This search include the synthesis of some new 1,3-oxazepine derivatives have been prepared, starting from reaction of L-ascorbic acid with dry acetone in presence of dry hydrogen chloride afforded the acetal (I). Treatment of the latter with p-nitrobenzoyl chloride in dry pyridine yielded the ester (II) which was dissolved in (65%) acetic acid in absolute ethanol yielded the glycol (III). The reaction of the glycol (III) with sodium periodate in distilled water at room temperature produced the aldehyde (IV). The compound (V) [2-amino-5-mercapato-1,3,4-thiadiazole] was prepared through the reaction of thiosemicarbazide with carbon disulphide (CS2) in entity of anhydrous (Na2CO3) in (abs. ethanol ). Compound (VI) [2-(5-mercapto-1,3,4-thiadiazol-2-yl)isoindoline-1,3-dione] was synthesized by the reaction of phthalic anhydride with compound (V) in presence of (gla. CH3COOH). Reaction of compound (VI) with (ClCH2COOH) in entity of anhydrous (Na2CO3) in distilled water produced compound (VII) and then reaction with thionyl chloride yielded acid chloride (VIII). Condensation of acid chloride with hydrazine hydrate afforded 2-(5-(1,3-dioxoisoindolin-2-yl)-1,3,4-thiadiazol-2-ylthio)acetohydrazide (IX). The azomethine (X) has been synthesized from the reaction between compounds (IX) and (IV). Moreover compounds (XI-XIII) were synthesized from the cyclic condensation of Schiff base (X) with (maleic, phthalic and 3-nitrophthalic) anhydride, the structures of the novel synthesized compounds have been confirmed by physical properties and spectral measurements such as (FTIR and some of them by 1H-NMR and 13C-NMR).
The lead-acid battery has become so dependable in its used applications of automobile starting, emergency lighting and telecommunications, which left an impression that no further investigation is necessary or desirable. While there has been slow continuous improvements in lead-acid battery performance and mainly limited to design and material engineering. This work is mainly devoted to the properties of the active mass of the positive electrode and the acid/water ratio during the manufacturing process. A field study is carried out at the State Battery Manufacturing Company located in Baghdad, to prepare batches of lead mono-oxide with predefined quantities of liquid additives (i.e. sulfuric acid and water). Quality control and laborator
... Show MoreIn this search, Ep/SiO2 at (3, 6, 9, 12 %) composites is prepared by hand Lay-up method, to measure the change in the thermal conductivity and Impact Strength of epoxy resin before and after immersion in H2SO4 Solution with a 0.3N for 10 days. The results before immersion decreases with the increase of the weight ratios of the reinforcement material (SiO2), It changed from (82.6×10-2 to 38.7×10-2 W/m.°C) with change weight ratios from (3 to 12) % respectively, but after immersion time in the chemical solution where it was (65.6×10-2 W/m.°C) at the weight ratios (6 %) and became (46.6 × 10-2 W/m.°C) after immersion in sulfuric acid. The results of the Impact strength decreased by increasing the percentage weight ratio, it changed f
... Show More
Laser etching may be an alternative to acid etching of enamel and dentin. Several characteristics of irradiated dental hard tissues have been considered advantageous, microscopically rough surfaces without demineralization, open dentinal tubules without smear layer production and dentin surface sterilization. The aim of this study is to determine and compare histology the microleakage in class V cavity restored with a light cured composite after conditioning the samples(tooth surface) with 1-acid etching, 2-Q-switched Nd:YAG Laser etching and finally 3- acid and laser etching. Materials and methods: Twenty four non carious human extracted teeth were used in this study. The samples were equally grouped into four groups of six teeth each.
... Show More
(13)
(13)
KE Sharquie, AA Noaimi, SA Galib, Journal of Cosmetics, Dermatological Sciences and Applications, 2013 - Cited by 4
KE Sharquie, AA Noaimi, EA Al-Janabi, Our Dermatology Online, 2014 - Cited by 11
In recent years, there has been a rapid development in research on high performance ceramics for mechanical, electrical and medical industries. This development will be shown for alumina as a representative for oxide ceramics powders.
Dry–pressing forming technique was used to prepare different ceramic compacts for alumina grafted by polymethacrylate polymers. All Alumina compact were fired firstly at 1200 ◌ْ C, then
at 1600 ◌ْ C.
Mechanical strength was examined in different means, some
depends on compression and other depends on impact. Hardness was
also measured .The results obtained were compared with that of
Alumina compact prepared under the same condition from Alumina
especially made for pressing .