Physical and chemical adsorption analyses were carried out by nitrogen gas using ASTM apparatus at 77 K and hydrogen gas using volumetric apparatus at room temperature, respectively. These analyses were used to determine the effect of coke deposition and poisoning metal on surface area, pore size distribution, and metal surface area of fresh and spent hydrodesulphurization catalyst Co-Mo\Al2O3 . Samples of catalyst (fresh and spent) used in this study are taken from AL-Dura refinery. The results of physical adsorption shows that surface area of spent catalyst reduced to third compare with fresh catalyst and these catalysts exhibit behavior of type four according to BET classification ,so, the pores of these samples are cylindrical, and the pores of fresh catalyst suffers during the hydrodesulphurization . The result of chemical adsorption shows that the metal surface area of fresh catalyst is 50.72 m2/g while it reduced to 39.04 m2 /g for spent catalyst.
Esterification considers the most important reaction in biodiesel production. In this study, oleic acid was used as a suggested feedstock in order to study and simulate production of biodiesel. The batch esterification reaction of oleic acid was carried out at various operating conditions; temperature from 40 to 70 °C, ethanol to oleic acid molar ratio from 3/1 and 6/1 and a reaction time up to 180 min.
The catalyst used was prepared NaY zeolite, which is added to the reaction mixture as 2, 5 and 10 wt.% of oleic acid.
The results show that the optimum conditions, gives 0.81 conversion of oleic acid, were 6/1 molar ratio of ethanol/oleic acid, 5 wt.% NaY relative to initial oleic acid, 70°C and 60 minutes. The activation energy o
The current research includes the adsorption of Rhodmine-B Dye on the surface of Citrus Leaves using the technique of UV. Vis spectrophotometer to determine data of quantitative adsorption at various contact time, ionic strength, PH and temperature conditions. As a function of temperatures 25,35,45,55 0C, the dsorption phenomenon was examined, and the results showed that Rhodamine-B adsorption Citrus leaves rose with increasing temperatures on the surface (endothermic process). Using various NaCl solution concentrations, the effect of ionic strength on adsorption has also been studied. Increasing the importance of ionic strength has been shown to improve the amount of adsorption of Rhodamine-B on citrus leaves at constant temp
... Show MoreEquilibrium adsorption isotherm for the removal of trifluralin from aqueous solutions using ? –alumina clay has been studied. The result shows that the isotherms were S3 according Giels classification. The effects of various experimental parameters such as contact time, adsorbent dosage, effect of pH and temperature of trifluralin on the adsorption capacities have been investigated. The adsorption isotherms were obtained by obeying freundlich adsorption isotherm with (R2 = 0.91249-0.8149). The thermodynamic parameters have been calculated by using the adsorption process at five different temperature, the values of ?H, ?G and ?S were (_1.0625) kj. mol-1, (7.628 - 7.831) kj.mol-1 and (_2.7966 - _2.9162) kg.
... Show MoreThe present work describes the adsorption of Ba2+ and Mg2+ions from aqueous solutions by activated alumina in single and binary system using batch adsorption. The effect of different parameters such as amount of alumina, concentration of metal ions, pH of solution, contact time and agitation speed on the adsorption process was studied. The optimum adsorbent dosage was found to be 0.5 g and 1.5 g for removal of Ba2+ and Mg2+, respectively. The optimum pH, contact time and agitation speed, were found to be pH 6, 2h and 300 rpm, respectively, for removal of both metal ions. The equilibrium data were analyzed by Langmuir and Freundlich isotherm models and the data fitted well to both isotherm modes as indicated by higher correlation of deter
... Show MoreHydrogen sulfide removal catalyst was prepared chemically by precipitation of zinc bicarbonate at a controlled pH. The physical and chemical catalyst characterization properties were investigated. The catalyst was tested for its activity in adsorption of H2S using a plant that generates the H2S from naphtha hydrodesulphurization and a unit for the adsorption of H2S. The results comparison between the prepared and commercial catalysts revealed that the chemical method can be used to prepare the catalyst with a very good activity.
It has observed that the hydrogen sulfide removal over zinc oxide catalyst follows first order reaction kinetics with activation energy of 19.26 kJ/mole and enthalpy and e
... Show MoreIncreasing demands on producing environmentally friendly products are becoming a driving force for designing highly active catalysts. Thus, surfaces that efficiently catalyse the nitrogen reduction reactions are greatly sought in moderating air-pollutant emissions. This contribution aims to computationally investigate the hydrodenitrogenation (HDN) networks of pyridine over the γ-Mo2N(111) surface using a density functional theory (DFT) approach. Various adsorption configurations have been considered for the molecularly adsorbed pyridine. Findings indicate that pyridine can be adsorbed via side-on and end-on modes in six geometries in which one adsorption site is revealed to have the lowest adsorption energy (–45.3 kcal/mol). Over a nitr
... Show MoreThe present study intends to prepare nanofibers mat of polyacrylonitrile by electrospinning technique and investigates their adsorption capacity to Congo red dye from the aqueous solution, after characterize it by different techniques such as FTIR, SEM, EDA, XRD and BET. The influence factors on adsorption were studied including adsorbent dosage, initial concentration, contact time, pH and ionic strength. The results confirmed that the increasing in pH decreases the adsorption capacity. So, the optimum adsorbent dosage, initial concentration and contact time were 0.006 g, 25 mg/L and 150 min respectively. The isotherm models of Freundlich and Langmuir were applied on the experimental adsorption data to evaluate the maximum capacity and ener
... Show MoreCurrent study was carried out to determine the adsorption ability of the Multiwall carbon nanotubes (MWCNTs) by adsorption Malachite Green dye from an aqueous solution. Crystal structure of the materials was measured using powder X-rays diffraction (PXRD), UV–Vis diffuse reflectance and specific surface area (BET). Many parameters that affecting the adsorption process such as contact time, pH, adsorbent dosage, initial dye concentration and temperature were studied. The outcome showed that an increasing occurred in the adsorbent dosage and the rate of dye removal, and the best efficiency for Malachite Green dye removal was amounted 99. 11 %. The results were obtained at optimal reaction conditions were pH = 5.5, cata
... Show MoreDrug overdose and poisoning are common clinical problems and could occur with Diphenhydramine hydrochloride (DFH) (one of anti histaminic drug ). It therefore important to study the adsorption of the DFH on pharmaceutical adsorbents which could serve as possible antidotes for the emergency treatment of DFH overdose or poisoning when they occur. The rate and extent of adsorption of DFH on some pharmaceutical adsorbents, bauxite were investigated spectra photometrically also the effect temperature, pH, presence of sucrose as additive have been studied as well, adsorbent's weight and partical size.The equilibrium adsorption contact times were determined for clay surface. Adsorption isotherms have been analyzed by the freundlich model. The appa