This study aimed to evaluate the surface changes of commercial pure Titanium disks (CP Ti) and the Ti 13Nb 13 Zr (Alloy) with a zigzag pattern of laser surface treatment. In vitro, experimental study of CNC Laser treatment on the CP Ti and Alloy disks. Texturing the surfaces of CP Ti and Alloy disks via CNC laser, the sample disks were analyzed using surface roughness, wettability and FESEM. The FESEM revealed a proper increase in the surface texturing and roughness on macro and micro measures without crack formation or dramatic change of the core substance of the CP Ti and Alloy disks. The CNC laser is an effective and suitable method for surface texturing CP Ti and Alloy for dental implantology. Keywords: Commercial pure Titanium;

Well integrity is a vital feature that should be upheld into the lifespan of the well, and one constituent of which casing, necessity to be capable to endure all the interior and outside loads. The casing, through its two basic essentials: casing design and casing depth adjustment, are fundamental to a unique wellbore that plays an important role in well integrity. Casing set depths are determined based on fracturing pressure and pore pressure in the well and can usually be obtained from well-specific information. Based on the analyzes using the improved techniques in this study, the following special proposition can be projected: The selection of the first class and materials must be done correctly and accurately in accordance with

A new simple and sensitive spectrophotometric method for the determination of trace amount of Co(II) in the ethanol absolute solution have been developed. The method is based on the reaction of Co(II) with ethyl cyano(2-methyl carboxylate phenyl azo acetate) (ECA) in acid medium of hydrochloric acid (0.1 M) givining maximum absorbance at ((λmax = 656 nm). Beer's law is obeyed over the concentration range (5-60) (μg / ml) with molar absorptivity of (1.5263 × 103 L mol-1 cm-1) and correlation coefficient (0.9995). The precision (RSD% ˂ 1%). The stoichiometry of complex was confirmed by Job's method which indicated the ratio of metal to reagent is (2:1). The studied effect of interference elements Zn(II), Cu(II), Na(I), K(I), Ca(II) and Mg

In this research, Mn-doped TiO2 thin films were grown on glass, Si and OIT/glass substrates by R.F magnetron sputtering technique with thicknesses (250 nm) using TiO2:Mn target under Ar gas pressure and power of 100 Watt. Through the results of X-ray diffraction, the prepared thin films are of the polycrystallization type after the process of annealing at 600°C for two hour The average crystalline size were 145.32, 280.97 and 261.23 nm for (TiO2:Mn) thin film on glass, Si and OIT/glass substrates respectively, while the measured surface roughness is between 0.981nm and 1.14 nm. The fabricated (TiO2:Mn) thin film on glass sensors have high sensitivity for hydrogen( H2 reducing gas) compared to the sensitivity for hydrogen gas on Si and OIT/

The present research was conducted to reduce the sulfur content of Iraqi heavy naphtha by adsorption using different metals oxides over Y-Zeolite. The Y-Zeolite was synthesized by a sol-gel technique. The average size of zeolite was 92.39 nm, surface area 558 m²/g, and pore volume 0.231 cm³/g. The metals of nickel, zinc, and copper were dispersed by an impregnation method to prepare Ni/HY, Zn/HY, Cu/HY, and Ni + Zn /HY catalysts for desulfurization. The adsorptive desulfurization was carried out in a batch mode at different operating conditions such as mixing time (10,15,30,60, and 600 min) and catalyst dosage (0.2,0.4,0.6,0.8,1, and 1.2 g). The most of the sulfur compounds were removed at 10 min for all catalyst ty

The molluscicidal effects of herbicide 2, 4-D were studied against tow species of freshwater snail Bulinus truncatus and Melanopsis nodosa by short term experiments. Calculated values of lethal concentrations (LC50 and LC100) were maid to two spices for different period of time 24hr, 48hr, 72hr and 96hr. The study had showed that the herbicide 2, 4-D was toxic against the tow species. The toxicity of the herbicide was low or unknown in low concentrations in the first period of exposure 24and 48hr to two spices but it increase gradually with increase period of exposure. The spice of B.truncatus was more tolerant than the M.nodosa. All the individual of M nodosa was death while in B.truncatus the complete death was not appear until finish the

In this research, 5- membered heterocyclic compounds as oxazolidine-5-one J1-J5 derivatives were prepared using primary aromatic amine, aromatic carbonyl compounds and chloroacetic acid. By combining primary aromatic amines and aromatic carbonyl compounds, Schiff's bases were synthesized. Schiff bases are used with the chloroacetic acid compound to prepare oxazolidine-5-one J1-J5 derivatives. The compounds J1-J5 were described using NMR spectroscopy and FT-IR. .The biological efficacy was evaluated according to maximum inhibitory concentrations (MICs) toward Staphyloccoccus aureus and Esherichia coli. The best MIC was 210 μg ml-1 for J4 against the two pathogenic bacteria, while J1, J4, and J1 did not show any inhibitory effect against all