Background: An injury to both the primary and permanent teeth and the supporting structures is one of the most common dental problems seen in children. Splinting is usually difficult or impossible to perform in the primary dentition (due to diminutive room size and lack of patient cooperation). Healing must, therefore, occur despite mobility at the fracture line, usually resulting in interposition of connective tissue. In some instances, infection will occur in the coronal pulp. The present study reported a case of trauma to the anterior primary teeth and alveolar bone in a four year old child. The trauma has caused fracture to the crowns and roots of the primary anterior teeth. The following case was managed in a procedure that may

In this study, SnO2 nanoparticles were prepared from cost-low tin chloride (SnCl2.2H2O) and ethanol by adding ammonia solution by the sol-gel method, which is one of the lowest-cost and simplest techniques. The SnO2 nanoparticles were dried in a drying oven at a temperature of 70°C for 7 hours. After that, it burned in an oven at a temperature of 200°C for 24 hours. The structure, material, morphological, and optical properties of the synthesized SnO2 in nanoparticle sizes are studied utilizing X-ray diffraction. The Scherrer expression was used to compute nanoparticle sizes according to X-ray diffraction, and the results needed to be scrutinized more closely. The micro-strain indicates the broadening of diffraction peaks for nano

One of the most important problems in tablet process is to control the flow of the catalyst through the hopper; Controlling the flow can be done either by changing the size of particles or added the different lubricant (stearic acid, starch, graphite) or blending of different lubricants. The study showed that we can control (increase or decrease) on the flow of the catalyst through the hopper by blending different lubricants for the constant percentage. The flow increasing when particles size (0.6 mm) and then decrease with or without lubricants, no effect on flow when particles size lower than (0.2 mm) with use that lubricants, and good flow on (0.4 mm) when use stearic acid and starch.

A thin CdS Films have been evaporated by thermal evaporation technique with different thicknesses (500, 1000, 1500 and 2000Å) and different duration times of annealing (60, 120 180 minutes) under 573 K annealing temperature, the vacuum was about 8 × 10-5 mbar and substrate temperature was 423 K. The structural properties of the films have been studied by X- ray diffraction technique (XRD). The crystal growth became stronger and more oriented as the film thickness (T) and duration time of annealing ( Ta) increases.

Background: An injury to both the primary and permanent teeth and the supporting structures is one of the most common dental problems seen in children. Splinting is usually difficult or impossible to perform in the primary dentition (due to diminutive room size and lack of patient cooperation). Healing must, therefore, occur despite mobility at the fracture line, usually resulting in interposition of connective tissue. In some instances, infection will occur in the coronal pulp. The present study reported a case of trauma to the anterior primary teeth and alveolar bone in a four year old child. The trauma has caused fracture to the crowns and roots of the primary anterior teeth. The following case was managed in a procedure that may prov

BACKGROUND: The degree of the development of coronary collaterals is long considered an alternate – that is, a collateral – source of blood supply to an area of the myocardium threatened with vascular ischemia or insufficiency. Hence, the coronary collaterals are beneficial but can also promote harmful (adverse) effects. For instance, the coronary steal effect during the myocardial hyperemia phase and that of restenosis following coronary angioplasty. OBJECTIVES: Our study explores the contribution of coronary collaterals – if any exist – while considering other potential predictors, including demographics and medical history, toward the left ventricular (LV) dysfunction measured through the LV ejection fraction (LVEF). METH

The study objectives were to 1) explore the real-world experience of hospital pharmacists with the differences in effectiveness safety, and interchangeability between biosimilar medicines and their reference biological counterparts, 2) reveal pharmacist recommendations to enhance the safety of biopharmaceutical medicines in public hospitals.

The study has a mixed-method design where the core component was qualitative (interviews) and the supplemental component was quantitative (adverse drug reaction, ADR, reports). This qualitative component included semi-structured (mostly face-to-face) interviews involving hospital pharmacists from different hospitals with experience with biological or biosimilar medicines. The interviews were c

Thermal conductivity for epoxy composites filled with Al2O3 and Fe2O3 are
calculated, it found that increasing the weight ratio of Al2O3 and Fe2O3 lead to
increase in the values of thermal conductivity, but the epoxy composite filled with
Fe2O3, have values of thermal conductivity less than for epoxy composite filled with
Al2O3, for the same weight ratio. Also thermal conductivity calculated for epoxy
composites by contact to every two specimens (like sandwich) content same weight
ratio of alumina-oxide and ferrite-oxide, its found that the value of thermal
conductivity lays between the values of epoxy filled Al2O3 and of epoxy filled Fe2O3

This work describes, selenium (Se) films were deposited on clean glass substrates by dc planar magnetron sputtering technique.The dependence of sputtering deposition rate of Se film deposited on pressure and DC power has been studied. The optimum argon pressure has range (4x10-1 -8x10-2 )mbar. The optical properties such as absorption coefficient (α) was determined using the absorbance and transmission measurement from UnicoUV-2102 PC spectrophotometer, at normal incidence of light in the wavelength range of 200-850 nm. And also we calculated optical constants(refractive index (n), dielectric constant (εi,r), and Extinction coefficient (κ) for selenium films.