New Fourteen compounds were synthesized in four steps. The first step included synthesis of 2-biphenyl fused ring of imidazo(1,2- a)pyrimidine from the reaction of 2-aminopyrimidine and biphenyl phenacyl bromide . The second step was introduced aldehyde group from the reaction of 2-biphenyl fused rings of imidazo(1,2-a)pyrimidine with POCl3 in presence of DMF and CHCl3. 3-Carbaladehyde derivatives of fused imidazo/pyrimidine was reacted with different aromatic amines to afford new Schiff bases. These new 3- imines derivatives was reduced by using sodiumborohydride to yield another new 3-aminomethyl-2-biphenyl imidazo (1,2-a)pyrimidine derivatives in moderate yield .Some new prepared compounds were identified by melting point, FT- IR , 13C-

In this research a new compounds were synthesized started from compound 1 which was synthesized from two moll of piperidine (secondary cyclic amine) with dichloro acetic acid, compound 1 reacted by condensation reaction with methanol and H 2 SO 4 as a catalyst to give the ester compound 2. Compound 2 was reacted with hydrazine hydrate 80 % to give compound 3 , then the compounds 4-13 were synthesized from refluxing of compound 3 with the selected aldehydes and ketones via using few drops of glacial acetic acid, finely step the compounds 4-13 were reacted with phtalic anhydride to give compounds 14-23.. All these compounds were characterized by using of melting point, FTIR, 1 HNMR and mass spectroscopy. Scheme 1 and Scheme 2 shown the all re

Tetragonal compound CuAl0.4Ti0.6Se2 semiconductor has been prepared by
melting the elementary elements of high purity in evacuated quartz tube under low
pressure 10-2 mbar and temperature 1100 oC about 24 hr. Single crystal has been
growth from this compound using slowly cooled average between (1-2) C/hr , also
thin films have been prepared using thermal evaporation technique and vacuum 10-6
mbar at room temperature .The structural properties have been studied for the powder
of compound of CuAl0.4Ti0.6Se2u using X-ray diffraction (XRD) . The structure of the
compound showed chalcopyrite structure with unite cell of right tetragonal and
dimensions of a=11.1776 Ao ,c=5.5888 Ao .The structure of thin films showed

Abstract Rasha Hameid Jehad Baghdad University Background: The high reactivity of hydrogen peroxide used in bleaching agents have raised important questions on their potential adverse effects on physical properties of restorative materials. The purpose of this in vitro study was to evaluate the effect of in-office bleaching agents on the microhardness of a new Silorane-based restorative material in comparison to methacrylate-based restorative material. Materials and method: Forty specimens of Filtek™ P90 (3M ESPE,USA) and Filtek™ Supreme XT (3M ESPE, USA) of (8mm diameter and 3m height) were prepared. All specimens were polished with Sof-Lex disks (3M ESPE, USA). All samples were rinsed and stored in incubator 37˚C for 24 ho

Photonic Crystal Fiber Interferometers (PCFIs) are widely used for sensing applications. This work presents the fabrication and the characterization of a relative humidity sensor based on a polymer-coated photonic crystal fiber that operates in a Mach- Zehnder Interferometer (MZI) transmission mode. The fabrication of the sensor involved splicing a short (1 cm) length of Photonic Crystal Fiber (PCF) between two single-mode fibers (SMF). It was then coated with a layer of agarose solution. Experimental results showed that a high humidity sensitivity of 29.37 pm/%RH was achieved within a measurement range of 27–95%RH. The sensor also showed good repeatability, small size, measurement accuracy and wide humidity range. The RH sensitivity o

Photonic Crystal Fiber Interferometers (PCFIs) are widely used for sensing applications. This work presents the fabrication and study the characterization of a relative humidity sensor based on a polymer-infiltrated photonic crystal fiber that operates in a Mach- Zehnder Interferometer (MZI) reflection mode. The fabrication of the sensor only involves splicing and cleaving Photonic Crystal Fiber (PCF) with Single Mode Fiber (SMF). A stub of (LMA-10) PCF spliced to SMF (Corning-28). In the splice regions. The PCFI sensor operation based on the adsorption and desorption of water vapour at the silica-air interface within the PCF. The sensor shows a high sensitivity to RH variations from (27% RH - 95% RH), with a change in its reflected powe