PVC/Kaolinite composites were prepared by the melt intercalation method. Mechanical properties, thermal properties, flammability and water absorption percentage of prepared samples were tested. Mechanical characteristic such as tensile strength, elongation at break; hardness and impact strength (charpy type) were measured for all samples. It was found that the tensile strength and elongation at break of PVC composites decreased with increasing kaolinite loading. Also, the hardness of the composites increases with increase in filler content .The impact strength of the composites at the beginning increases at lower kaolinite loadings is due to the lack of kaolin adhesion to the matrix. However, at higher kaolin loadings. This severe agglom

Twelve N-(6-sustirured benzothanol-2-y1) succinamic acids and 3-(6-substitted benzonathol-2-y1)-carbamoyl propionyl chloride were synthesized in good yields from reaction of benzonathol2-yl)

Di Benzylidenes were prepared by condensation of 1,2-diamino benzene with o- hydroxy benzaldehyde. These dibenzylidenes when treated with one equivalent of malonic anhydride or 5-oxo-spiro[2,3]hexane-4,6-dione in dry benzene give 6-membered heterocyclic ring system of 3-{2-[(2-Hydroxy-benzylidene)-amino]-phenyl}-2-(2-hydroxy –phenyl)-[1,3]oxazinane-4,6-diones ( 1-3) or 7-{2-[(2-hydroxy-benzylidene)-amino]-phenyl}-6-(2-hydroxy-phenyl)-5-oxa-7-aza-spiro[2.5]octane-4,8-diones ( 7- 9 ) But when two equivalents of malonic anhydride or 5-oxo-spiro[2,3]hexane-4,6-dione were used and under sam conditions compounds (4-6 , 10-12 ) were obtained .

The - mixing ratios of -transitions from levels in populated in the reactions are calculated in present work using - ratio, constant statisticalTensor and least squares fitting methods The results obtained are in general, in good agreement or consistent, within the associated uncertainties, with these reported in Ref.[9],the discrepancies that occurs are due to inaccuracy existing in the experimental data The results obtained in the present work confirm the –method for mixed transitions better than that for pure transition because this method depends only on the experimental data where the second method depends on the pure or those considered to be pure -transitions, the same results occur in – method

    The behaviour of Np-239 during the Continuous extraction and stripping  was followed . Three Continuous extraction experiments were carried out . In the first experiment the extraction and stripping were carried out by using Tributyl Phosphate / treated odorless kerosene as the organic phase , while the aqueous phase was uranium and neptunium-239 dissolved in 3M HNO3 . In the second experiment irradiation of organic phase up to 30 M rad were carried out , while keeping the aqueous phase as it is in the first experiment. In the third experiment , the acidity of the aqueous phase was 1.5M instead of 3M and keeping the organic phase as it is in experiment 1. The results obtained in tables 1-3 show the possibility of

New metal ion complexes were synthesized with the general formula; K[PtLCl4], [ReLCl4] and K[ML(Cl)2] where M = Pd(II), Cd(II), Zn(II) and Hg(II), from the Azo ligand (HL) [2-Hydroxy-3-((5-mercapto-1,3,4-thiadiazol-2-yl)diazenyl)-1-naphth aldehyde] (HL) the ligand was synthesized from (2-hydroxy-1-naphthaldehyde) and (5-amino-1,3,4-thiadiazole-2-thiol). The ligand and its metal complexes are characterized by phisco- chemical spectroscopic techniques (FT.IR, UV-Vis and Mass spectra, elemental analysis, molar conductivity, Atomic Absorption, Chloride contain and magnetic susceptibility). The spectral data suggest that the (HL) behaves as a bidentate ligand in all complexes. These studies revealed tetrahedral geometries for all metal complexes

Used cooking oil was undergoing trans-esterification reaction to produce biodiesel fuel. Method of production consisted of pretreatment steps, trans-esterification, separation, washing and drying. Trans-esterification of treated oils was studied at different operation conditions, the methanol to oil mole ratio were 6:1, 8:1, 10:1, and 12:1, at different temperature 30, 40, 50, and 60 ^º C, reaction time 40, 60, 80, and 120 minutes, amount of catalyst 0.5, 1, 1.5, and 2 wt.% based on oil and mixing speed 400 rpm. The maximum yield of biodiesel was 91.68 wt.% for treated oils obtained by trans-esterification reaction with 10:1 methanol to oil mole ratio, 60 ^º C reaction temperature, 80 minute reactio

CdO:NiO/Si solar cell film was fabricated via deposition of CdO:NiO in different concentrations 1%, 3%, and 5% for NiO thin films in R.T and 723K, on n-type silicon substrate with approximately 200 nm thickness using pulse laser deposition. CdO:NiO/n-Si solar cell photovoltaic properties were examined under 60 mW/cm2 intensity illumination. The highest efficiency of the solar cell is 2.4% when the NiO concentration is 0.05 at 723K.

To achieve sustainability, use waste materials to make concrete to use alternative components and reduce the production of Portland cement. Lime cement was used instead of Portland cement, and 15% of the cement's weight was replaced with silica fume. Also used were eco-friendly fibers (copper fiber) made from recycled electrical. This work examines the impact of utilizing sustainable copper fiber with different aspect ratios (l/d) on some mechanical properties of high-strength green concrete. A high-strength cement mixture with a compressive strength of 65 MPa in line with ACI 211.4R was required to complete the assignment. Copper fibers of 1% by volume of concrete were employed in mixes with four different aspect ratios