الوصف New complexes of Cu (ll), Ni (II)„Co (II), and Zn (ll) with 2-amino-5-p-Flouro Phenyl 1, 3, 4-Thiadiazole have been synthesized. The products were isolated, studied and characterized by physical measurements, ie,(FT-IR)„UV-Vis and the melting points were determined. The new Schiff base (L) has been used to prepare some complexes. The prepared complexes were identified and their structural geometry were suggested

In this research, Schiff bases derived from the reaction of anthrone with different heterocyclic amines have been described. The resulted Schiff base compounds were reacted with various nucleophiles in order to obtain new heterocyclic derivatives. Chemical structures of all products were confirmed by IR, 1H-, 13C-NMR spectral data and elemental analysis. All synthesized compounds were in vitro tested against a standard strain of pathogenic microorganism including Gram +ve bacteria (Staphylococcus aureus), Gram –ve bacteria (Escherichia coli), and fungi (Candida albicans).

A new ligand [N-(3-acetylphenylcarbamothioyl)-4-methoxybenzamide](MAA) was synthesized by reaction of 4-methoxybenzoylisothiocyanate with 3-aminoacetophenone,The ligand was characterized by elemental microanalysis C.H.N.S, FT-IR, UV-Vis and 1H,13CNMR spectra, some transition metals complexes of this ligand were prepared and characterized by FT-IR, UV-Vis spectra, conductivity measurements, magnetic susceptibility and atomic absorption, From obtained results the molecular formula of all prepared complexes were [M(MAA)2(H2O)2]Cl2 (M+2 =Mn, Co, Ni, Cu, Zn, Cd and Hg),the proposed geometrical structure for all complexes were octahedral

A new ligand [N-(4-chlorobenzoyl amino) -thioxomethyl] valine (cbv) is synthesized by reaction of 4- chloro benzoyl iso thio cyanate with valine acid. The ligand is Characterized by elemental analysis ,FT-IR, and 13C 1H NMR spectra, some transition metals complex of this ligand were prepared and Characterized by FTIR , UV-Visible spectra , conductivity measurement's ,magnetic susceptibility , atomic absorption and determination of molar ratio (M:L), from results obtained , the following formula [M(cbv)2] where M+2 =Mn, Fe ,Co , Ni , Cu,Zn,Cd, and Hg and the proposed molecular structure for these complexes as tetrahedral geometry, except copper complex is have square planer geometry

A new ligand ( 4- methoxy benzoyl ) carbamothioyl ) Glycine (MCG) is synthesized by reaction of (4- methoxy benzoyl isothiocyanate) with Glycine(1:1). It is characterized by micro elemental analysis (C.H.N.S.), FT-IR, (UV-Vis) and 1H and 13CNMR spectra. Some metals ions complexes of this ligand were prepared and characterized byFT-IR,UV-Visible spectra, conductivity measurements, magnetic susceptibility and atomic absorption. From results obtained, the following formula [M(MCG)2] where M2+ = Mn, Co, Ni, Cu, Zn, , Cd and Hg, the proposed molecular structure for these complexes as tetrahedral geometry, except copper complex is has square planer geometry.

This study focuses on producing wood-plastic composites using unsaturated polyester resin reinforced with Pistacia vera shell particles and wood industry waste powder. Composites with reinforcement ratios of 0%, 20%, 30%, and 40% were prepared and tested for thermal conductivity, impact strength, hardness, and compressive strength. The results revealed that thermal conductivity increases with reinforcement, while maintaining good thermal insulation, reaching a peak value of 0.633453 W/m·K. Hardness decreased with increased reinforcement, reaching a minimum nominal hardness value of 0.9479. Meanwhile, impact strength and compressive strength improved, with peak values of 14.103 k/m² and 57.3864568 MPa, respectively. The main aim is to manu

Microwave heating is caused by the ability of the materials to absorb microwave energy and convert it to heat. The aim of this study is to know the difference that will occur when heat treating the high strength aluminum alloys AA7075-T73 in a microwave furnace within different mediums (dry and acidic solution) at different times (30 and 60) minutes, on mechanical properties and fatigue life. The experimental results of microwave furnace heat energy showed that there were variations in the mechanical properties (ultimate stress, yielding stress, fatigue strength, fatigue life and hardness) with the variation in mediums and duration times when compared with samples without treatment. The ultimate stress, yielding stress and fatigue streng

Thin films were prepared from poly Berrol way Ketrrukemaaih pole of platinum concentrations both Albaarol and salt in the electrolytic Alastontrel using positive effort of 7 volts on the pole and the electrical wiring of the membrane record

AA3003-H14 aluminum alloy plates were welded by friction stir welding and TIG welding.
Fatigue properties of the welded joints were evaluated based on the superior tensile properties for
FSW at 1500 rpm rotational speed and 80 mm/min welding speed. However, there is not much
information available on effect of welding parameters with evolution of fatigue life of friction stir
welds. The present study experimentally analyzed fatigue properties for base, FSW, and TIG welds
of AA 3003-H14 aluminum alloy. Fatigue properties of FSW joints were slightly lower than the
base metal and higher than TIG welding.