Ureteric obstruction is rarely noted in cases of gastric cancer. Its involvement by distant metastasis from gastric adenocarcinoma without direct invasion is an exceptionally unusual occurrence. This is the story of a 58-year-old man who arrived at the emergency department with acute flank pain and fever. He was initially diagnosed with obstructive pyelonephritis after the discovery of a new onset, complete ureteric obstruction on the left side. Subsequent investigations and follow-up revealed the presence of gastric adenocarcinoma with possible ureteric metastasis bilaterally, flank pain and hydronephrosis were the first and only presentations of gastric cancer. The rarity of the condition and the unusual presentation encouraged us to r

There are no single materials which can withstand all the extreme operating conditions in modern technology.  Protection of the metals from hostile environments has therefore become a technical and economic necessity.  

In this work, for enhancing their wear-resistance, boride layers were deposited on the surface of low carbon steel by a pack cementation method at 850 °C for (2, 4, and 6) h using vacuum furnace. The boronizing process was achieved using different concentration of boron source (20, 25, and 30) % wt. into coating mixture to optimize the best conditions which ensure the higher properties with lower time. The coating was characteristic by X ray diffraction (XRD), and it is confirmed t

The microstructure and wear properties of 392 Al alloy with different Mg contents were studied using centrifugal casting. All melted alloys were heated to 800 ºC and poured into the preheated centrifugal casting mold (200-250 ^ºC) at different mould rotational speeds (1500, 1900 and 2300 r.p.m).  It is clear from the results obtained that wear rate was dependent on the Mg content, applied load and mould rotational speed. Furthermore, wear test showed that the minimum wear rate was found in the inner layer of produced rings at mould rotational speed of 1900 r.p.m and Mg content of 5%.

This research studies Reinforcing and applied load of  Wear Rate for Epoxy composites contains from epoxy resin (Ep) as a matrix material and reinforced by Gawain red wood flour , Russian white wood flour , glass powder and rock wool fibers , with volume fraction (20%) for all samples in lab conditions.  by using the load (10,20 ,30 ,40) Newton of iron disc for testing  time(10) minute, and the results have shown that the reinforcing of epoxy resin led to decrease  wear rate for all samples except the hybrid composites reinforced earth glass powder , that the wear rate values  decrease  from   (22×10-9g/cm) to (4×10-9g/cm) of composite material(Ep+R.W.F) and thus(Ep+W.W.F)   at la

The work reported in this study focusing on the abrasive wear behavior for three types of pipes used in oil industries (Carbone steel, Alloy steel and Stainless steel) using a wear apparatus for dry and wet tests, manufactured according to ASTM G65. Silica sand with
hardness (1000-1100) HV was used as abrasive material. The abrasive wear of these pipes has been measured experimentally by measuring the wear rate for each case under different sliding speeds, applied loads, and sand conditions (dry or wet). All tests have been conducted using sand of particle size (200-425) µm, ambient temperature of 34.5 °C and humidity 22% (Lab conditions).
The results show that the material loss due to abrasive wear increased monotonically with

In this study, nanocomposites have been prepared by adding
multiwall carbon nanotubes (MWCNTs) with weight ratios (0, 2, 3,
4, 5) wt% to epoxy resin. The samples were prepared by hand lay-up
method. Influence of an applied load before and after immersion in
sodium hydroxide (NaOH) of normality (0.3N) for (15 days) at
laboratory temperature on wear rate of Ep/MWCNTs
nanocomposites was studied. The results showed that wear rate
increases with increasing the applied load for the as prepared and
immersed samples and after immersion. It was also found that epoxy
resin reinforced with MWCNTs has wear rate less than neat epoxy.
The sample (Ep + 5wt% of MWCNTs) has lower wear rate. The
immersion effect in base so