Manganese dioxide rotating cylinder electrode prepared by anodic deposition on a graphite substrate using MnSO4 solution in the presence of 0.918 M of H2SO4. The influence of different operational parameters (MnSO4 concentration, current density, time, and rotation speed) on the structure, and morphology of MnO2 deposit film was examined widely. The structure and crystal size determined by X-ray diffraction (XRD), the morphology examined by scanning electron microscopy (SEM) and atomic force microscopy (AFM) techniques. The γ-MnO2 obtained as the main product of the deposition process. It found that the four parameters have a significant influence on the structure, morphology, and roughness of the prepared MnO2 deposit. The crystal size increases with MnSO4 concentration, current density, and rotation speed, and decreasing with time, while the roughness decreases with increasing all of four parameters. It found that the optimum conditions used in preparing MnO2 rotating electrode that gave the smallest crystal size, low roughness and less cracking were 0.33 M of MnSO4, 6 mA/cm2, 2 h, and 200 rpm. Electrochemical oxidation of phenol in a batch reactor was carried out in the presence of NaCl to examine the performance of the prepared MnO2 electrode for degrading phenol and any organic byproducts at different current densities. The results indicate that as the current density increased from 25 to 100 mA/cm2, the chemical oxygen demand (COD) removal efficiency was increased from 59.26 to 99.90%. Kinetics and the effect of temperature on the COD disappearance have been studied. It was clear that COD decreases with time and as the temperature increases, and the value of reaction order equals to 1 as has been found.
In this work Polyynes was synthesized by pulse laser ablation of graphite target in ethanol solution. UV-Visible Spectrophotometer, Fourier Transform Infrared Spectroscopy (FTIR) and Transmission electron microscopy (TEM) were used to study the optical absorption, chemical bonding, particle size and the morphology. UV absorption peaks coincide with the electronic transitions corresponding to linear hydrogen – capped polyyne (Cn+1H2), the absorption peaks intensity increased when the polyynes were produced at different laser energies and the formation rats of polyynes increased with the increasing of laser pulse number. The FTIR absorption peak at 2368.4 cm-1, 1640.0 cm-1 and 1276.
... Show MoreMass transfer has been studied at rotating cylinder electrodes fabricated with spiral-wound woven-wire meshes using reduction of copper as a test reaction. The experimental data were correlated by an empirical expression between the Sherwood number and the Reynolds number, both regarding the hydraulic diameter as a characteristic length. It was found that the Sherwood number was dependent upon the Reynolds number to the power of 0.521. An enhancement factor was adopted to compare the efficiency of the new rotating cylinder electrode with previous three-dimensional rotating cylinder electrodes. The results showed that the new type has a mass-transfer enhancement factor 2.3 times higher than those obtained with smooth rotating cylinder electr
... Show MoreThin films of Nb2O5 have been successfully deposited using the DC reactive magnetron sputtering technique to manufacture NH3 gas sensors. These films have been annealed at a high temperature of 800°C for one hour. The assessment of the Nb2O5 thin films structural, morphological, and electrical characteristics was carried out using several methods such as X-ray diffraction (XRD), atomic force microscopy (AFM), energy-dispersive X-ray spectroscopy (EDS), Hall effect measurements, and sensitivity assessments. The XRD analysis confirms the polycrystalline composition of the Nb2O5 thin films with a hexagonal crystal structure. Furthermore, the sensitivity, response time, and recovery time of the gas sensor were evaluated for the Nb2O5 thin film
... Show MoreThe nanostructured MnO2 /carbon fiber (CF) composite electrode was prepared using the anodic electrodeposition process. The crystal structure and morphology of MnO2 particles were determined with X-ray diffraction and field-emission scanning electron microscopy. The electrosorptive properties of the prepared electrode were investigated in the removal of cadmium ions from aqueous solution, and the effect of pH, cell voltage, and ionic strength was optimized and modeled using the response surface methodology combined with Box–Behnken design. The results confirm that the optimum conditions to remove Cd(II) ions were: pH of 6.03, a voltage of 2.77 V, and NaCl concentration of 3 g/L. The experimental results showed a good fit for the Freundli
... Show More