2p)) level of theory was used to calculate the minimize structure, physical properties and inhibition chemical parameters, in vacuum and two solvents (DMSO and H2O), all at equilibrium geometry. The results indicated that the new derivative could adsorb on the surface of carbon steel through the heteroatom, showing that the new inhibitor has good corrosion inhibition performance.

View Publication Preview PDF
Scopus (4)
Crossref (1)
Scopus Crossref
Publication Date
Fri Mar 15 2019
Journal Name
Al-khwarizmi Engineering Journal
Effect Use of Two Chemical Compounds Sodium Nitrate and Sodium Silicate as Corrosion Inhibitor to Steel Reinforcement
...Show More Authors

Corrosion of steel reinforcement is one of the biggest problems facing all countries in the world like bridges in the beach area and marine constructions which lead to study these problems and apply some economical solutions. According to the high cost of repair for these constructions, were studied the effect of using kind of chemical compounds sodium nitrite(NaNO2) and sodium silicate(Na2SiO3) as corrosion inhibitors admixture for steel bars that immersed partially in electrolyte solution (water + sodium chloride in 3% conc.) (Approximately similar to the concentration of salt in sea water). The two inhibitors above added each one to the electrolyte solution at concentrations (0.5%, 1% and 2%) for both

... Show More
View Publication
Crossref (1)
Crossref
Publication Date
Sun Dec 07 2014
Journal Name
Baghdad Science Journal
Corrosion Behavior of Copper and Carbon Steel in Acidic Media
...Show More Authors

The corrosion behavior of copper and carbon steel in 1M concentration of hydrochloric acid (HCl) and sulphuric acid (H2SO4) has been studied. The corrosion inhibition of copper and carbon steel in 1M concentration of hydrochloric acid (HCl) and sulphuric acid (H2SO4) by Ciprofloxacin has been investigated. Specimens were exposed in the acidic media for 7 hours and corrosion rates evaluated by using the weight loss method. The effect of temperature (from 283 ºK to 333 ºK), pH (from 1to 6), inhibitor concentration (10-4 to 10-2) has been studied. It was observed that sulphuric acid environment was most corrosive to the metals because of its oxidizing nature, followed by hydrochloric acid. The rate of metal dissolution increased with incre

... Show More
View Publication Preview PDF
Crossref
Publication Date
Thu Mar 31 2016
Journal Name
Iraqi Journal Of Chemical And Petroleum Engineering
Corrosion Inhibition of Low Carbon Steel in Sulfuric Acid Using Polyvinyl Alcohol
...Show More Authors

The inhibitive power of Polyvinyl Alcohol (PVA) was investigated toward the corrosion of carbon steel in 0.2N H2SO4 solution in the temperature range of 30-60˚C and PVA concentration range of 150-2000 ppm.

   The corrosion rate was measured using both the weight loss and the electrochemical techniques. The weight loss results showed that PVA could serve as a corrosion inhibitor but its inhibition power was found to be low for the corrosion of carbon steel in the acidic media. Electrochemical analysis of the corrosion process of carbon steel in an electrochemical corrosion cell was investigated using 3-Electrode corrosion cell. Polarization technique was used for carbon steel corrosion in 0.2N H