Enhancing asphalt binder performance through nano-SiO2 and nano-CaCO3 additives: Rheological and physical insights
...Show More Authors

During the last two decades, nanomaterial application has gained a significant attraction into asphalt technology due to their effect in enhancing asphalt binder improving the asphaltic mixture. This study will modify the asphalt binder with two different nano types, nano SiO2 and CaCO3, at levels ranging from 1% to 7%. The resulting optimum nano-modified Asphalt will be subject to a series of rheological tests, including dynamic shear rheometer (DSR), Viscosity, and bending beam rheometer (BBR) to determine asphalt binder sensitivity towards low-medium-high temperature range. Results indicate that both nano types improved the physical characteristics of Asphalt, and 5% by weight of Asphalt was suggested as a reasonable dosage of nano-SiO2 and nano-CaCO3 based on the overall desirability analysis of physical tests. The viscosity and temperature sensitivity of bitumen were improved by adding nano SiO2 and CaCO3. On the other hand, the asphalt rutting resistance's capabilities were improved at higher temperatures. In contrast, it decreases resistance against fatigue at intermediate temperatures due to the lowest phase angles and higher loss moduli. The BBR test, however, reveals a modest decrease in bituminous anti-cracking.

Scopus Clarivate Crossref
View Publication
Publication Date
Wed Dec 30 2020
Journal Name
Journal Of Planner And Development
Enhancing livelihood through urban intensification
...Show More Authors

 The research deals with a modern concept in its applications and the studies it deals with, as the concept of urban densification is one of the most recent sustainable development strategies for cities.

Studies looking at the relationship between condensation and viability show mixed results. This study sheds light on how the built environment of dense urban areas affects the perceived quality of life of the population. How to enhance acceptance of dense life is an important question to investigate.

Adopting the concept of urban densification in city planning policies to be more sustainable and livable is of great importance by achieving efficient use of urban land and limiting urban sprawl, as well as reducing the

... Show More
View Publication Preview PDF
Publication Date
Tue Dec 24 2024
Journal Name
Journal Of Baghdad College Of Dentistry
Evaluation the effect of nano-fillers (TiO2, AL2O3, SiO2) addition on glass transition temperature, E-Moudulus and coefficient of thermal expansion of acrylic denture base material
...Show More Authors

Background: The PMMA polymer denture base materials are low in thermal and strength properties. The aim of the study was to investigate the change in glass transition temperature, E-Moudulus and coefficient of thermal expansion of acrylic denture base material by addition of Al2O3, TiO2 and SiO2nano-fillers in 5% by weight. Materials and methods: The type of polymerization is free radical bulk polymerization. one hundred twenty (120) specimens were prepared , the specimens were divided into four groups according to the material had been added (one control and three for Al2O3, TiO2 and SiO2nanocomposite) each group was subdivided in to three groups according to the test had been done on it, the degree of transition (Tg) was measured by The d

... Show More
View Publication Preview PDF
Publication Date
Sun Jun 01 2014
Journal Name
Baghdad Science Journal
Modification Of Rheological Properties Of Asphalt Effect Of Addition Of Asphaltenes And Oxidized Asphaltenes On The Compatibility Of Asphalt- Sulfur Blends
...Show More Authors

This study is a complementary one to an extended series of research work that aims to produce a thermodynamiclly stable asphalt –sulfur blend. Asphalt was physically modified wiht different percentages of asphaltenes , oxidized asphaltenes and then mixed with sulfur as an attempt to obtaine a stable compatible asphalt-sulfur blend. The homogeneneity of asphalt-asphaltenes[oxidized asphaltenes]-sulfur blends were studied microscopically and the results are prsented as photomicrographs. Generally more stable and compatible asphalt-sulfur blends were obtained by this treatment.

View Publication Preview PDF
Crossref
Publication Date
Thu Dec 31 2015
Journal Name
Al-khwarizmi Engineering Journal
Synthesis and Characterization of Nano-crystalline ZSM-5 Zeolite
...Show More Authors

Abstract

 Nano-crystalline ZSM-5 zeolite was synthesized by hydrothermal method using chelating agent and two gel compositions:Compositionɪ:Al2O3:86SiO2:5.5TPA:12.7Na2O:3.4Trien:3320H2O.Compositionɪɪ:Al2O3:68SiO2:5.4TPA:10Na2O:2.6Trien:2626H2O.Study of hydrothermal reaction factors on characteristics of nano- sized zsm-5 has been carried on ,among them are crystallization temperature, crystallization time and concentration of template ( TPAOH ) solution. Synthesis was accomplished in PTFE lined autoclave ( reactor ) . The product were characterized by X-ray diffraction ( XRD ),Atomic force microsc

... Show More
View Publication Preview PDF
Publication Date
Thu Jun 30 2022
Journal Name
Iraqi Journal Of Science
Investigate and Prepare silver Nano Particles Using Jet Plasma
...Show More Authors

