Introduction: This study aimed to evaluate the impact of ozonated water on water sorption and solubility of heat-cure acrylic resin. Methods: Thirty-three samples of heat-cured acrylic resin were manufactured and divided into three groups: control, immersion for 10 and 20 minutes in ozonated water. Water sorption and water solubility tests were carried out in line with ADA Standard No. 12 for denture-base acrylic resin. Data were analyzed using one-way ANOVA at a significance level of 5%. Results: There was a nonsignificant difference between the control and experimental groups regarding water sorption (P

Copper oxide nanoparticles (CuO NPs) were synthesized by two methods. The first was chemical method by using copper nitrate Cu (NO3)2 and NaOH, while the second was green method by using Eucalyptus camaldulensis leaves extract and Cu (NO3)2. These methods easily give a large scale production of CuO nanoparticles. X-ray diffraction pattern (XRD) reveals single phase monoclinic structure. The average crystalline size of CuO NPs was measured and used by Scherrer equation which found 44.06nm from chemical method, while the average crystalline size was found from green method was 27.2nm. The morphology analysis using atomic force microscopy showed that the grain size for CuO NPs was synthesized by chemical and green methods were 77.70 an

Copper oxide nanoparticles (CuO NPs) were synthesized by two methods. The first was chemical method by using copper nitrate Cu (NO3)2 and NaOH, while the second was green method by using Eucalyptus camaldulensis leaves extract and Cu (NO3)2. These methods easily give a large scale production of CuO nanoparticles. X-ray diffraction pattern (XRD) reveals single phase monoclinic structure. The average crystalline size of CuO NPs was measured and used by Scherrer equation which found 44.06nm from chemical method, while the average crystalline size was found from green method was 27.2nm. The morphology analysis using atomic force microscopy showed that the grain size for CuO NPs was synthesized by chemical and green methods were 77.70 and 89.24

To investigate the antiplaque and antigingivitis efficacy in addition to evaluating side effects and subjects’ perceptions of three commercially available mouthwashes.

The research deals with the lyrical introduction in the commentary of Tarfa bin al-Abd as a formative system characterized by flexibility and richness of imagination, which achieved a formative treatment and a unique construction within the structures of the structural and semantic language. I dealt with the poetic verses represented by the lyrical introduction as a formative hypothesis, basing its goal on a methodological framework distributed on the problem that was summarized by the following question: Is it possible to look at the poetic pattern within the pre-Islamic poem / hanging blinking as a model, in its plastic dimensions and to identify the stylistic treatment that achieves the formation space within the poetic text. The rese

Acinetobacter baumannii received attention for its multi-drug resistant associated with many severe infections and outbreaks in clinical environment. The aims of the study are to investigate the antibiotic susceptibility profile of clinically isolated A. baumannii, biofilm production, and the efficiency of Low Frequency Ultrasound (LFU) and honey to attenuate biofilm production. A total of 100 samples were taken from different sources from Baghdad hospitals. The susceptibility patterns revealed the percentage of pan drug resistant (PDR) isolates were 1.5 %, 72.7 % were extended drug resistant (XDR), 16.7 % were multidrug resistant (MDR), and 9.1 % were non MDR and sensitive to most antibiotics used. The ability to form

Background: This study aimed to evaluate the effect addition of polyester fibers on the some mechanical properties of heat cured acrylic resin (implant strength, flexural strength and hardness) Materials and methods: Ninety specimens were used in the study. Thirty specimens were used for impact strength measurements (80mm X 10mm X 4mm) length, width and thickness respectively. The specimens divided into three test groups (n=10), first group formed from heat cure acrylic resin without fiber reinforcement. Second group was formed from heat cure acrylic resin was reinforced with 2 mm length polyester fiber and third group was formed from heat cure acrylic resin reinforced with 4mm length polyester fiber, impact strength measured by impact test

The influence of fiber orientation and water absorption on fatigue crack growth resistance for cold cure acrylic (PMMA) reinforced by chopped and woven -glass-fibers were investigated. A weight of 2 g for chopped fibers and the same weight for woven -glass-fibers (one layer) were used to prepare samples. Some of these samples would storage in dry condition; the others were immersed in water for 15 days. Fatigue test was carried out. The results shows that, for PMMA, the initial bending stress for dry specimen was 3.392 N/cm2 and the number of cycles were 1364, the initial bending stress for wet samples was 4.20 N/cm2, and the number of cycles was 2411. The samples would cut in two pieces because of the cracks would propagated fast during

P. aeruginosa is a famous bacterium that causes several diseases and has a high ability to be a multidrug resistant organism that is linked with the formation of biofilm. This study aimed to investigate tssC1 gene role in the resistance of different antibiotics in the presence of biofilm. We constructed biofilm for the isolates under the study and showed the effect of different antibiotics on biofilm formation and maturation. The presence of the gene was detected through achieving PCR reaction. Finally, tssC1 gene variation was determined through sequencing and aligning the sequencing products. The results showed that most of the isolates (80%) formed biofilm that played a role in the resistance of different antibiotics which could

Low conversion copolymerization of acrylamide AM (monomer-1) have been conducted with acrylic acid AA in dry benzene at 70°C , using Benzoyl peroxide BPO as initiator . The copolymer composition has been determined by elemental analysis. The monomer reactivity ratios have been calculated by the Kelen-Tudos and Finman-Ross graphical procedures. The derived reactivity ratios (r1, r2) are: (0.620, 0.996) for (AM / AA) systems , and found that the reactivity of the monomer AA is more than the monomer AM in the copolymerization of (AA/AM) system. The reactivity ratios values were used for microstructures calculation.