Friction stir welding (FSW) of Tee-joints is obtained by inserting a specially designed rotating pin into the clamped blanks, through top plate (skin) to bottom plate (stringer), and then moving it along the joint, limiting the contact between the tool shoulder and the skin. The present work aims to investigate the defects occur for Tee-joint of an Aluminum alloy (Al 5456) with dimensions (180mm x 70mm) for the skin plate, (180mm x 30mm) for stringer plate and thickness of (4mm).
The effects of welding parameters such as rotational speed, linear speed, plunging depth, tool tilting, and die radii of welding fixture on the welding quality of Aluminum Alloy will be studied. Weld defects had been summarized and studied, and then the best

Abstract

    Corrosion-fatigue occurs by the combined actions of cyclic loading and corrosive environment. The effect of shot peening on cumulative corrosion-fatigue life of 1100-H12 Al alloy was investigated. Before fatigue testing, specimens were submerged in 3.5%NaCl solution for 71 days. Constant fatigue tests were performed with and without corrosive environment. Cumulative corrosion-fatigue tests were also carried out in order to determine the fatigue life before and after shot peening. The constant fatigue life was significantly reduced due to corrosive environment and the endurance fatigue limit was reduced by 13% compared with dry fatigue. In case of shot peening the cumul

During of Experimental result of this work , we found that the change of electrical conductivity proprieties of tin dioxide with the change of gas concentration at temperatures 260oC and 360oC after treatment by photons rays have similar character after treatment isothermally. We found that intensive short duration impulse annealing during the fractions of a second leads to crystallization of the films and to the high values of its gas sensitivity.

Abstract

       The current study was carried out to reveal the plasma parameters such as ,the electron temperature ( ), electron density (n_e) , plasma frequency (fp), Debye length ( ) , Debye number (   for  CdS to employ the LIBS for the purpose of analyzing and determining spectral emission lines using . The results of electron temperature for CdS range (0.746-0.856) eV , the electron density(3.909-4.691)×10¹⁸ cm^-3. Finally ,we discuss plasma parameters of CdS  through  nano second  laser generated plasma .

Wheat is rich in sources of fiber, oligosaccharides, and resistant starch, simple carbohydrates which may have a protective role against carcinoma. Additionally, Whole wheat/bran as well includes contains phytochemicals such as flavonoids, lignans, folate, phytosterols, phenolic acids, and tocols. The above phytochemicals suitable forms antioxidant and cholesterol-reducing activities. Phytoestrogens are regarded as especially essential in the preventative measures of hormonally dependent malignancies such as breast cancer (BC). In this study lowered BC risk has been associated with whole grain/bran consumption with an odds ratio (OR=0.24 and 95 %CI=0.10-0.56). Wheat/bran appears to have a reliable protective impact against BC. While intake

Incremental Sheet Metal Forming (ISMF) is a modern sheet metal forming technology which offers the possibility of manufacturing 3D complex parts of thin sheet metals using the CNC milling machine. The surface quality is a very important aspect in any manufacturing process. Therefore, this study focuses on the resultant residual stresses by forming parameters, namely; (tool shape, step over, feed rate, and slope angle) using Taguchi method for the products formed by single point incremental forming process (SPIF). For evaluating the surface quality, practical experiments to produce pyramid like shape have been implemented on aluminum sheets (AA1050) for thickness (0.9) mm. Three types of tool shape used in this work, the spherical tool ga

          This study was done to evaluate a new technique to determine the presence of methamphetamine in the hair using nano bentonite-based adsorbent as the filler of extraction column. The state of the art of this study was based on the presence of silica in the nano bentonite that was assumed can interact with methamphetamine. The hair used was treated using methanol to extract the presence of methamphetamine, then it was continued by sonicating the hair sample. Qualitative analysis using Marquish reagent was performed to confirm the presence of methamphetamine in the isolate.The hair sample that has been taken in a different period confirmed that this current developing method can be used to analyzed methamphetamine. This m

Hysterectomy is one of the most common gynecological operations done worldwide. Early diagnosis of the psychosexual effects of a hysterectomy and the fast application of appropriate treatment can prevent further worsening and persistence of symptoms, especially with respect to higher levels of anxiety, depression, lower self-esteem, and sexual impact after a hysterectomy. The aim of this study was to assess the psychological and sexual problems of women with hysterectomy. A descriptive study was carried out from March 1, 2023 to May 25, 2023 to determine the level of psychosexual problems experienced by women after hysterectomy. A purposive (non-probability) sample of 120 women who visited the outpatient clinic at Baghdad Teaching H