Effect of bentonite addition on some properties of porcelain
...Show More Authors

Porcelain is one of the most important ceramic materials with a wide range of traditional and technical applications. Since most mixtures of porcelain have a high sintering temperature, bentonite has been added in this research to improve the characteristics of sintering and burning. The porcelain mixture consisted of the following Iraqi raw materials: 30% wt kaolin, 30 wt% non-plastic clay (grog), 10% wt sodium feldspar, 10 wt% potassium feldspar and 20 wt% flint. After the mechanical mixing process and transfer the powder mixture to the slurry by adding distilled water, then different weight percentage of the sodium bentonite(0, 2.5, 5, 7.5 and 10) wt% was added. The specimens were prepared by using the solid casting method, and after the drying process, the specimens were burned at1100 oC. The results of x-ray diffraction showed that bentonite reduced the crystallization of the main ceramic phases (mullite, quartz), which stimulates the appearance of amorphous glass phases. Also, the loss of mass on ignition increased when the addition of bentonite from 5.66% to 8.2%. There was also a great convergence between the granules of porcelain when adding bentonite and thus increase the shrinkage of the dimensions from 9.33% to 12.37 %. This led to increasing the bulk density from 1.97 g/cm3 to 2.67 g/cm3 at firing temperature 1100oC, and the porosity was decreased from 17.1% to 1.44%. Diametrical strength and flexural strength (bending) increased with bentonite (14.88 to 34.46MPa), (6.2 to 8.65 MPa), respectively.

 

Crossref
View Publication Preview PDF
Quick Preview PDF
Publication Date
Sat Mar 18 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
The Effect of Annealing on The Structural and Optical Properties of SnS Thin Films
...Show More Authors

 Thin  films   of  pure   tin mono-sulfide  SnS with thicknesses of   (0.85) μm  were prepared by chemical spray  pyrolysis  technique  and  annealed for  two  hours with 673K.The effect of annealing on structural and optical properties for films prepared was  studied.  X-Ray   diffraction  analysis  showed   the  polycrystalline  with   orthorhombic structure.  It was  found  that   annealing process increased the intensity of diffraction peaks. Optical   properties  of  all  samples  were studied by  recording  the  absorption  and  transmission &nbsp

... Show More
View Publication Preview PDF
Publication Date
Tue Jan 08 2019
Journal Name
Iraqi Journal Of Physics
Effect of sputtering power on optical Properties of RF sputtering deposited Ti6Al4V Thin Films
...Show More Authors

Ti6Al4V thin film was prepared on glass substrate by RF
sputtering method. The effect of RF power on the optical properties
of the thin films has been investigated using UV-visible
Spectrophotometer. It's found that the absorbance and the extinction
coefficient (k) for deposited thin films increase with increasing
applied power, while another parameters such as dielectric constant
and refractive index decrease with increasing RF power.

View Publication Preview PDF
Crossref
Publication Date
Wed Sep 01 2021
Journal Name
Iraqi Journal Of Physics
The Effect of Etching Time On Structural Properties of Porous Quaternary AlInGaN Thin Films
...Show More Authors

Using photo electrochemical etching technique (PEC), porous silicon (PS) layers were produced on n-type silicon (Si) wafers to generate porous silicon for n-type with an orientation of (111) The results of etching time were investigated at: (5,10,15 min). X-ray diffraction experiments revealed differences between the surface of the sample sheet and the synthesized porous silicon. The largest crystal size is (30 nm) and the lowest crystal size is (28.6 nm) The analysis of Atomic Force Microscopy (AFM) and Field Emission Scanning Electron Microscope (FESEM) were used to research the morphology of porous silicon layer. As etching time increased, AFM findings showed that root mean square (RMS) of roughness and po

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Sun Jun 05 2011
Journal Name
Baghdad Science Journal
Effect of Milk Substitution with liquid whey on the quality properties of fatty cake
...Show More Authors

This study exposed to use the liquid whey (which was produced from of soft cheese processed) partially or completely instead of milk in fatty cake, this whey residue is still not used, instead it is thrown in rivers which effect different environment and economic problems. Different concentrations was used (25% , 50% , 75% , and 100%) of whey in baked cake , Volume , height and other different properties ( panel taste ) was studied too . Sensory evaluation results showed that an improved in all the character of the baked cake was happen by the used of 25% and 50% of the whey in comparison with the control treatment, the 75% replacement showed a decrease in appearance , texture and tenderness , while the degrees of color and fla

... Show More
View Publication Preview PDF
Crossref
Publication Date
Mon Oct 01 2012
Journal Name
Iraqi Journal Of Physics
Effect of Cu doping on optical properties of Mn2O3 films prepared by spray pyrolysis
...Show More Authors

Thin films of Mn2O3 doped with Cu have been fabricated using the simplest and cheapest chemical spray pyrolysis technique onto a glass substrate heated up to 250 oC. Transmittance and absorptance spectra were studied in the wavelength range (300 -1100) nm. The average transmittance at low energy was about 60% and decrease with Cu doping, Optical constants like refractive index, extinction coefficient and dielectric constants (εr), (εi) are calculated and correlated with doping process.

