Magnesium hydroxide was used as flame inhibitor to increased flame resistance for tires .Magnesium hydroxide was adding with (5%,10%) weight percents to rubber master batch of tire and then exposed the resulting material to a flame generated from gas torch with (10 mm) exposure distance . Method of measuring the surface temperature opposite to the flame was used to determine the heat transferred through tire material. The results were obtained shows enhanced flame resistance for tire by added magnesium hydroxide and this resistance increased by increasing hydroxide Percentage .

Background: Prosthodontic services have changed markedly due to an introduction of new materials, techniques and treatment options. The aim of this study were to identify the type of materials and the methods used by dental practitioners in their clinics to construct conventional complete dentures and to specify the type and design for removable partial dentures (RPDs); and to then compare them with those taught in dental schools. Materials and methods: A total of 153 dental practitioners in Sulaimani city completed a written questionnaire. The questionnaire included 19 questions regarding complete and RPDs fabrication. Results: Most of the practitioners provide complete dentures (81.6%) and RPDs (95.3%) in their clinics. Polyvinyl silox

The past several years have seen an increase in awareness of the pervasiveness of medications as pollutants in the aquatic environment. The main reason for concern regarding the release of pharmaceuticals into the environment is the possibility that biological agents may become opposing to them. The development of precise and reliable analytical techniques for pharmaceutical determination in a range of samples is necessary for their safe use in the pharmaceutical industry and medical treatments. This review offers a summary of chromatographic techniques for identifying and quantifying the examination of pharmaceuticals in a range of environmental samples. Both the general public and the scientific community are currently very intere

The present study aims at knowing the effect of discussion method for students of fifth grade in preparatory school.

Methodology of the Study:

          In order to achieve the objective of the study, the researcher chooses non-randomly the preparatory school affiliated to the District Chamchamal \ Suliemnaniya. The sample attained 64 students in 32 per group (control and experimental) groups. The researcher used the discussion method which was applied on experimental group. She uses the traditional method on the control group.

The researcher matched the two group in ago, intelligence, marks at the Kurdish Language in the previous year , pretest and posts for the indepe

In this research PbS thin film have been prepared by chemical bath deposition technique (CBD).The PbS film with thickness of (1-1.5)μm was thermally treated at temperature of 100°C for 4 hours. Some Structural characteristics was studied by using X-ray diffraction (XRD)and optical microscope photograph some of chemical gas sensing measurements were carried out ,it shown that the sensitivity of (CO2) gas depend on the grain Size and deposition substrate. The grain size of PbS film deposited on on glass closed to 21.4 nm while 37.97nm for Si substrate. The result of current-voltage characterization shwon the sensitivity of prepared film deposited on Si better than film on glass.

Copper Telluride Thin films of thickness 700nm and 900nm, prepared thin films using thermal evaporation on cleaned Si substrates kept at 300K under the vacuum about (4x10-5 ) mbar. The XRD analysis and (AFM) measurements use to study structure properties. The sensitivity (S) of the fabricated sensors to NO2 and H2 was measured at room temperature. The experimental relationship between S and thickness of the sensitive film was investigated, and higher S values were recorded for thicker sensors. Results showed that the best sensitivity was attributed to the Cu2Te film of 900 nm thickness at the H2 gas.

In this work the structural, optical and sensitive properties of Cerium - Copper oxide thin film prepared on silicon and glass substrate by the spray pyrolysis technique at a temperature of (200, 250, 300 °C). The results of (XRD) showed that all the prepared films were of a polycrystalline installation and monoclinic crystal structure with a preferable directions was (111) of CuO. Optical characteristics observed that the absorption coefficient has values for all the prepared CuO: Ce% (104 cm-1) in the visible spectrum, indicating that all the thin films prepared have a direct energy gap. Been fabrication of gas sensors of (CuO: Ce %) within optimum preparation conditions and study sensitivity properties were examined her exposed to ni