The eflicacy  of six formula from chloropyrifos against tem1ite

Microterotermes - diversus on citrus tree orchards has been

tested years .

Data!rom field trials confirmed that Dursbau 4TC, chlorpyrifos -

500 EC and Talaban 40,8 TC at rate 100 mL L protected citrus trees for two years.  While ch1orfate. 40.8 TC, Dormate 40,8TC, Yamasban

40,8 TC protected  them for 16,16 and 12 months respectively at the same concentration.

But the rate of 5m1/ L of Dursban, chropyfros 500 EC , Chlorfat,

Tafabun yamashan and Dormate protected the trees tor 24,16,4,4,2

and 4 months  , respectively .

Bacterial water pollution is a genuine general wellbeing concern since it causes various maladies. Antimicrobial nanofibers can be integrated by incorporating nanobiocides, for example, silver nanoparticles into nanofibers. Nylon 6 was dissolved in formic acid at a concentration of (25 wt. %) and tough antibacterial (AgNO₃/Nylon) nanofibers were produced utilizing electrospinning system. Polymer solution was tested before accomplishing electrospinning process to acquire its surface tension, electric conductivity and viscosity, where every one of those parameters increased relatively with increasing concentration of (AgNO₃) additions. SEM and EDX spectra were utilized to focus on the morphology, surface elemental mem

Polypyrrole/silver (PPy/Ag) nanocomposites was synthesized via a chemical oxidative method. The AFM analysis is performed to study the surface roughness, morphology and size distribution of the PPy particles and PPy-ag nanocomposites. The results indicated that as the concentration of Ag in the nanocomposite increases, the roughness also increases. The size of nanoparticles was also evaluated and found in the range of 15 nm to 125 nm. The PPy/Ag nanocomposites exhibited an effectiveness against Gram-negative Escherichia coli showing an inhibition zone of 4mm and displayed poor efficacy against Gram-positive Staphylococcus aureus. Based on given adequate antibacterial characteristics of PPy/Ag nanocomposites, it can be identified as

Background: With the increasing demand on esthetic orthodontic appliances, discoloration of clear elastomeric chains and modules remains an issue which concerns both orthodontics and patients. This in vitro study was conducted to evaluate the effect of exposing stretched clear elastomeric chains from six different companies (Ortho Technology, Ormco, Ortho Organizer, American Orthodontics, Opal and G&H companies) to three types of dietary media (tea, coffee and turmeric). Materials and methods: A total of 960 lengths of six modules were cut from short type elastomeric chain; 160 pieces from each brand. The specimens were stretched 50%, placed on plastic boards, and incubated in water at 37°C for 1 day, 7 days, 14 days and 28 days. Once a

Objective. This study aimed to evaluate and compare the force degradation of two types of elastomeric chains following different periods of immersion in zinc-containing mouthwashes. Materials and Methods. Four hundred and forty pieces of Elasto-Force and Super Elasto-Force elastomeric chains were divided into two control and eight experimental groups. The pieces were stretched to 25 mm on pins mounted on an acrylic block and stored in distilled water at 37°C. The experimental groups were immersed in four different types of mouthwash for one minute twice a day throughout the test period. Ten continuous thermocycles per day between cold and hot water baths (5–55°C) were carried out. Forces were measured at six-time intervals (in

To assess the biochemical, mechanical and structural characteristics of retained dentin after applying three novel bromelain‑contained chemomechanical caries removal (CMCR) formulations in comparison to the conventional excavation methods (hand and rotary) and a commercial papain‑contained gel (Brix 3000). Seventy‑two extracted permanent molars with natural occlusal carious lesions (score > 4 following the International Caries Detection and Assessment System (ICDAS‑II)) were randomly allocated into six groups (n = 12) according to the excavation methods: hand excavation, rotary excavation, Brix 3000, bromelain‑contained gel (F1), bromelain‑chloramine‑T (F2), and bromelain chlorhexidine gel (F3). The superficial and deepe

The study included the extraction of volatile oil from Mentha piperita which was 1.3 % in the leaves and flowers . Volatile oil of the Mentha piperita leaves had special aromatic odour, pale yellow color, slightly pungent taste . The specific gravity and refractive index were (0.9794) and ( 1.464) respectively. The inhibition activity of the Mentha piperita Volatile oil extracts were studied on some pathogenic microorganisms like Staphylococcus aureus, Salmonella typhi, Escherichia coli, Proteus sp, and Klebsiella pneumoniae . The result showed that the volatile oil had an inhibition effect on the growth of all microorganisms, and it gave the higher inhibition effect on the growth of S. aureus in which the inhibition zone reached to 2

Background: One of the major problems in endodontics is micro-leakage of root canal fillings which might contribute to the failure of endodontic treatment. To avoid this problem, a variety of sealers have been tested. The objective of this, in vitro, study was to evaluate the shear bond strength of four resin based sealers (AH plus, silver free AH26, RealSeal SE and Perma Evolution permanent root canal filling material) to dentin. Materials and Methods: Forty non-carious extracted lower premolars were used. The 2mm of the occlusal surfaces of teeth were sectioned, to expose the dentin surface. The exposed dentin surfaces of teeth were washed with 5ml of 2.5% NaOCl solution followed by 5ml of 17 % EDTA then rinsed by deionized water to remov

In view of this work, plasma nitriding was executed on Ti-6Al-4V and the effect of nitriding by using glow discharge with 2 mbar of Ar+N₂ gas on corrosion resistance with different nitriding time and studied. The structure properties and the external appearance for alloys were performed with x-ray diffraction and optical microscopic. The investigation of XRD indicates the Ti alloys are polycrystalline with a cubic type (bcc). When the external appearance of the surface indicates was of β+α structure which have been better technical properties on biomedical application. The biocompatibility investigation of nitride alloys in vitro medium containing human body fluid: we showed a layer of hydroxyapatite HAP which might