View Publication Preview PDF
Publication Date
Thu Oct 01 2009
Journal Name
Iraqi Journal Of Physics
The effect of Titanium dioxide on the tensile properties of Polycarbonate and Polystyrene Polymers
...Show More Authors

This research study the effect of Titanium dioxide on the tensile properties of
Polystyrene (PS) and Polycarbonate (PC) polymers. The stress – strain curve for pure PS
and pure PC, shows that Young modulus for PS is higher than Young modulus for PC,
because PS have higher ultimate strength than PC.
The addition of TiO2 to PS and PC will reduce the Young modulus and ultimate stress,
because the TiO2 particles will reduces or freeze the orientation of these molecular chain
and reduced the toughness of PC, while when the TiO2 were added to PS, the value of
toughness will be stabilized because TiO2 particles make these chains interlocked and the
mobility of the chains will be restrict.

View Publication Preview PDF
Publication Date
Thu Dec 01 2011
Journal Name
Journal Of Engineering
EFFECT OF COOLING RATE ON MECHANICAL PROPERTIES OF EUTECTIC AND HYPOEUTECTIC Al-Si ALLOYS
...Show More Authors

In this research the effect of cooling rate and mold type on mechanical properties of the eutectic
and hypoeutectic (Al-Si) alloys has been studied. The alloys used in this research work were (Al- 12.6%Si
alloy) and (Al- 7%Si alloy).The two alloys have been melted and poured in two types of molds with
different cooling rates. One of them was a sand mold and the other was metal mold. Mechanical tests
(hardness, tensile test and impact test) were carried out on the specimens. Also the metallographic
examination was performed.
It has been found that the values of hardness for the alloys(Al-12.6%Si and Al-7%Si) which poured in
metal mold is greater than the values of hardness for the same alloy when it poured in a heated

... Show More
View Publication Preview PDF
Crossref (2)
Crossref
Publication Date
Sun Nov 25 2018
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Effect of Cu doping on the electrical Properties of ZnTe by Vacuum Thermal Evaporation
...Show More Authors

In this study, the ZnTe thin films were deposited on a glass substrate at a thickness of 400nm using vacuum evaporation technique (2×10-5mbar) at RT. Electrical conductivity and Hall effect measurements have been investigated as a function of variation of the doping ratios (3,5,7%) of the Cu element on the thin ZnTe films. The temperature range of (25-200°C) is to record the electrical conductivity values. The results of the films have two types of transport mechanisms of free carriers with two values of activation energy (Ea1, Ea2), expect 3% Cu. The activation energy (Ea1) increased from 29meV to 157meV before and after doping (Cu at 5%) respectively. The results of Hal

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Thu Mar 09 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Effect of Gamma Ray Irradiation on Structural and Optical Properties of ZnO Thin Films
...Show More Authors

In this research, the structural and optical measurements were made on the Zinc oxide (ZnO) films prepared by two methods once by using chemical spray pyrolysis technique, and another by using thermal evaporation technique before and after irradiation by Gamma –Ray (γ – rays) from source type (Cs 137) with an energy (0.611)MeV as a function of gamma dose (0.15,0.3 and 0.45) Gy. The thickness of all films prepared by two method was about (300 ± 50) nm. XRD is used to characterize the structural properties, the results demonstrated that all samples prepared by two method before and after irradiation have polycrystalline structure with a preferred orientation (002).Also it showed that the structural properties are weakly

... Show More
View Publication Preview PDF
Publication Date
Mon Apr 10 2017
Journal Name
Ibn Al-haitham Journal For Pure And Applied Sciences
Effect of Doping Cu on the Structural and Optical Properties of (CdTe) Thin Films
...Show More Authors

   In this research we studied  the structural and optical properties of (CdTe) thin films which have been prepared  by thermal evaporation deposition method on the glass substrate at R.T with thickness (450  25) nm., as  a function of doping  ratio with copper element  in (1,3,5) % rate .The structure  measurement  by X-ray diffraction (XRD) analyses shows that the single phase of (CdTe) with polycrystalline structure with a preferred orientation [111].   The optical  measurement shows that the (CdTe) films have a direct energy gap, and they decrease with the increase of doping ratio reaching to 5% . The optical constants are investigated and calculated, such as absorpti

... Show More