Background: The miswak is a teeth cleaning twig made from a twig of the Salvadora persica tree (known as arak in Arabic).A traditional alternative to the modern toothbrush, it has a long, well-documented history and is reputed for its medicinal benefits. It also features prominently in Islamic hygienical jurisprudence. Materials and methods: Twenty maxillary first premolars were treated with the selected solutions which included siwak water extract (5%, 10%) and sodium fluoride 0.05% for 2minutes once daily for 20 days interval, deionized water was used as control negative. Then the concentration of the dissolved calcium ion in the etching solution of 2N HCL was measured. Results: The least amount of the dissolved calcium ion was registere

Photovoltaic devices (PVs) were fabricated by spray-coating an ink of copper indium diselenide CuInSeR 2 R(CIS) nanocrystals as the light-absorbing layer. Without high-temperature post-deposition annealing, PVs were made on glass substrates with power conversion efficiencies of up to 1.5% and 0.9%, for Au and Mo coated respectively, under AM 1.5 illumination. UV–Vis spectrophotometer in the wavelength range 350–1500 nm. X-ray diffraction (XRD) and energy dispersive spectroscopy (EDS) analysis it is evident that CuInSeR 2 R have the chalcopyrite structure as the major phase and no secondary phase with a preferred orientation along (112) direction and The atomic ratio of Cu : In : Se in the nanocrystals is nearly 1 : 1 : 2.

Background: Aesthetic archwires are used to overcome the aesthetic problems of stainless steel wires but the color of the coating layer can be changed with time when exposed to oral environments. The aim of this study was to evaluate the degree of color change of different aesthetic archwires from different companies under different coloring solutions. Materials and Methods: One hundred fifty samples of coated archwires from three companies (Highland, G&H and Dany) were immersed in 5 solutions (artificial saliva, turmeric, tea, coffee and Miranda) to evaluate the degree of color changes after 7, 14 and 21 days using visible spectrophotometer. Data were collected and analyzed using one way ANOVA and post hoc Tukey’s tests. Resu

Abstract: Iatrogenic furcal root perforations are serious complications during dental treatment. This study was aimed to compare the sealing ability of new bioceramic root repair material TotalFill® with the other perforation repair materials (GIC, MTA and Biodentine) using a dye- extraction method.Materials and Methods: Forty extracted, human mandibular molars with non-fused well developed root were collected. Artificial perforations were made from the external surface of the teeth. Then the teeth were randomly divided into 4 experimental groups (n= 10) according to the type of repair material used in this study; Medifil glass ionomercement, TotalFill® bioceramic root repair material, BiodentineTM and MTA Plus. The specimens were then im

The electrical insulation of the manufacture sulfonated phenol-formaldehyde viscous material (product) has been studied with Polyvinyl-acetate (PVA) and toluene diisocyanate (TDI) blend has been prepared by fixing percentage by weight 3:1 and mixed with different percentages by weight of the product sulfonated phenol formaldehyde viscous mass (SPF). The Fourier transform infrared (FTIR) spectroscopy is done on (SPF) resin powder and prepared film of PVA-TDI-SPF viscous mass. The quality factor (Q), dissipation factor (D), parallel resistance (Rp), series resistance (Rs), parallel capacitance (Cp), series capacitance (Cs) and phase shift (?) are measured. The calculated maximum dielectric constant (??) is 3.49x107 at sample (1) wt.1% SPF vis

Mortar of ordinary Portland cement was blended with cockles shell
powder at different weight ratios to investigate the effect of powder
admixture on their strength and thermal conductivity. Results showed
that addition of cockles shell powder at 50% of mortar weight
improves hardness and compressive strength notably and reduces the
thermal conductivity of the end product. Results suggest the
possibility to incorporate cockles shell powders as constituents in
cement mortars for construction and plastering applications.

Todays, World is faced an energy crisis because of a continuous increasing the consumption of fuels due to intension demand for all types of vehicles. This study is one of the efforts dealing with reduce the weight of vehicles by using a new material of sandwich steel, which consists of two skin steel sheets with core of a polymer material. Resistance spot welding (RSW) can be easily implemented on metals; however a cupper shunt tool was designed to perform the resistance welding of sandwich steel with DP800 cover sheets to resolve a non-conductivity problem of a polymer core. Numerical simulations with SORPAS^®3D were employed to test the weldability of this new material and supported by many practical experiments. In conclus

Magnesium hydroxide was used as flame inhibitor to increased flame resistance for tires .Magnesium hydroxide was adding with (5%,10%) weight percents to rubber master batch of tire and then exposed the resulting material to a flame generated from gas torch with (10 mm) exposure distance . Method of measuring the surface temperature opposite to the flame was used to determine the heat transferred through tire material. The results were obtained shows enhanced flame resistance for tire by added magnesium hydroxide and this resistance increased by increasing hydroxide Percentage .

In this study, a packed bed was used to remove pathogenic bacteria from synthetic contaminated water. Two types of packing material substrates, sand and zeolite, were used. These substrates were coated with silver nanoparticles (AgNPs), which were prepared by decomposition of Ag ions from AgNO3 solution. The prepared coated packings were characterized using scanning electron microscopy, energy-dispersive X-ray spectroscopy and transmission electron microscopy. The packed column consisted of a PVC cylinder of 2 cm diameter and 20 cm in length. The column was packed with silver nanoparticlecoated substrates (sand or zeolite) at a depth of 10 cm. Four types of bacteria were studied: Escherichia coli, Shigella dysenteriae, Pseudomonas aerugi

Background: The development of orthodontic biomaterials that attract less biofilm has been a goal for decades. Adhesion and colonization of cariogenic streptococci are considered to play key roles in the development of enamel demineralization related to orthodontic materials. The aim of this study was to quantitatively evaluate the Mutans streptococci adhesion to coated orthodontic archwires (Epoxy and Teflon) and uncoated archwires (stainless steel and nickel-titanium) with respect to incubation time in the presence and absence of saliva. Material and Method: Six types of archwires stainless steel and nickel titanium with two type of coating (Epoxy, Teflon) were used in this study. Twelve specimens of each archwire were incubated in steri