The synthesis of nanoparticles (GNPs) from the reduction of HAuCl₄ ^.3H₂O by aluminum metal was obtained in aqueous solution with the use of Arabic gum as a stabilizing agent. The GNPs were characterized by TEM, AFM and Zeta potential spectroscopy. The reduction process was monitored over time by measuring ultraviolet spectra at a range of λ 520-525 nm. Also the color changes from yellow to ruby red, shape and size of GNP was studied by TEM. Shape was spherical and the size of particles was (12-17.5) nm. The best results were obtained at pH 6.

Metoclopramide HCl (MTB) is a potent antiemetic drug used for the treatment of nausea and vomiting. Many trials were made to prepare a satisfactory MTB orodispersible tablet using direct compression method.Various super disintegrants were used in this study which are croscarmellose sodium (CCS), sodium starch glycolate (SSG) and crospovidone (CP). The latter was the best in terms of showing the fastest disintegration time in the mouth.Among the different diluents utilized, it was found that a combination of microcrystalline cellulose PH101 (MCC 101), mannitol, dicalcium phosphate dihydrate (DPD) and Glycine was the best in preparing MTB orodispersible tablet with fastest disintegration time in the mouth.The physical parameters of the pre

The mucilage from the seeds of Lallemantia royleana family Labiatae was extracted and subjected to preformulation study for evaluation of its suitability for use as suspending agent. Furosemide suspensions were prepared using (1.5% w/v) of the extracted Lallemantia royleana mucilage, (1.5% w/v) chitosan and (0.35% w/v) xanthan gum. The mucilage was white in color and the average yield of dried mucilage obtained from L.royleana nutlets was 14 % w/w of the seeds used. It is sparingly soluble in water but swells in contact with it, giving a highly viscous solution. It is slightly acidic to neutral. It was found that the extracted natural mucilage of Lallemantia royleana exhibited a higher viscosity profil

Many approaches have been developed over time to counter the bioavailability limitations of poorly soluble drugs. With advances in nanotechnology in recent decades, this issue has been approached through the formulation of drugs as nanocrystals. Nanocrystals consist of pure drug(s) and a minimum of surface active agent(s) required for stabilization. They are carrier-free submicron colloidal drug delivery systems with a mean particle size typically in the range of 200 - 500 nm. By reducing particle size to nanoscale, the surface area available for dissolution is increased, and thus bioavailability is enhanced. Drug nanocrystals constitute a versatile formulation approach to enhance the pharmacokinetic and pharmacodynamic properties of poorly

Alpha-tocopherol acetate is one of the most important vitamin E derivatives,that were used  as antioxidants. Adsorbents like kaolin, magnesium carbonate, and microcrystalline cellulose were used successfully to incorporate oily alpha-tocopherol acetate into an acceptable powder dosage form. The results revealed that microcrystalline cellulose as an adsorbents gave the best results with 50% loading capacity at time, 8 minutes before and after incubation period (3 months at 30C°), while kaolin and magnesium carbonate have been shown a significant difference before and after incubation. Addition of 1% w/w magnesium carbonate to the kaolin enhanced the loading capacity by decreasing the time of adsorption from 20 to 6 minutes and 47

                The advertising mail is considered as one of potential tools that followed to transfer the printed messages to the consumers and public customers whom are located at homes or works. This type of advertising is preferable due to the zero expense to receive the announcements of products, which became recently one of the successful procedures to create new customers and keep them in touch with direct communication. It is also possible to send them to specific group of people who can be classified by the advertisers to select even by name their own clients to give the personality to the clients for a long term of communication.

&

PKE Sharquie MD, PDPAA Noaimi MD, DDV, FDSM Al-Ogaily MD, IOSR Journal of Dental and Medical Sciences (IOSR-JDMS), 2015

         This study aims to encapsulate atenolol within floating alginate-ethylcellulose beads as an oral controlled-release delivery system using aqueous colloidal polymer dispersion (ACPD) method.To optimize drug entrapment efficiency and dissolution behavior of the prepared beads, different parameters of drug: polymer ratio, polymer mixture ratio, and gelling agent concentration were involved.The prepared beads were investigated with respect to their buoyancy, encapsulation efficiency, and dissolution behavior in the media: 0.1 N HCl (pH 1.2), acetate buffer (pH 4.6) and phosphate buffer (pH 6.8). The release kinetics and mechanism of the drug from the prepared beads was investigated.All prepare

In this research the a-As flims have been prepared by thermal evaporation with thickness 250 nm and rata of deposition (1.04nm/sec) as function to annealing temperature (373 and 373K), from XRD analysis we can see that the degree of crystalline increase with , and I-V characteristic for dark and illumination shows that forward bias current varieties approximately exponentially with voltage bias. Also we found that the quality factor and saturation current dependence on annealing temperatures.

    Ni2O3 nanomaterial, a phase of nickel oxide, is synthesized by a simple chemical process. The pure raw materials used in the present process were nickel chloride hexahydrate NiCl2.6H2O and potassium hydroxide KOH by utilizing temperature at 250 oC for 2 hour.  The structural, morphological and optical properties of the synthesized specimens of Ni2O3 were investigated employing diverse techniques such as XRD, AFM, SEM and UV-Vis, respectively. The XRD technique confirms the presence of Ni2O3 nanomaterial with crystal size of 57.083 nm which indexing to the (2θ) of 31.82; this results revealed the Ni2O3 was a phase of nickel oxide with Nano structure. The synthesized Ni2O3 will be useful in manufacturng electrodes materials f