Abstract: Tin oxide thin films were deposited by direct current (DC) reactive sputtering at gas pressures of 0.015 mbar – 0.15 mbar. The crystalline structure and surface morphology of the prepared SnO2 films were introduced by X-ray diffraction (XRD) and atomic force microscopy (AFM). These films showed preferred orientation in the (110) plane. Due to AFM micrographs, the grain size increased non-uniformly as the working gas pressure increased.

Reactive Powder Concrete (RPC) can be incorporate as a one of the most important and progressive concrete technology. It is a special type of ultra-high strength concrete (UHSC) that’s exclude the coarse aggregate from its constitutive materials. In this research an experimental study had been carried out to investigate the effect of using three types of materials (porcelain aggregate) and others sustainable materials (glass waste and granular activated carbon) as a partial replacement of fine aggregate. Four percentages had considered (0, 10, 15 and 20) % to achieve better understanding for the influence of these materials upon the compressive strength of RPC. Four curing ages had included in this study, these are; 7, 28, 60 and

In this work, novel copolymers of poly(adipic anhydride-co-mannitol) were synthesized by melting condensation polymerization of poly(adipic anhydride) with five percentages of mannitol sugar, 1 to 5 Wt.%. These copolymers were purified and then, characterized by FT-IR, which was proved that the cross-linking reaction was caused by nucleophilic attack of mannitol hydroxyl group to acidic anhydride groups of poly(adipic anhydride) backbone and new ester groups were formed and appeared. Also, modified organic-soluble chitosan, N-maleoyl-chitosan, were synthesized by grafting reaction of chitosan with maleic anhydride in DMF as solvent, and it was also purified and characterized by FT-IR. Biodegradation in vitro of the IPNs of poly(adipic anhyd

Fabrication of solar cell prepared by thermal spray and vacuum thermal evaporation method on silicon wafer(n-type) and studying its efficiency. The film have been deposited on three layers(ZnO then CdS and CdTe) on Si and glass respectively.Direct energy gap was calculated and equal to (4.3,3.4,3)eV and indirect energy gap equal to (3.5,2.5,1.5)eV respectively . Efficiency was calculated for the cell of area 2cm2 it was equal to 0.14%.

       Copper Phthalocyanine (CuPc) thin film with and without multi-walled carbon nanotubes (MWCNTs) is prepared using the solution based method and used in gas sensor and solar cell applications. The structural characteristics of the CuPc thin films showed a single peak around 7^o with the preferred orientation for charge transportation. Using atomic force microscopy (AFM), morphological properties show a rough surface with some aggregates and ribbons. The optical absorption properties were determined using UV-Visible absorption spectroscopy; the optical band gap has varied after adding MWCNTs to CuPc. Electrical conductivity of CuPc:MWCNTs composite is higher than that of the pure CuPc. The CuPc thin film sensr have sh

Reactive arthritis (ReA) has been as joint developing after infection, it belongs to spongylo arthritis (SpA). The etiology of this disease was multi factorial, the combination between genetic and environmental factors for triggering this disease. This study included 75 Iraqi Arab patients and 39 healthy control. Urine samples and blood were collected from each subject. The results showed that Escherichia coli bacteria (E. coli) was isolated from 32% of urine samples. HLA-B*27 allele frequencies was higher in ReA patients infected with E. coli. This lead to suggest that E. coli may be trigger factor in ReA patients with UTI which had HLA-B*27 positive.

This paper studies the behavior of reinforced Reactive Powder Concrete (RPC) two-way slabs under static and repeated load. The experimental program included testing six simply supported RPC two-way slabs of 1000 mm length, 1000 mm width, and 70 mm thickness. All the tested specimens were identical in their material properties, and reinforcement details except their steel fibers content. They were cast in three pairs, each one had a different steel fibers ratio (0.5 %, 1 %, and 1.5 %) respectively. In each pair, one specimen was tested under static load and the other under five cycles of repeated load (loading-unloading). Static test results revealed that increasing steel fibres volume fraction from 0.5 % to 1 % and from 1% to 1.5%,

     In this work,  we presented a study of the structural formula for a new series of complexes with Ag(I), Cu(II), Zn(II), and Cd(II) derived from the guanine azo dye ligand 2-amino-8-((3-hydroxyphenyl)diazinyl)-1,7-dihydro-6H-purin-6-one (HAG), which is investigated using various physicochemical analyses, spectroscopic techniques (FT-IR, U.V-VIS, and ¹H NMR), thermogravimetric analysis (TGA). In addition, elemental analyses, magnetic susceptibility, and molar conductance measurements were all stabilized. As well as the mole ratio, stability constant, and Gibbs free energy were studied for all complexes, where they showed high stability and spontaneous synthesis. The Cu(II) complex was suggested to have octahedral stere

New complexes of M(II) with mixed ligand of 5-Chlorosalicylic acid (CSA) C7H5ClO3 as primary ligand and L- Valine (L-Val) C5H11NO2 as a secondary ligand were prepared and characterized by elemental analysis (C.H.N), UV., FT-IR, magnetic susceptibility, μeff (B.M) as well as the conductivity measurements (Λm ). In the complexes, the 5-chlorosalicylic acid is bidentate in all complexes coordinating through –OH- and –COO- groups; also L-Valine behaves as a bidentate ligand in all complexes through –NH2 and –COO- groups. These five mixed ligand complexes formulated as Na3[M(CSA)2(L-Val)]. The proposed molecular structure for all complexes is octahedral geometries. The synthesis complexes were tested in vitro for against four bacteria

New complexes of M(II) with mixed ligand of 5-Chlorosalicylic acid (CSA) C7H5ClO3 as primary ligand and L- Valine (L-Val) C5H11NO2 as a secondary ligand were prepared and characterized by elemental analysis (C.H.N), UV., FT-IR, magnetic susceptibility, µeff (B.M) as well as the conductivity measurements (Λm ). In the complexes, the 5-chlorosalicylic acid is bidentate in all complexes coordinating through –OH- and –COO- groups; also L-Valine behaves as a bidentate ligand in all complexes through –NH2 and –COO- groups. These five mixed ligand complexes formulated as Na3[M(CSA)2(L-Val)]. The proposed molecular structure for all complexes is octahedral geometries. The synthesis complexes were tested in vitro for against four bacteria