A numerical computation for determination transmission coefficient and resonant tunneling energies of multibarriers heterostructure has been investigated. Also, we have considered GaN/Al_0.3Ga_0.7N superlattice system to estimate the probability of resonance at specific energy values, which are less than the potential barrier height. The transmission coefficient is determined by using the transfer matrix method and accordingly the resonant energies are obtained from the T(E) relation. The effects of both well width and number of barriers (N) are observed and discussed. The numbers of resonant tunneling peaks are generally increasing and they become sharper with the increasing of N. The resonant tunneling levels are sh

This paper studied the behaviour of reinforced reactive powder concrete (RPC) two-way slabs under static load. The experimental program included testing three simply supported slabs of 1000 mm length, 1000 mm width, and 70 mm thickness. Tested specimens were of identical properties except their steel fibers volume ratio (0.5 %, 1 %, and 1.5 %). Static test results revealed that, increasing steel fibers volume ratio from 0.5% to 1% and from 1% to 1.5%, led to an increase in: first crack load by (32.2 % and 52.3 %), ultimate load by (36.1 % and 17.0 %), ultimate deflection by (33.6 % and 3.4 %), absorbed energy by (128 % and 20.2 %), and the ultimate strain by (1.1 % and 6.73 %). The stiffness and ductility of the specimens also increased. A

In this paper, Nordhaus-Gaddum type relations on open support independence number of some derived graphs of path related graphs under addition and multiplication are studied.

Background: the aim of this study was to evaluate the effect of different surface acids treatments (37%phospjoric acid, 5%hydrofluoric acid, 1.23 acidulated phosphate fluoride) of feldspathic ceramic VITA 3D MASTER , and the effect of thermocycling on shear bond strength using a ceramic repair kit (ivoclar/vivadent). Material and Methods: sixty Nickel-Chromium metal base plates were prepared(9mm diameter,3mm depth) using lost wax technique, 2mm thick layer of ceramic(VITA 3D MASTER) fused to metal plates, all specimens were embedded in acrylic resin blocks except their examined surfaces and divided into 3 main groups 20 specimens each, Grp A: treatment with 37%phosphoric acid for 2 mins, Grp B: etching with 5% hydrofluoric acid for 2mins,

Nearly, in the middle of 1970s the split-brain theory became the only theory that explains human creativity used in all fine art and art education schools. In fact, this theory- which appeared for first time in the middle of 1940s – faced many radical changes including its concepts and structures, and these changes affected both teaching art and art criticism. To update people awareness within art field of study, this paper reviews the split-brain theory and its relationship with teaching art from its appearance to its decay in 2013 and after.

                In this investigation a high density polyethylene (HDPE) was used as a substitute to polyvinylchloride in the production of lead acid battery separators. This has been achieved by preparing mixtures of different percentages of the feed materials which include a high density polyethylene (HDPE) locally produced, filler materials such as silica and oils such as dioctylphthalate (DOP) or paraffin which were added to the mixture to improve the final properties of the separator. The materials were compounded by two roll-mills under the same conditions. The following parameters are involved:           &nb

A high Tc superconductor with a nominal composition
(Bi1-xPbx)2(Sr1-yBay)2Ca2Cu3O10+δ for (0 £ x £ 0.5) and (0 £ y £ 0.5) was prepared by
a solid state reaction method. The effect of the substitution of Pb for Bi and Ba for Sr and
quenching temperature on the superconductivity has been investigated to obtain the
optimum conditions for the formation and stabilization of the high Tc phase (2223).
The results showed that the optimum sintering temperature for the pure composition is
equal to 875°C and the sintering time is equal to 240h with heating and cooling rate of
60°C/h . Our results indicated that a small amount of (Ba = 0.1) could raise the transition
temperature (Tc), but enhancing Ba to 0.4 has raised

حضر الليكاند (L) 1-فنيل-3-بردين-2-يل مثيل-ثايويوريا من تفاعل 2-أمينو مثيل بردين مع فنيل ايزوثايوسيانيت وبنسبة 1: 1 وشخص الليكاند بواسطة التحليل الدقيق للعناصر (C, H, N), الأشعة تحت الحمراء، الأشعة فوق البنفسجية–المرئية وطيف الرنين النووي المغناطيسي كما حضرت وشخصت معقدات أملاح بعض ايونات العناصر الثنائية التكافؤ (Co, Ni, Cu, Cd and Hg). استخدمت تقنية الأشعة تحت الحمراء، الأشعه فوق البنفسجية-المرئية, التوصيلية الكهربائية و الا

The azo Schiff base [Reaction of 4-aminoanypyrine and P-hydroxy acetophenone] and O-Phenylene diamine have been prepared. One azo Schiff base chelate of Co(Il), Ni(II), Cu(II) and Zn(II)ion was also prepared. The chemical frameworks of the azo Schiff base and like elemental analyses (CHN), determinations of molar conductance, 1 H &13C NMR, IR mass and electronic spectroscopy .The elemental analyses exhibited the combination of [L: M] 1:1 ratio. Established on the values IR spectral, it is showed that the azo Schiff base compound acts as neutral hexadentate ligand bonded with the metal ion from two hydroxyl, two azomethine and two azo groups of the azo Schiff base compound in chelation was confirmed by IR , 1Hand 13CNMR spectral outco

The purpose of my thesis is to prepare four new ligands (L1-L4) that have been ‎used to prepare a series of metal complexes by reacting them with metal ions:‎ ‎ M=(Mn(II), Co(II), Ni(II), Cu(II), Zn(II), Cd(II), Hg(II) ‎ ‎ Where succinyl chloride was used as a raw material for the preparation of ‎bi-dented ligands (L1-L4) by reacting it with potassium thiocyanate as a first ‎step and then reacting with (2-aminobenzothiazole, Benzylamine, 4-‎aminoantipyrine, Sulfamethoxazole) respectively as a second step with the use ‎of dry acetone as a solvent, the chemical formula of the four ligands prepared in ‎succession:‎ N1,N4-bis(benzo[d]thiazol-2-ylcarbamothioyl)succinamide (L1)‎ N1,N4-bis(benzylcarbamothioyl)succinami