Samples prepared by using carbon black as a filler material and phenolic resin as a binder. The samples were pressed in a (3) cm diameter cylindrical die to (250)MPa and treated thermally within temperature range of (600-1000)oC for two and three hours. Physical properties tests were performed, like density, porosity, and X-ray tests. Moreover vicker microhardness and electric resistivity tests were done. From the results, it can be concluded that density was increased while porosity was decreased gradually with increasing temperature and treating time. In microhardness test, it found that more temperature and treating time cause more hardness. Finally the resistivity was decreased in steps with temperature and treating time. It can be c

In this paper a thin films of selenium was prepare on substrates of n-Si by evaporation in a vacuum technique with thickness about 0.5μm. And then an annealing process was done on samples at two temperature (100 and 200) C ° in a vacuum furnace (10^-3 torr).
Some structural, optical and mechanical properties of prepared thin films were measured. Results showed that the prepared film was the crystallization, optical transmittance and micro hardness of the prepared thin films increased significantly after annealing.

Dental clinicians and professionals need an affordable, nontoxic, and effective disinfectant against infectious microorganisms when dealing with the contaminated dental impressions. This study evaluated the efficiency of hypochlorous acid (HOCl) as an antimicrobial disinfectant by spraying technique for the alginate impression materials, compared with sodium hypochlorite, and its effect on dimensional stability and reproduction of details. HOCl with a concentration of 200 ppm for 5 and 10 min was compared with the control group (no treatment) as a negative control and with sodium hypochlorite (% 0.5) as a positive control. Candida albicans, Staphylococcus aureus, and Pseudomonas aeruginosa were selected to assess the antimicrobi

The present study aimed to evaluate the concentration of Malon dialdehyde (MDA) in pregnant women during different stages of pregnancy (stage of pregnancy, abortion, contraceptives and parity number).The study included (120) blood samples from normal pregnant women in age of the procreating were subdivided into three trimesters of pregnancy (40/group), and (40) samples from non-pregnant women as a control group. The results showed a significant increase in MDA in three stages of pregnancy compared with the control group. The concentration of MDA increased significantly in pregnant women with multipregnancy when compared with pregnant women for the first time, and in pregnant women whom was using contraceptions compared with p

Background: Fracture of different types of acrylic denture base is a common problem associated with dental prosthesis. Studies suggested that the repair strength may be improved by several means including surface treatment with chemical agents. The aim of the study was to evaluate the effect of surface treatment with acrybond-bonding agent and monomer on fractured denture base in respect to transverse, tensile and shear bond strength and evaluation of the mode of failure by light microscope. Materials and methods: Two hundred seventy specimens were prepared and divided into 3 groups according to the material used (regular conventional, rapid simplified and high impact) heat cure acrylic. The specimen in each groups were prepared specificall

Abstract : Silicone elastomer is widely used as the material of choice for fabricating maxillofacial prosthesis. However, silicone properties are far from ideal; low tear strength, low tensile strength and insufficient elasticity are the most undesirable properties. The purpose of this study was to evaluate the effect of addition of nano SiO2filler on tear strength, tensile strength, elongation at break, hardness and color of Cosmesil M-511 HTV maxillofacial silicone elastomer. Nano SiO2was added to the silicone base in concentrations of 4%, 5% and 6% by weight. Silicone with 0% nano filler served as a control. Tear test was done according to ISO 34-1. Tensile and elongation test was done according to ISO 37. Shore A hardness test was done

The study was conducted in the poultry field, College of Agriculture, Al-Muthanna University from 1/3/2018 to 6/4/2018 to determine the effect of commercial Ascomax powder produced from seaweed (Ascophyllum nodocum) on some productive performance of broilers. A total of 400, one day, Ross 308 broiler chicks were used for 35 days. The chicks were randomly distributed to 4 treatments, four replicates per treatment (25 chick / replicate). The treatments were as follows: T1: (control treatment), while T2, T3 and T4 added diet by Ascomax powder by 1, 1.5 and 2 g per 1 kg of the basal diet, respectively. The results of the study showed a significant superiority (P <0.05) for the added Ascomax powder treatments compared to the treatment of control

Background: elastomeric impression materials are indicated when a high degree of accuracy is required, due to their excellent properties like details reproduction, dimensional stability and tear strength but with main two disadvantages those are their hydrophilicity as well as the absence of antibacterial activity. This study aimed to evaluate the effect of incorporation of 0.5% wt Ag-Zn zeolite into condensation silicone through the following tests; setting time, dimensional stability, reproduction of details, wettability, and hardness . Materials and methods: one hundred specimens were constructed of condensation silicone, divided into two groups for the first 50 specimens one0.5% by wt Ag -Zn zeolite was added, keeping the other fifty sp

To investigate the effect of spraying some plant extraction and anti-oxidants on growth and yield of two cultivars of sunflower, a field experiment was conducted during fall season of 2009 and spring season of 2010 at the Experimental Farm, Department of Field Crop Science, College of Agriculture/ University of Baghdad. RCBD with three replications as factorial at two factors was used. First factor was cultivars Akmar and Shmoss, second was spraying with extraction of karkade at 25%, liquorices at 50%, vitamin C at concentration 1.5 mg.l-1 and nutrient which content 15 elements at concentration 15 % in addition to control treatment which sprayed with distilled water only. The result showed no significant differences between the two cultivar

The present study aimed to explain the dose-dependent possible deleterious effects of 30 day administration of Tramadol on some hematological and biochemical parameters of laboratory male rats (Rattus norvegicus), the study consisted of eighteen adult male rats randomly divided into three equal groups (each of six). Group 1 (control) were treated by intraperitoneal injection of normal saline solution (0.2 ml), group two (low dose) was treated by intraperitonealy (i.p) injection of Tramadol at a dose of 50 mg/kg/day, group three (high dose) was treated by intraperitonealy injection of Tramadol at a dose of 100 mg/kg/day for 30 days. At the end of experimental period, rats were sacrificed. Blood were collected by cardiac puncture to inv