Improving the Physical and Mechanical Properties of Fireclay Refractory Bricks by Added Bauxite
...Show More Authors

In this study, the investigation of Local natural Iraqi rocks kaolin with the addition of different proportions of bauxite and its effect on the physical and mechanical properties of the produced refractories was conducted. Kaolin/bauxite mixture was milled and classified into various size fractions, the kaolin (less than 105 μm) and the bauxite (less than 70μm). The specimens were mixed from kaolin and bauxite in ranges B1 (95+5)%, B2 (90+10)%, B3(85+15)%, and B4 (80+20)%  respectively. The green specimens were shaped by the semi-dry method using a hydraulic press and a molding pressure of 7 MPa with the addition of (9-12) %wt. of PVA ratio. After molding and drying, the specimens were fired at (1100, 1200 and 1300) °C. Physical properties (density, porosity, water absorption) and mechanical properties (indirect tensile strength and hardness) were measured for all the prepared samples. The results showed that the porosity was increased and the density was decreased, such increase and decrease affected on to the mechanical properties for refractory. The highest values of indirect tensile strength and hardness were obtained at 20% Bauxite at 1300 °C (0.85386 MPa, 1411Kg / mm²) respectively.

 

Crossref
View Publication Preview PDF
Quick Preview PDF
Publication Date
Sun Mar 04 2018
Journal Name
Iraqi Journal Of Science
Assessment of ISNAG fluorimeter (Total fluorescence measurements at+ 90° & - 90° using four solar cell on each side for 100mm distance at 2mm path length) with well-known fluorescent molecules via CFIA
...Show More Authors

Two well-known fluorescent molecules: fluorescein sodium salt (FSS) and 2,7-dichloro fluorescein (DCF) were tried to prove the efficiency, trustability and repeatability of ISNAG fluorimeter by using discrete and continuous flow injection analysis modes.A linear range of 0.002-1 mmol/L for FSS and 0.003-0.7 mmol/L was for DCF, with LOD 0.0018 mmol/L and 0.002 mmol/L for FSS and DCF respectively, were obtained for discrete mode of analysis. While the continuous mode gave a linear range of 0.002-0.7 mmol/L and 0.003-0.5 mmol/L for FSS and DCF respectively, the LOD were 0.0016mmol/L and 0.0018 mmol/L for FSS and DCF respectively. The results were compared with classical method at variable λex for both fluorescent molecules at 95

... Show More
View Publication Preview PDF
Publication Date
Tue Jan 21 2025
Journal Name
Journal Of Baghdad College Of Dentistry
Shear bond strength of stainless steel brackets bonded to porcelain surface treated with 1.23% acidulated phosphate fluoride gel compared to hydro fluoric acid with silane coupling agent (In vitro comparative study)
...Show More Authors

Background: With the increasing demands for adult orthodontics, a growing need arises to bond attachments to porcelain surfaces. Optimal adhesion to porcelain surface should allow orthodontic treatment without bond failure but not jeopardize porcelain integrity after debonding.The present study was carried out to compare the shear bond strength of metal bracket bonded to porcelain surface prepared by two mechanical treatments and by using different etching systems (Hydrofluoric acid 9% and acidulated phosphate fluoride 1.23%). Materials and Methods: The samples were comprised of 60 models (28mm *15mm*28mm) of metal fused to porcelain (feldspathic porcelain). They were divided as the following: group I (control): the porcelain surface left u

... Show More
View Publication Preview PDF
Publication Date
Sun Jan 26 2020
Journal Name
Journal Of Global Pharma Technology
Synthesis, Characterization of 2-azido-4-(azido (2-azido-2-( azido carbonyl)-1,3-dioxoian-4-yl)methyl)– 5-((R-azido (hydroxyl) methyl- 1,3-dioxole-2-carbonyl azide. ethanol. hydrate (L-AZD) with Some Metal Complexes
...Show More Authors

The reaction oisolated and characterized by elemental analysis (C,H,N) , 1H-NMR, mass spectra and Fourier transform (Ft-IR). The reaction of the (L-AZD) with: [VO(II), Cr(III), Mn(II), Co(II), Ni(II), Cu(II), Zn(II), Cd(II) and Hg(II)], has been investigated and was isolated as tri nuclear cluster and characterized by: Ft-IR, U. v- Visible, electrical conductivity, magnetic susceptibilities at 25 Co, atomic absorption and molar ratio. Spectroscopic evidence showed that the binding of metal ions were through azide and carbonyl moieties resulting in a six- coordinating metal ions in [Cr (III), Mn (II), Co (II) and Ni (II)]. The Vo (II), Cu (II), Zn (II), Cd (II) and Hg (II) were coordinated through azide group only forming square pyramidal

... Show More