Nano- particles (Ag NPs) are synthesized by using plasma Jet  argon gas. The prepared Ag NPs are characterized by Atomic Absorption Spectroscopy (AAS) The measure was performed for different time exposuring 15,30,45 and 60 sec. The results shows the low concentration of nano-silver time expose (15 sec) and very) and high concentration at 60 sec. The UV-VIS spectrometer for nano-silver different time exsposuring to plasma, shows the Surface Plasmon Resonance (SPR) appeared around 419 nm, and the  energy gab is 4.1 eV for the 15 second exposure and 1.6eV for 60 second exposure.  The Scanning Probe Microscope (SPM) is used to identify the characterization of silver  nanoparticles, the average diameter of nano-silver  for 15 second exp

... Show More
View Publication Preview PDF
Scopus (3)
Crossref (3)
Scopus Crossref
Publication Date
Mon Oct 01 2012
Journal Name
Iraqi Journal Of Physics
Structural and optical properties for nano GaxSb1-x films
...Show More Authors

Alloys of GaxSb1-x system with different Ga concentration (x=0.4, 0.5, 0.6) have been prepared in evacuated quartz tubes. The structure of the alloys were examined by X-ray diffraction analysis (XRD) and found to be polycrystalline of zincblend structure with strong crystalline orientation (220). Thin films of GaxSb1-x system of about 1.0 μm thickness have been deposited by flash evaporation method on glass substrate at 473K substrate temperature (Ts) and under pressure 10-6 mbar. This study concentrated on the effect of Ga concentration (x) on some physical properties of GaxSb1-x thin films such as structural and optical properties. The structure of prepared films for various values of x was polycrystalline. The X-ray diffraction analy

... Show More
View Publication Preview PDF
Publication Date
Sun Dec 30 2012
Journal Name
Iraqi Journal Of Chemical And Petroleum Engineering
Prediction of The Chemical Composition and Physical properties of Aged Asphalt Cement
...Show More Authors

In the present work a modification was made on three equations to represent the
experiment data which results for Iraqi petroleum and natural asphalt. The equations
have been developed for estimating the chemical composition and physical properties
of asphalt cement at different temperature and aging time. The standard deviations of
all equations were calculated.
The modified correlation related to the aging time and temperature with penetration
index and durability index of aged petroleum and natural asphalts were developed.
The first equation represents the relationship between the durability index with aging
time and temperature.

loge(DI)=a1+0.0123(2loge T

... Show More
View Publication Preview PDF
Publication Date
Thu Jun 15 2017
Journal Name
Journal Of Baghdad College Of Dentistry
Mechanical evaluation of nano hydroxyapatite, chitosan and collagen composite coating compared with nano hydroxyapatite coating on commercially pure titanium dental implant
...Show More Authors

Background: Dental implants act as infrastructure for fixed restoration to look like as a natural tooth. Osseointegration is a biological events and considered as a base for success of dental implant. The aim of this study is to evaluate the bond strength between bone and Ti implant coated with mixture of nano hydroxyapatite-chitosan-collagen compared with Ti implants coated with nano hydroxyapatite implanted in rabbit tibia, after different period of implantation time (two and six weeks) by torque removal test. Material and methods: 36 screws of commercially pure titanium; 8mm in length and 3mm diameter , 18 screws coated with mixture of nano hydroxyapatite-chitosan-collagen and18 screws coated with nano hydroxyapatite by dip coating. St

... Show More
View Publication Preview PDF
Crossref (3)
Crossref
Publication Date
Wed Mar 10 2021
Journal Name
Baghdad Science Journal
Effect of Adding (Binder-Plastisizer-Lubricat) on the Physical Properties of Kaolin
...Show More Authors

The study concern with the preparation of three type of mixtures; which are prepared from different percentage of polyvenil Butyral, Di-n-butyl phathalate and paraffin wax pastillated. The solvent used is Xylolzul analyses. After washing, Drying and milling the kaolin Dukhla, as a matrix in this study, and by using sieving Tech. The range of particle size used is less than and less than as a mesh batch. The added percentage from prepared mixture were 5% and 10% to 95% and 90% of the matrix respectively. Then disk samples were prepared by using a compaction pressure with heating. After cooling and drying the samples were undergo heat treatment in the range of (1250 – 1350) oC. The measurement of shrinkage and Dielectric properties sho

... Show More
View Publication Preview PDF
Crossref
Publication Date
Sat Dec 31 2016
Journal Name
Iraqi Journal Of Chemical And Petroleum Engineering
Synthesis Of Nano Ni-Mo/γ-Al2O3 CatalystSynthesis Of Nano Ni-Mo/γ-Al2O3 Catalyst
...Show More Authors

Nano γ-Al2O3 support was prepared by co-precipitation method by using different calcination temperatures (550, 600, and 750) oC. Then nano NiMo/γ-Al2O3 catalyst was prepared by impregnation method were nickel carbonate (source of Ni) and ammonium paramolybdate (source of Mo) on the best prepared nano γ-Al2O3 support at calcination temperature 550 oC. Make the characterizations for prepared nano γ-Al2O3 support at different temperatures and for nano NiMo/γ-Al2O3 catalyst like X-ray diffraction, X-ray fluorescent, AFM, SEM, BET surface area, and pore volume.

The N

... Show More
View Publication Preview PDF