The high temperature superconductor’s compounds are one of the hot spot field of science, due to their applications in industries. Hg0.8Sb0.2Ba2Ca2Cu3O8+δ and Hg0.8Sb0.2Ba2Ca1Cu2O6+δ, were manufactured using a doable-step of solid state reaction method. The samples were sintered at 800 ° C. The transition temperatures Tc are found from electrically resistively by using four probe techniques. The resistivity become zero when the transition temperature Tc(offset) have 131 and 119 K, and the onset temperature Tc(onset) have 139 K for Hg0.8Sb0.2Ba2Ca2Cu3O8+δ and 132 K for Hg0.8Sb0.2Ba2Ca1Cu2O6+δ. Analysis of X-ray diffraction showed a tetragonal structure with lattice parameters changes for all samples.
The main goal of our research is to synthesize novel nano Zn2+ complex with the 8-(2-(dansyl chloride)azo) adenine (LA) ligand as a pH sensor because of its advantageous properties, obtained from a single molecule. The Zn2⁺- LA complex was based on the production of an intensely dark purple-colored substance with λmax at 552 nm. Molar ratio of Zn2⁺- LA complex is a 1:2 in aqueous buffer. The optimum concentration (0.3) mM, pH (2-5.5), and time (0-3) hr at pH=5.5, that in the studies followed Lambert-law Beer'
The studies on the antiviral compound chalcone in vitro in both tissue and organ culture systems against rubella virus glass that this compound relatively non toxic to the cell culture and organ culture of the concentration of 8 ug/ml or less, chalcone have significantly antiviral activity against rubella virus in tissue culture and organ culture. We find that a concentration of 0.03ug/ml or more inhibit the IOOTCID50 of rubella virus. The therapeutic index (TI) used in this study to evaluate the drug, the (TI) which is the ratio of the dose of drug which is just toxic (Maximum tolerated dose) to the dose which is just effective (Minimum effective dose). If this index is one or less it not possible to use the drug under the conditions outli
... Show Moreon this research is to study the effect of nickel oxide substitution on the pure phases superconductor Tl0.5Pb0.5Ba2Can-1Cun-xNixO2n+3-δ (n=3) where x=(0,0.2,0.4,0.6,0.8.and 1.0). The specimens in this work were prepared with used procedure of solid state reaction with sintering temperature 8500C for 24 h .we used technical (4-prob)to calculated and the critical temperature Tc . The results of the XRD diffraction analysis showed that the structure for pure and doped phases was tetragonal with phases high-Tc phase (1223),(1212) and low-Tc phase (1202) and add
... Show MoreNew complexes of cobalt (II). palladium (II). and platiniurn(H) with 5-phenyl- 1.3,4-oxadiazole-2- thioethylcarbanate (OXE) have been prepared and characterized by elemental analysis, 1R.L-V-Vis spectra. magnetic susceptipibility. and conductivity- measurements. Probable structures of the prepared complexes have been reported.
Copper Zinc Sulphide (Cu0.5Zn0.5S) alloy and thin films were fabricated in a vacuum. Nano crystallized (CZS) film with thick 450±20 nm was deposit at substrates glasses using thermal evaporation technique below ~ 2 × 10− 5 mbar vacuum to investigated the films structural, morphological and optical properties depended on annealing temperatures ( as-deposited, 423, 523 and 623) K for one hour. The influences annealed temperature on structurally besides morphologically characteristics on these films were investigated using XRD and AFM respectively. XRD confirms the formation a mixed hexagonal phase of CuS-ZnS in (102) direction with polycrystalline in nature having very fine crystallites size varying from (5.5-13.09) nm. AFM analys
... Show MoreThe present study included the impact of the follow-up variation in the temperature of aqueous medium in the vertical migration behavior of different groups of Zooplankton, consisted species Cyclops vernalis, Daphnia magna, Diaptomus dilopatus, that have been grown in controlled in terms of light and pH laboratory conditions, so choosing temperature of respectively 16,20,24,28, and 32 ËšC. The result showed a clear change in the migration behavior of testing planktonic species, it was a negative relationship between temperatures arises and individual of D. magna in the water column.While being appositive relationship with individual of C. vernalis and the same with D. dilopatus. Also, the result revealed a different impact
... Show MoreTin Oxide (SnO2) films have been deposited by spray pyrolysis technique at different substrate temperatures. The effects of substrate temperature on the structural, optical and electrical properties of SnO2 films have been investigated. The XRD result shows a polycrystalline structure for SnO2 films at substrate temperature of 673K. The thickness of the deposited film was of the order of 200 nm measured by Toulansky method. The energy gap increases from 2.58eV to 3.59 eV when substrate temperature increases from 473K to 673K .Electrical conductivity is 4.8*10-7(.cm)-1 for sample deposited at 473K while it increases to 8.7*10-3 when the film is deposited at 673K
The reliability of optical sources is strongly dependent on the degradation and device characteristics are critically dependent on temperature. The degradation behaviours and reliability test results for the laser diode device (Sony-DL3148-025) will be presented .These devices are usually highly reliable. The degradation behaviour was exhibited in several aging tests, and device lifetimes were then estimated. The temperature dependence of 0.63?m lasers was studied. An aging test with constant light power operation of 5mW was carried out at 10, 25, 50 and 70°C for 100hours. Lifetimes of the optical sources have greatly improved, and these optical sources can be applied to various types of transmission systems. Within this degradation range,
... Show MoreIn this work the effect of annealing temperature on the structure and the electrical properties of Bi thin films was studied, the Bi films were deposited on glass substrates at room temperature by thermal evaporation technique with thickness (0.4 µm) and rate of deposition equal to 6.66Å/sec, all samples are annealed in a vacuum for one hour. The X-ray diffraction analysis shows that the prepared samples are polycrystalline and it exhibits hexagonal structure. The electrical properties of these films were studied with different annealing temperatures, the d.c conductivity for films decreases from 16.42 ? 10-2 at 343K to 10.11?10-2 (?.cm)-1 at 363K. The electrical activation energies Ea1 and Ea2 increase from 0.031 to 0.049eV and
... Show More