The aim of this study is to calculate the marketing efficiency to measures range of efficiency of the marketing processes of crop and their satisfaction of consumer demand, and calculate the marketing margin in marketing process  for stage producer – whole sale and whole sale- retailer stage, and to fulfillment the requirements the research it is aims . The data was collected from 32 farms of tomato from AL-Taji District_Baghdad province Agricultural season 2015 non covered agriculture. The marketing efficiency of sample low 32. 5, and the  absolute marketing margin in stage of wholesaler-retailer was 230 I.d/kg, and retailers importance it was 39.36%, although that relative importance of the retailer profits from the marketing

Copper oxide thin films were deposited on glass substrate using Successive Ionic Layer Adsorption and Reaction (SILAR) method at room temperature. The thickness of the thin films was around 0.43?m.Copper oxide thin films were annealed in air at (200, 300 and 400°C for 45min.The film structure properties were characterized by x-ray diffraction (XRD). XRD patterns indicated the presence of polycrystalline CuO. The average grain size is calculated from the X-rays pattern, it is found that the grain size increased with increasing annealing temperature. Optical transmitter microscope (OTM) and atomic force microscope (AFM) was also used. Direct band gap values of 2.2 eV for an annealed sample and (2, 1.5, 1.4) eV at 200, 300,400oC respect

In Present study, 25 clinical isolates of Proteus spp. of clinical samples, urine, wounds and burns collected from different hospitals in Baghdad city, all isolates were identified as Proteus mirabilis using different bacteriological media, biochemical assays and Vitek-2 system. It was found that 15 (60%) isolates were identifying as P. mirabilis. The susceptibility of P. mirabilis isolates to cefotaxime was 66.6 %, while to ceftazidime was 20%. Extended spectrum β-lactamses producing Proteus was 30.7 %. DNA of 5 isolates of P. mirabilis was extracted and detection for blaVEB-1 gene by using multiplex polymerase chain reaction (PCR). Results showed that the presence of this gene in all tested isolates, as an important indicator for increas

Background: Presence of maxillary sinus septa has been known to be a complicating factor for sinus elevation procedure and implant placement in posterior maxilla. The maxillary sinuses septa are thin walls of cortical bone inside the sinus. They vary in number, location, and height. This study aimed to discover the accuracy of Spiral Computed Tomographic Scan in evaluation the maxillary sinus septa (prevalence, location, height) in subjects with dentate, partially edentulous and completely edentulous maxilla. Material and method: This study included (267) subjects ranged from (20-70 years), (132) male and (135) female divided into three groups, (97) fully dentate group, (102) partially edentulous group and (68) completely edentulous group w

Tourism is one of the most important sources of income of economic key countries in the world so are imports of tourism for some countries a source of income is not significant of the total revenues of States. Making those countries, and those countries a destination for visitors, and here should be interest in the Wealth and cultural heritage that distinguishes Islamic countries in general, and Iraq in particular, must be placed specialist studies in all areas for the development of this area of tourism, especially religious tourism to achieve a desired and desired of such research.It is the most important ways to develop tourism in general and religious tourism is of particular publications, advertising, and is important for us in this

Objective(s): The world of dentistry is constantly evolving, and with the advent of 3D printing technology, the possibilities are endless. However, little is known about the effects of adding ZrO2 NPs to the denture base resin of 3D additive manufacturing technique.Aim of this study is to evaluate the behavior of resin which is used to 3D printing of denture base with the addition of ZrO2 NPs on denture adaptation property and diametral compression strength.Methods: 60 samples were printed, 30 disks for diametral compressive test and 30 denture base for denture adaptation test. Three groups per test (n=10). The control group for each test included unreinforced 3Dprinted denture base resin, and the other groups were  reinforced with (2&

In this study water quality was indicated in terms of Water Quality Index that was determined through summarizing multiple parameters of water test results. This index offers a useful representation of the overall quality of water for public or any intended use as well as indicating pollution, water quality management and decision making. The application of Water Quality Index (WQI) with sixteen physicochemical water quality parameters was performed to evaluate the quality of Tigris River water for drinking usage. This was done by subjecting the water samples collected from eight stations in Baghdad city during the period 2004-2010 to comprehensive physicochemical analysis. The sixteen physicochemical parameters included: Turbidity,

Objective: The aim of this study was to evaluate the effect of pumice, burning investment material
and black sand on the surface roughness of heat cure acrylic resin.
Methodology: Sixty specimens were prepared from pink heat cure acrylic resin, the specimens
where grouped into; 20 specimens which polished with pumice and water (control group); 20
specimens which polished with investment material (after burning it) and water; and 20 specimens
which polished with black sand and water. The average surface roughness of specimens after
polishing procedure had been determined by profilometer (surface roughness tester).
Results: Through the application of ANOVA and LSD tests, the result of this study showed that there
wa

PVC/Kaolinite composites were prepared by the melt intercalation method. Mechanical properties, thermal properties, flammability and water absorption percentage of prepared samples were tested. Mechanical characteristic such as tensile strength, elongation at break; hardness and impact strength (charpy type) were measured for all samples. It was found that the tensile strength and elongation at break of PVC composites decreased with increasing kaolinite loading. Also, the hardness of the composites increases with increase in filler content .The impact strength of the composites at the beginning increases at lower kaolinite loadings is due to the lack of kaolin adhesion to the matrix. However, at higher kaolin loadings. This severe agglom