The purpose of the current work was to evaluate the effect of Radiation of Gamma on the superconducting characteristics of the compound PbBr2Ca1.9Sb0.1Cu3O8+δ utilizing a 137Cs source at doses of 10, 15, and 20MRad. Solid state reaction technology was used to prepare the samples. Before and after irradiation, X-ray diffraction (XRD) and superconductor properties were examined. Results indicated that the tetragonal structure of our chemical corresponds to the Pb-1223 phase with an increase in the ratio c/a as a result of gamma irradiation. (Tc (onset) ) and on set temperature Tc (offset)) were also dropping from 113 to the 85.6 K and 129.5 to 97 K, respectively, for a transition temperatu

A new spectrophotometric method has been developed for the assay of olanzapine (OLN.) in pure and dosage forms. The method is based on the diazocoupling of (OLN.) with diazotized p-nitroaniline in alkaline medium to form a stable brown colored water-soluble azo dye with a maximum absorption at 405 nm.  The variables that affect the completion of reaction have been carefully optimized. Beer’s law is obeyed over the concentration range of (0.5-45.0 μg.mL^-1) with a molar absorptivity of 1.5777×10⁴ L.mol^-1.cm^-1.  The limit of detection was  0.3148  Î¼g.mL^-1 and  Sandell’s  sensitivity value was 0.0198 μg.cm^-2. The propose

This study evaluated the structural changes of enamel treated by the Regenerate system and carbon dioxide (CO2) laser against acid challenge. Thirty human enamel slabs were prepared and assigned into three groups: Group I: untreated (control); Group II: treated with the Regenerate system; and Group III exposed to CO2 laser. All specimens were subjected to an acid challenge (pH 4.5–7.0) for 14 days. Specimens were evaluated and compared at 120 points using five Raman microspectroscopic peaks; the phosphate vibrations ν1, ν2, ν3, and ν4 at 960, 433, 1029, and 579 cm−1, respectively, and the carbonate at 1070 cm−1, followed by Vickers microhardness test. The ratio of carbonate to phosphate was correlated to the equivalent mic

This work aimed to prepare and study the characteristic feature of lead nanoparticles (PbNPS) and follow its effects on some physiological aspects in rats.PbNPS was prepared by laser ablation of pure lead mass with a pulse of 500 and 100 mJ of energy. The results indicated that the wavelength was approximately 196 and the concentration was reported at 53,8967 mg / L. AFM, as the average diameter has been estimated at 69.93 nm. EFSEM shows the spherical shape of the particle.The experimental animals (rats) were divided into two groups, with seven rats for each one. The first group was a control and the second group was injected with 1 milliliter of PbNPS (53.8673 mg/l) per day for 45 days. Bioaccumulated lead ( in liver, spleen kidney and

Two field experiments were conducted during the season 2021-2022 in central Iraq represented by the Al-Muthanna governorate - Al-Majd District and Al-Qadisiyah governorate / Al-Nouriah Research Station to determine the productivity of the Baghdad 3 cultivar from spray foliar fertilization of Macro and Micro elements with alcoholic sugars and half the fertilizer recommendation for addition floor, three treatments were used for fertilization: T1 as the control treatment and T2 with alcoholic sugar fertilization at a concentration of 20 g.L-1 + the fertilizer combination of Macro and Micro elements, and T3 with alcoholic sugar fertilization at a concentration of 40 g.L-1 + the fertilizer combination of Macro and Microelements, at irrigation 55

In this work, we are obviously interested in a general solution for the calculation of the image of a single bar in partially coherent illumination. The solution is based on the theory of Hopkins for the formation of images in optical instruments in which it was shown that for all practical cases, the illumination of the object may be considered as due to a self – luminous source placed at the exit pupil of the condenser , and the diffraction integral describing the intensity distribution in the image of a single bar – as an object with half – width (U0 = 8 ) and circular aperture geometry is viewed , which by suitable choice of the coherence parameters (S=0.25,1.0.4.0) can be fitted to the observed distribution in various types of mi

PVC/Kaolinite composites were prepared by the melt intercalation method. Mechanical properties, thermal properties, flammability and water absorption percentage of prepared samples were tested. Mechanical characteristic such as tensile strength, elongation at break; hardness and impact strength (charpy type) were measured for all samples. It was found that the tensile strength and elongation at break of PVC composites decreased with increasing kaolinite loading. Also, the hardness of the composites increases with increase in filler content .The impact strength of the composites at the beginning increases at lower kaolinite loadings is due to the lack of kaolin adhesion to the matrix. However, at higher kaolin loadings. This severe agglom

Chitosan (CH) / Poly (1-vinylpyrrolidone-co-vinyl acetate) (PVP-co-VAc) blend (1:1) and nanocomposites reinforced with CaCO3 nanoparticles were prepared by solution casting method. FTIR analysis, tensile strength, Elongation, Young modulus, Thermal conductivity, water absorption and Antibacterial properties were studied for blend and nanocomposites. The tensile results show that the tensile strength and Young’s modulus of the nanocomposites were enhanced compared with polymer blend [CH/(PVP-co-VAc)] film. The mechanical properties of the polymer blend were improved by the addition of CaCO3 with significant increases in Young’s modulus (from 1787 MPa to ~7238 MPa) and tensile strength (from 47.87 MPa to 79.75 MPa). Strong interfacial

This study is concerned with the effect of Deep Cryogenic Treatment (DCT) at liquid nitrogen temperature (-196 o C) on the mechanical properties and performance of low carbon steel (A858). The tests specimens were divided in to two groups, the first group was subjected to the conventional heat treatment of normalizing, and the second group was also normalized then subjected to (DCT). The results have shown that after (DCT), the Hardness, Tensile properties and the impact energy absorbed were all slightly increased. However the fatigue test showed some positive improvement in fatigue limit by 20(N/mm2 ), and the volume wear rates at different loads were significantly decreased after (DCT). The changes in microstructure due to (DCT) were c

Cobalt substituted nickel copper ferrite samples with general formula Ni0.95-xCoxCu0.05Fe2O4, where (x= 0.00, 0.01, 0.02, 0.03, 0.04 and 0.05) were prepared by solid-state reactions method at 1373 K for 4h. The samples prepared were examined by X-ray diffraction (XRD(, atomic force microscope (AFM), Fourier transform infra-red spectroscopy (FTIR) and Vickers hardness. X-ray diffraction patterns confirm the formation of a single phase of cubic spinel structure in all the prepared samples . XRD analysis showed that the increase in the cobalt concentration causes an increase in the lattice constant, bulk density (ρm) and the x-ray density (ρx), whereas porosity (p) and crystallite size (D) decrease. The Topography of the surface observed