Background: Dental implants act as infrastructure for fixed restoration to look like as a natural tooth. Osseointegration is a biological events and considered as a base for success of dental implant. The aim of this study is to evaluate the bond strength between bone and Ti implant coated with mixture of nano hydroxyapatite-chitosan-collagen compared with Ti implants coated with nano hydroxyapatite implanted in rabbit tibia, after different period of implantation time (two and six weeks) by torque removal test. Material and methods: 36 screws of commercially pure titanium; 8mm in length and 3mm diameter , 18 screws coated with mixture of nano hydroxyapatite-chitosan-collagen and18 screws coated with nano hydroxyapatite by dip coating. St

Compounds of (ZnO)1-x(SnO 2 ) x were prepared with various proportions of tin oxide (SiO 2) (x = 0.0, 0.2, 0.4, 0.6, 0.8, 1.0) by mixing zinc oxide (ZnO) with highpurity tin oxide and then sintering the mixture in an oven at a temperature of 1000 °C for a period of 1 h. The resulting powders were ground and pressed into tablets of 1 cm diameter and 0.5 cm thickness. The properties of (ZnO) 1-x(SnO 2 ) x composites flms were prepared and studied as sensitive to the diferent gases NO2 and H2 S. Thin flms were prepared from (ZnO) 1-x(SnO 2 ) x via pulsed laser deposition method using glass and single crystal silicon for investigation the morphology and gas sensing properties with a thickness of 150 nm. The morphology examinat

This study provides a systematic and bibliometric review of ASTM F75 cobalt–chromium alloys, focusing on microstructure and the shift from conventional to laser-based manufacturing. Using combined analytical methods, it evaluates microstructure, mechanical properties, corrosion behavior, and biocompatibility. Results show that laser-based techniques such as LPBF and DMLS produce finer grain sizes (1–10 µm vs. 50–200 µm), leading to improved hardness (20–40%) and tensile strength (15–30%). Despite challenges like residual stress and process optimization, these methods show strong potential for high-performance and sustainable applications.

This investigation reports application of a mesoporous nanomaterial based on dicationic ionic liquid bonded to amorphous silica, namely nano-N,N,N′,N′-tetramethyl-N-(silican-propyl)-N′-sulfo-ethane-1,2-diaminium chloride (nano-[TSPSED][Cl]2), as an extremely effectual and recoverable catalyst for the generation of bis(pyrazolyl)methanes and pyrazolopyranopyrimidines in solvent-free conditions. In both synthetic protocols, the performance of this catalyst was very useful and general and presented attractive features including short reaction times with high yields, reasonable turnover frequency and turnover number values, easy workup, high performance under mild conditions, recoverability and reusability in 5 consecutive runs without lo

This study expands the state of the art in studies that assess torsional retrofit of reinforced concrete (RC) multi-cell box girders with carbon fiber reinforced polymer (CFRP) strips. The torsional behavior of non-damaged and pre-damaged RC multi-cell box girder specimens externally retrofitted by CFRP strips was investigated through a series of laboratory experiments. It was found that retrofitting the pre-damaged specimens with CFRP strips increased the ultimate torsional capacity by more than 50% as compared to the un-damaged specimens subjected to equivalent retrofitting. This indicated that the retrofit has been less effective for the girder specimen that did not develop distortion beforehand as a result of pre-loading. From

This study deals with the elimination of methyl orange (MO) from an aqueous solution by utilizing the 3D electroFenton process in a batch reactor with an anode of porous graphite and a cathode of copper foam in the presence of granular activated carbon (GAC) as a third pole, besides, employing response surface methodology (RSM) in combination with Box-Behnk Design (BBD) for studying the effects of operational conditions, such as current density (3–8 mA/cm2), electrolysis time (10–20 min), and the amount of GAC (1–3 g) on the removal efficiency beside to their interaction. The model was veiled since the value of R2 was high (>0.98) and the current density had the greatest influence on the response. The best removal efficiency (MO Re%)