Porous silicon (PS) layers are prepared by anodization for
different etching current densities. The samples are then
characterized the nanocrystalline porous silicon layer by X-Ray
Diffraction (XRD), Atomic Force Microscopy (AFM), Fourier
Transform Infrared (FTIR). PS layers were formed on n-type Si
wafer. Anodized electrically with a 20, 30, 40, 50 and 60 mA/cm2
current density for fixed 10 min etching times. XRD confirms the
formation of porous silicon, the crystal size is reduced toward
nanometric scale of the face centered cubic structure, and peak
becomes a broader with increasing the current density. The AFM
investigation shows the sponge like structure of PS at the lower
current density porous begi

An experimental study is conducted on the utilization of the inlet ethanol injection technique in order to evaluate its impact on the performance of a two-shaft T200D mini-gas turbine engine. The maximum degradation recorded in power output was 32.8% at the climate temperature of 45^oC. Nevertheless, at that temperature, adding ethanol with Eth/LPG ratio of 20% by volume brought an enhancement in power output of 19.2% compared to normal LPG run. SFC of the dual-fuel engine ranked a level of 22% higher than that with pure LPG consumption. The overall efficiency suffered a maximum reduction of 14.4% with Eth/LPG fuel ratio of 20%, but when the loading was raised beyond 70% of the engine full load; the efficiency of dual-fuel engi

A field experiment was carried out during the spring season 2019 and 2020 to obtain a fast, uniform, and high field emergence ratio of maize seeds under a wide range of environmental conditions. Randomize complete block design in the split-plot arrangement was used with three replications. The first factor in the main plots was cultivars (5018, Baghdad3 and Sumer). The second factor in the sub-plots was seeds soaking with ascorbic and citric acids (100 mg L−1) each and humic (1 ml L−1) in addition to control treatment (seeds soaking with distilled water only). Results showed the superiority of soaking with humic acid significantly, as means of characteristics of field emergence in both seasons, respectively, were as follows: Last day of

Thin films of microcrystalline and nanocrystalline -silicon carbide and silicon, where deposited on glass substrate with substrate temperature ranging from 350-400C, with deposition rate 0.5nm per pulse, by laser induced chemical vapor deposition. The deposition induced by TEACO2 laser. The reactant gases (SiH4 and C2H4) photo decompose throughout collision associated multiple photon dissociate. Such inhomogeneous film structure containing crystalline silicon, silicon carbide and amorphous silicon carbide matrix, give rise to a new type of material nanocrystalline silicon carbide in which the optical transmittance is governed by amorphous SiC phase while nanocrystalline grain are responsible for the conduction processes. This new m

The study included adding antimony oxide to mixtures of coating metal surfaces (Enameling), after it was selected ceramic materials used in the coating metal pieces of the type of steel and cast iron in two layers. The first is called a ground coat and the second is a cover coat.
Ceramic materials layer for ground coat have been melted down in
platinum crucible at a temperature of 1200oC to prepare the glass
mixture (Frit). It was coated on metals at a temperature of 780oC for
two minutes, while the second layer was prepared glass mixture
(Frit) at a temperature of 1200oC, but was coated at a temperature of
760oC for two minutes.
Underwent tests crystalline state of powders (Frits) and enameled samples using X-ray di