In this paper we have studied the optical properties of CuBr thin

films.  Different  sample  thicknesses  have  been  prepared  by  using thermal evaporation  technique with 14.4 runlsec as the average deposition rate and 1 00°C as the substrate temperature.

Fifty isolates of Bacillus sp. were subjected to the first and second screening to detect the ability to produce laccase enzyme and select the highest ones production of laccase on Petri plates containing nutrient agar supplemented with Cu2+.
Syringaldazine was used as an indicator and substrate for the determination of laccase activity. Three isolates, which consumed less time to developed pink color were tested for the production of laccase quantitatively. The effective isolate B16 with significant amounts of laccase 1.84 unit /ml was selected for laccase study.
The optimization studies revealed that the maximum laccase production was achieved when the production medium was at the following conditions: 5 days of incubation, tempe

This study presents determination of the paleostress magnitudes and orientation of Bekhme Structure in Shaqlawa area northeastern Iraq. Paleostress Analysis of slip-fault measurements is performed using Right dihedral, Lisle diagram and Mohr Circles methods. Depending on Mohr Circles, Bott law and vertical thickness, the magnitudes of the paleostress at the time of the tectonic activity were determined. Firstly, Georient Software was used to estimate the orientation of the paleostresses (σ1, σ2 and σ3). Secondly, using the rupture –friction law, taking into account depth of the overburden and the vertical stress (σv) was calculated to determine the magnitude of the paleostresses (σ1=4500 bars, σ2=1

This study presents the determination of the paleostress magnitudes and orientation of Bekhme Structure in Shaqlawa area, northeastern Iraq. Paleostress analysis of slip-fault measurements is performed using Right dihedral, Lisle diagram, and Mohr Circles methods. Depending on Mohr Circles, Bott law, and vertical thickness, the magnitudes of the paleostress at the time of the tectonic activity were determined. Firstly, Georient Software was used to estimate the orientation of the paleostresses (σ1, σ2, and σ3). Secondly, using the rupture –friction law, taking into account the depth of the overburden and the vertical stress (σv),the magnitudes of the paleostresses were calculated (σ1=4500 bars, σ2=1900 bars and σ3=700 bars). &nb

A polycrystalline CdSe thin films doped with (5wt%) of Cu was fabricated using vacuum evaporation technique in the substrate temperature range(Ts=RT-250)oC on glass substrates of the thickness(0.8?m). The structure of these films are determined by X-ray diffraction (XRD). The X-ray diffraction studies shows that the structure is polycrystalline with hexagonal structure, and there are strong peaks at the direction (200) at (Ts=RT-150) oC, while at higher substrate temperature(Ts=150-250) oC the structure is single crystal. The optical properties as a function of Ts were studied. The absorption, transmission, and reflection has been studied, The optical energy gap (Eg)increases with increase of substrate temperature from (1.65

The eff ect of partial substitution for lanthanum (La) on the structural properties of the compound Y1-xLaxBa4Cu7O15+δ were studied. The variation of (x) are x=0.1, 0.2 and 0.3, which was synthesized by solid state reaction method. The mixed powder was pressed with pressure (7 ton / cm2) as a disc (1.5 cm) diameter and a thickness of (0.25 to 0.3 cm). The samples were sintering by 120 °C / hour with a changing rate from room temperature to 850 ° C through 72 hours. XRD analysis using to calculate crystal size, strain and degree of crystallinity. It was found all samples have orthorhombic structure and change of structure with increasing lanthanum concentration. It was shown that the change lanthanum concentrations of all our samp

The aim of this research is to develop mechanical properties of a new aluminium-lithium-copper alloy. This alloy prepared under control atmosphere by casting in a permanent metal mould. The microstructure was examined and mechanical properties were tested before and after heat treatment to study the influence of heat treatment on its mechanical properties including; modulus of elasticity, tensile strength, impact, and fatigue. The results showed that the modulus of elasticity of the prepared alloy is higher than standard alloy about 2%. While the alloy that heat treated for 6 h and cooled in water, then showed a higher ultimate tensile stress comparing with as-cast alloy. The homogenous heat treatment gives best fatigue

Several schottky diodes were fabricated from polyaniline/ Carbon nanotube (single and multiwalled) composites. These composites were synthesized with different concentration and two carbon nanotubes types, Single and Multi-Walled Carbon Nanotubes (SWCNT & MWCNT). Aluminum and silver paste were chosen as schottky and ohmic contact respectively. physical and electrical were used to studied these composite by using Atomic Force Microscopy (AFM) and electrical measurements. The Root Mean Square RMS surface roughness of the composite samples was found to be around 4nm. The currentvoltage characteristic were measurements for all samples in the bias range ±15V at room temperature. The results shows the increasing in carbon nanotubes concentration