1 - is not affected by illiteracy cells painful eggs after the first and seventh of the various concentrations used but found the effect of 21 and 35 days after treatment2 - repeat chromosomal aberrations illiteracy eggs cells no different distortions occurring sperm cells During Altnavra phase3 - increased chromosomal aberrations increase the dose especially for 21 and 35 days4 - The connective tissue is more sensitive phase of the pesticide from Altnavra phase

The research aims to apply the activities of the green value chain as one of the modern administrative techniques that economic units resort to develop solutions to the pollution problems that occur due to the activity of economic units and their products that may cause damage to the environment as well as the waste of natural resources and to identify the production of environmentally friendly products and reduce the costs of environmental failure of both types Internal and external that may be borne by economic units such as taxes, fines and compensation due to non- observance of environmental requirements and the preservation of human health and protection of the environment.To achieve the goal of the research, the researchers re

New Fourteen compounds were synthesized in four steps. The first step included synthesis of 2-biphenyl fused ring of imidazo(1,2- a)pyrimidine from the reaction of 2-aminopyrimidine and biphenyl phenacyl bromide . The second step was introduced aldehyde group from the reaction of 2-biphenyl fused rings of imidazo(1,2-a)pyrimidine with POCl3 in presence of DMF and CHCl3. 3-Carbaladehyde derivatives of fused imidazo/pyrimidine was reacted with different aromatic amines to afford new Schiff bases. These new 3- imines derivatives was reduced by using sodiumborohydride to yield another new 3-aminomethyl-2-biphenyl imidazo (1,2-a)pyrimidine derivatives in moderate yield .Some new prepared compounds were identified by melting point, FT- IR , 13C-

In the present work, different thicknesses of CdS film were prepared by chemical bath deposition. Z-Scan technique was used to study the nonlinear refractive index and nonlinear absorption coefficients. Linear optical testing were done such as transmission test, and thickness of films were done by the interference fringes (Michelson interferometer). Z-scan experiment was performed at 650nm using CW diode laser and at 532nm wavelength. The results show the effect of self-focusing and defocusing that corresponds with nonlinear refraction n2. The effect of two-photon absorption was also studied, which correspond to the nonlinear absorption coefficient B.

In this study, synthesised new ligand: potassium 2,2'-(quinoxaline-2,3- diyl)bis(1-phenylhydrazinecarbodithioate) (L). The ligand synthesised by reacting N1,N2-dip-tolyloxalamide as the starting material with CS2 and KOH to add the CS2 group and then with phenylendiammine to achieve (L). The ligand used in the synthesis of complexes with (CoII, NiII and CdII). The new ligand and its complexes characterised by FT-IR, UV-Vis, 1H, 13C-NMR, Mass spectroscopy, and elemental analysis, in addition to the above techniques were using magnetic moment, atomic absorption, chloride content, and melting point to describe the metal complexes.

To reduce solar radiation transmittance into buildings through windows facing east or west during summer, a window inclination from vertical position is suggested. The inclination of the window glazing and the rate of unwanted solar radiation during summer can be calculated knowing the dialy inclination of the sun rays. The inclination of window glazing depends on the latitude of the position required. For instance in Baghdad which is at about 33o north latitude a slope of 15o for window glazing is sufficient to prevent about 419 MJ/m2 of total solar radiation energy from penetration during summer for clear glazing of window facing east. This value drops to about 96 MJ/m2 during winter. Therefore the ratio between the energy saved for co

Alloys of InxSe1-x were prepared by quenching technique with
different In content (x=10, 20, 30, and 40). Thin films of these alloys
were prepared using thermal evaporation technique under vacuum of
10-5 mbar on glass, at room temperature R.T with different
thicknesses (t=300, 500 and 700 nm). The X–ray diffraction
measurement for bulk InxSe1-x showed that all alloys have
polycrystalline structures and the peaks for x=10 identical with Se,
while for x=20, 30 and 40 were identical with the Se and InSe
standard peaks. The diffraction patterns of InxSe1-x thin film show
that with low In content (x=10, and 20) samples have semi
crystalline structure, The increase of indium content to x=30
decreases degree o