New series of imidazole[1,2-a]pyridine-sulfonamides was designed and synthesized from 2-aminopyridine, which was reacted with p-bromo phenacyl bromide in the present of MgO to produce the corresponding imidazole[1,2-a]pyridine, which was then reacted with chlorosulfonic acid to produce 2-(4-bromophenyl)imidazole[1,2-a]pyridine-3-sulfonyl chloride [2]. Following that, treatment of (2) with different amines using the grand method to generate imidazole [1,2-a] pyridine sulfonamides. All the synthesized compounds have been characterized by FTIR, 1HNMR and 13CNMR and C.H.N analysis. The DFT, POM analysis and molecular docking were carried out on for all final compounds to investigate drug like attributes, and the results revealed showed that the

Complexes of Au (III), Pd (II), Pt (IV ) and Rh(III) with S–propynyle-2- thiobenzimidazole (BENZA) have been prepared and characterized by IR and UV- Visible spectral methods in addition to magnetic and conductivity measurements and micro–elemental analysis (CHN).The probable structures of the new complexes have been suggested.

A simple ,accurate and sensitive spectrophotometric method has been developed the determination of Cobalt(II) and Cupper (II) .The method is based on the chelation of Co(II) and Cu(II) ions with 4-(4´-pyrazolon azo) -2-Naphthol(APAN) in aqueous medium . The complexes have a maximum absorption at (513) and (506) nm and ? max 0.531×10 4 and 0.12×10 5 L.mol -1.cm -1 for Co(II) and Cu(II) respectively .The reagent and two complexes have been prepared in ethanolic solution.The stoichiometry of both complexes were found to be 1:2 (metal :legend) .The effects of various cations and anions on Co(II) and Cu(II) determination have been investigated .The stability constants and standard deviations for Co(II) and Cu(II) 0.291 x107 ,0.909X108 L.mol

Background: Alginate impression material is the irreversible hydrocolloid material that is widely used in dentistry. The contact time between alginate and gypsum cast could have a detrimental effect on the properties of the gypsum cast. The objective of this study is to evaluate the impact of various contact time intervals of Alginate impressions & type III dental stone on surface properties of stone cast. Materials and Methods: Time intervals tested were 1hour, 6 hours and 9 hours. Surface properties of stone cast evaluated were surface detail reproduction, hardness and roughness. Surface detail reproduction was determined using cylindrical brass test block in accordance with ISO 1563. Surface roughness was measured by profilometer

Striae distensae SD or stretch mark are frequent skin lesion that cause considerable aesthetic concern. The 1064nm long pulsed Nd:YAG Laser has been used to promote an increase in dermal collagen and is known to be a Laser that has a high affinity to vascular chromphores. Also by using fractional CO₂ Laser 10600nm as an effective modality in treatment of striae distensae SD. It works to stimulate fibroblast and enhance Collagen formation, which is important for newly generated skin tissue.

Objectives: This study aims to verify the efficacy of long pulsed Nd: YAG Laser (1064nm) in the treatment of immature striae distensae (SD) and the efficacy of C0₂ fractional Laser (10600nm) in treatment o

This study describes the preparation of a new bidentate Schiff base derived from the condensation of Isatin-3-hydrazone with 2-acetylthiophene and the preparation of new series of complexes with a good yield. The prepared ligand was characterized by IR, UV-Vis, C.H.N.S elemental analysis, 1H and 13C NMR, LC-Mass spectroscopy, and physical measurements. Its complexes were analyzed by C.H.N.S elemental analyses, UV-Vis., FTIR, NMR, LC-Mass Spectra, atomic absorption spectroscopy, magnetic susceptibility, and conductivity measurements The results from spectroscopy and measurement studies showed that the ligand coordinated to the metal ion as a bidentate ligand via oxygen and nitrogen, forming an octahedral geometry around it. In vitro antimicr

The study aims to investigate the effect of Al2O3 and Al additions to Nickel-base superalloys as a coating layer on oxidation resistance, and structural behavior of nickel superalloys such as IN 738 LC. Nickel-base superalloys are popular as base materials for hot components in industrial gas turbines such as blades due to their superior mechanical performance and high-temperature oxidation resistance, but the combustion gases' existence generates hot oxidation at high temperatures for long durations of time, resulting in corrosion of turbine blades which lead to massive economic losses. Turbine blades used in Iraqi electrical gas power stations require costly maintenance using traditional processes regularly. These blades are made

The construction of highly safe and durable buildings that can bear accident damage risks including fire, earthquake, impact, and more, can be considered to be the most important goal in civil engineering technology. An experimental investigation was prepared to study the influence of adding various percentages 0%, 1.0%, and 1.5% of micro steel fiber volume fraction (Vf) to reactive powder concrete (RPC)—whose properties are compressive strength, splitting tensile strength, flexural strength, and absorbed energy—after the exposure to fire flame of various burning temperatures 300, 400, and 500 °C using gradual-, foam-, and sudden-cooling methods. The outcomes of this research proved that the maximum reduction in mechanical prop

This research foxed on the effect of fire flame of different burning temperatures (300, 400 and 500)oC on the compressive strength of reactive powder concrete (RPC).The steady state duration of the burning test was (60)min. Local consuming material were used to mixed a RPC of compressive strength around (100) MPa. The tested specimens were reinforced by (3.0) cm hooked end steel fiber of (1100) MPa yield strength. Three steel fiber volume fraction were adopted in this study (0, 1.0and 1.5)% and two cooling process were included, gradual and sudden. It was concluding that increasing burning temperature decreases the residual compressive strength for RPC specimens of(0%) steel fiber volume fraction by (12.16, 19.46&24.49) and (18.20, 27.77 &3