In this study, evaluate the impact of organic extracts of leaf butterfly Albzl in some aspects of life has been affected performance ratio destruction of eggs increased by 0.8% extract Alorat ethanol solvent, ethyl acetate and hexane, respectively ..

In this work, MWCNT in the epoxy can be prepared at room temperature and thickness (1mm) at different concentration of CNTs powder. Optical properties of multi-walled carbon nanotubes (CNTs) reinforced epoxy have been measured in the range of (300-800)nm. The electronic transition in pure epoxy and CNT/epoxy indicated direct allowed transition. Also, it is found that the energy gap of epoxy is 4.1eV and this value decreased within range of (4.1-3.5)eV when the concentration of CNT powder increased from (0.001-0.1)% respectively.
The optical constants which include (the refractive index (n), the extinction coefficient (k), real (ε1) and imaginarily (ε2) part of dielectric constant calculated in the of (300-800)nm at different concent

In this work, magnesium aluminate spinel (MA) (MgO 28 wt%, Al2O3 72 wt%) stoichiometric compound , were synthesized via solid state reaction (SSR) Single firing stage, and the impact of sintering on the physical properties and thermal properties as well as the fine structure and morphology of the ceramic product were examined. The Spinel samples were pressed at of (14 MPa) and sintering soaking time (2h). The effect of adding oxide titania (TiO2) was studied. The obtained powders were calcined at a temperature range of 1200 and 1400 °C. The calcined samples spinel were characterized by XRD, it showed the presence of developed spinel phase end also showed that the best catalyst is titania. The SEM image showed the high sintering temperat

The aim of this study was to evaluate tensile properties of low and medium carbon ferrite -martensite dual phase steel, and the effect cryogenic treatment at liquid nitrogen temperature (-196 ºC) on its properties. Low carbon steel (C12D) and medium carbon steels (C32D & C42D) were used in this work. For each steel grade, five groups of specimens were prepared according to the type of heat treatment. The first group was normalized, the second group was normalized and subsequently subjected to cryogenic treatment then tempered at (200 ºC) for one hour, the third group was quenched from intercritical annealing temperature of (760 ºC) to obtain dual phase (DP) steel, the fourth and fifth groups were both quenched from (760 ºC), but

In this study, the effect of the thermal conductivity of phase change material (PCM) on the performance of thermal energy storage has been analyzed numerically. A horizontal concentric shell-and-tube latent heat thermal energy storage system (LHTESS) has been performed during the solidification process. Two types of paraffin wax with different melting temperatures and thermal conductivity were used as a PCM on the shell side, case1=0.265W/m.K and case2=0.311 W/m.K. Water has been used as heat transfer fluid (HTF) flow through in tube side. Ansys fluent has been used to analyze the model by taking into account phase change by the enthalpy method used to deal with phase transition. The numerical simulatio

Nisoldipine (NSD) is a dihydropyridine class of calcium channel blockers used for hypertension treatment, it belongs to class II BCS (low solubility with high permeability), its absolute bioavailability is only 5% due to presystemic metabolism in the gut wall. It is also a substrate for a CYP3A and P-gp. Bilosomes are lipid bilayer vesicles incorporating bile salts in their walls to prevent degredation by GIT bile salts. The aim of this study is to prepare nisoldipine bilosomes as vesicular carrier and assess the effect of different formulation variables such as type of surfactant, amount of cholesterol, surfactant and sonication time on particle size, entrapment efficiency and poly dispersity index of the prepared bilos

Ceramic to metal joining technique, which was used in this investigation includes the use of active filler alloy as a sandwich between the alumina and kovar alloy for brazing. High purity powdered metals of silver, copper, and additives of titanium were used to prepare the active filler alloy, through compacting the mixed powders and alloying in a furnace with argon atmosphere at the temperature of 800oC for 10 minutes. To use it as an active filler metal, it has been modified to a proper thickness. Two groups of alumina were prepared with different sintering temperatures (1450oC and 1650oC) and each group was tested under atmospheric pressure, vacuum furnace pressure of 2*10-4 torr and vacuum furnace pressure of 2*10-6 torr. All the pro

Background: Preparation of platelet-rich fibrin (PRF) is a simple, low cost and minimally invasive method to obtain a natural concentration of autologous growth factors that is widely used to accelerate soft and hard tissue healing, thus, PRF is used in different fields of medicine. The aim of this study was to evaluate the effect of local application PRF on stability of dental implants. Materials and methods: nineteen healthy patients with adequate alveolar bone with two or more adjacent missing teeth and/or bilaterally symmetric to the midline (split-mouth design) missing teeth participated in this study. Each patient received at least two dental implants (Dentium Co., Korea). After surgical preparation of the implant sockets, the PRF was

Leishmania is auxotroph to folic acid,antifolates drug inhibit the synthesis and conversion of folate derivatives. In this study, cytotoxic effect of methotrexate was investigated on the procyclic promastigotes proliferation of L. donovani. The results showed a significant (p ≥ 0.05) difference in growth of treated groups at high concentrations (1000, 500, 250, 125.5) μM after 24, 48 hrs., while at 72 hrs. significant difference was observed at all concentration. The IC50 values was measurable after 24, 48 and 72 hrs. and it was 174.238, 52.283 and 109.175 μM, respectively. The present study showed the cytotoxic effect of methotrexate on the proliferation of promastigotes of the visceral type of Leishmania.

Widely present in the environment, arsenic trioxide has been identified as a genotoxic substance that poses a serious risk to public health. The genotoxic potential of arsenic at low allowable dosage levels is assessed in this study. Four groups of twelve adult rats each were created from the 48 total. Animals in Group I were used as controls Chromosome abnormalities found in bone marrow cells were used to assess the mutagenic potential of arsenic. Hematological parameters were also assessed. At 60 and 90 days, the percentage of microsomal degranulation in the hepatic fraction increased and the amounts of RNA and proteins considerably reduced (P < 0.01) in all three dosages given. was employed in order to assess hematological par