The present study focused mainly on the analysis of stiffened and unstiffened composite laminated plates subjected to buckling load. Analytical, numerical and experimental analysis for different cases has been considered. The experimental investigation is to manufacture the laminates and to find mechanical properties of glass-polyester such as longitudinal, transverse young modulus, shear modulus. The compressive test was carried to find the critical buckling load of plate. The design parameters of the laminates such as aspect ratio, thickness ratio, boundary conditions and number of stiffeners were investigated using high order shear deformation theory (HOST) and Finite element coded by ANSYS .The main conclusion was the buckling load c

The adsorption of hexavalent chromium by preparing activated carbon from date seeds with zinc chloride as chemical activator and granular date seeds was studied in a batch system. The characteristics of date seeds and prepared activated carbon (ZAC) were determined and found to have a surface area 500.01 m²/g and 1050.01  m²/g , respectively and  iodine number of 485.78 mg/g and 1012.91  mg/g, respectively. The effects of PH value (2-12), initial sorbate concentration(50-450mg/L), adsorbent weight (0.004-0.036g) and contact time (30-150 min) on the adsorption process were studied . For Cr(VI) adsorption on ZAC, at 120 min time contact, pH solution 2 and 0.02  adsorbent  weight  will ach

KE Sharquie, MM Al-Waiz, AA Al-Nuaimy, Saudi medical journal, 2005 - Cited by 8

     Increasing need for our youth to effective dialogue at the present time, due to the nature of the era in which live, as it abounded risk of intellectual and cultural invasion.Moreover, the need to ensure that the dialogue between the members of the community to confront the many issues of contemporary society in various fields, politically, socially and economically, culturally and religiouslyThe absence of effective dialogue, or the consequent rejection of many of the negative aspects of social and cultural Kaezzlh coup and inertia and ignore the mental capacity of some non-existent among others.The importance of effective dialogue in being the most important foundations of social life a

Composite steel-concrete sections have a broad benefit through increasing structural strength as well as minimizing the self-loads. All past researches were concerned with pre-installed shear connectors (PRSC) in the manufacturing of composite sections. A new fabrication technique for steel-concrete-steel composite sections were presented in the current study by the post-installation shear connectors (POSC) passed-through an embedded polymerizing vinyl chloride (PVC) pipes. The performance of normal strength concrete prisms with a specified strength of 32 MPa connected to square steel tubes (SST) was investigated. Six specimens were fabricated in both methodologies, PRSC and POSC were experimentally tested by Push-out test. The spac

This study “discusses the benefit of “addition waste paper as a “new cellulose material “in mortar mixes. A partial addition of waste paper by cement weight was achieved to produce cement composite mortar.  Pulp and paper is the third major industrial dumper of air, soil and water. In recent year, paper and paperboard constitute a greater portion of many countries’ urban solid discarded generation. Beside, it increases characteristic “strength due to existence “of hydrogen links “in the microstructure of “paper. Furthermore, it consume “better thermal protection. The addition percentages “of waste paper used “in this work were (5%, 10%, 15% and 20%) by “mass of cement to measure and evaluat

Porous Silicon (PSi) has been produced in this work by using Photochemical (PC) etching process by using a hydrofluoric acid (HF) solution. The irradiation has been achieved using quartz- tungsten halogen lamp. The influence of various irradiation times on the properties of PSi اmaterial such as layer thickness, etching rate and porosity was investigated in this work too.
The XRD has been studied to determine the crystal structure and the crystalline size of PSi material

Abstract:Porous Silicon (PSi) has been produced in this work by using Photochemical (PC) etching process by using a hydrofluoric acid (HF) solution. The irradiation has been achieved using quartz- tungsten halogen lamp. The influence of various irradiation times on the properties of PSi اmaterial such as layer thickness, etching rate and porosity was investigated in this work too. The XRD has been studied to determine the crystal structure and the crystalline size of PSi material

For desulfurization of naphtha, NaY zeolite was prepared from Dewekhala kaolin clay (Al-Anbar region). For the prepared zeolite adsorbent, x-ray diffraction, sodium content, silica to alumina ratio, surface area, bulk density and crushing strength were determined. From the x-ray diffraction of the prepared NaY zeolite and by a comparison with the standard NaY zeolite, it was found that the prepared adsorbent in this work has approximately the same crystal structure as the standard. Adsorption process was done in a laboratory unit at 25