Direct Shear Behavior of Fiber Reinforced Concrete Elements
...Show More Authors

Improving the accuracy of load-deformation behavior, failure mode, and ultimate load capacity for reinforced concrete members subjected to in-plane loadings such as corbels, wall to foundation connections and panels need shear strength behavior to be included. Shear design in reinforced concrete structures depends on crack width, crack slippage and roughness of the surface of cracks.

This paper illustrates results of an experimental investigation conducted to investigate the direct shear strength of fiber normal strength concrete (NSC) and reactive powder concrete (RPC). The tests were performed along a pre-selected shear plane in concrete members named push-off specimens. The effectiveness of concrete compressive strength, volume fraction of steel fiber, and shear reinforcement ratio on shear transfer capacity were considered in this study. Furthermore, failure modes, shear stress-slip behavior, and shear stress-crack width behavior were also presented in this study.

Tests’ results showed that volume fraction of steel fiber and compressive strength of concrete in NSC and RPC play a major role in improving the shear strength of concrete. As expectedly, due to dowel action, the shear reinforcement is the predominant factor in resisting the shear stress. The shear failure of NSC and RPC has the sudden mode of failure (brittle failure) with the approximately linear behavior of shear stress-slip relationship till failure. Using RPC instead of NSC with the same amount of steel fibers in constructing the push-off specimen result in high shear strength. In NSC, shear strength influenced by the three major factors; crack surface friction, aggregate interlock and steel fiber content if present. Whereas, RPC has only steel fiber and cracks surface friction influencing the shear strength. Due to cementitious nature of RPC in comparisons with NSC, the RPC specimen shows greater cracks width.

It is observed that the Mattock model gives very satisfactory predictions when applied to the present test results with a range of parametric variations; ranging from 0 % to 0.5 % in steel fibers content; from 0 % to 0.53 % in transverse reinforcement ratio; from 15 to 105 MPa in compressive strength of concrete. While it gives a poor prediction for a specimen with 1% steel fiber.

 

View Publication Preview PDF
Quick Preview PDF
Publication Date
Thu Sep 30 2004
Journal Name
Iraqi Journal Of Chemical And Petroleum Engineering
Corrosion Inhibition of Steel Reinforcement in Concrete
...Show More Authors

View Publication Preview PDF
Publication Date
Mon Jun 01 2020
Journal Name
Iraqi Journal Of Physics
A Calculation real abundance of gaseous elements of the comet PanSTARRS C/2011 S4
...Show More Authors

    X-ray emission contains some of the gaseous properties is produced when the particles of the solar wind strike the atmosphere of comet ISON and PanSTARRS Comets. The data collected with NASA Chandra X-ray Observatory of the two comets, C/2012 S1 (also known as Comet ISON) and C/2011 S4 (Comet PanSTARRS) are used in this study.

   The real abundance of the observed X-ray spectrum elements has been extracted by a new simple mathematic model. The study found some physical properties of these elements in the comet’s gas such as a relationship between the abundance with emitted energy. The elements that have emission energy (2500-6800) eV, have abundance (0.1-0.15) %, while the elements

... Show More
View Publication Preview PDF
Crossref
Publication Date
Sat Dec 01 2018
Journal Name
Sustainable Materials And Technologies
A sustainable pavement concrete using warm mix asphalt and hydrated lime treated recycled concrete aggregates
...Show More Authors

Recently, increasing material prices coupled with more acute environmental awareness and the implementation of regulation has driven a strong movement toward the adoption of sustainable construction technology. In the pavement industry, using low temperature asphalt mixes and recycled concrete aggregate are viewed as effective engineering solutions to address the challenges posed by climate change and sustainable development. However, to date, no research has investigated these two factors simultaneously for pavement material. This paper reports on initial work which attempts to address this shortcoming. At first, a novel treatment method is used to improve the quality of recycled concrete coarse aggregates. Thereafter, the treated recycled

... Show More
View Publication
Crossref (28)
Crossref
Publication Date
Thu Nov 01 2012
Journal Name
Journal Of Cosmetics, Dermatological Sciences And Applications
Direct melanocytes transplant from normal donor area into vitiliginous recipient area by dermabrasion technique
...Show More Authors

KE Sharquie, AA Noaimi, HA Al-Mudaris, Journal of Cosmetics, Dermatological Sciences and Applications, 2012 - Cited by 6

View Publication
Publication Date
Sun Mar 07 2010
Journal Name
Baghdad Science Journal
The Direct Gene Injection Using of Egg Yolk Emulsion as Carrier and its Comparison with Liposomes.
...Show More Authors

The efficiency of egg yolk emulsion in coating DNA and its delivery across cellular membranes was evaluated in comparison with liposomes DOPE . The murine leukemia viral oncogene v-abl , cloned on pBR322 was used as a DNA substrate for direct injection into mice tissue . the DNA complexes were prepared by mixing the DNA with egg yolk emulsion and liposome . Each was directly injected into mice peritoneal cavity with proper control. The gene delivery was examined phenotypically by blood analysis and cytogenetic analysis . Chromosomal changes were detected in the bone marrow as from the fourth day post inoculation through the eleventh day when chromosomal ring s could be seen . this was accompanied by decrease in the WBC count ,

... Show More
View Publication Preview PDF
Crossref
Publication Date
Sun Mar 13 2011
Journal Name
Baghdad Science Journal
Evaluation the efficiency of Trichomonas vaginalis depending on clinical sings , direct examination ,culturing and serological test
...Show More Authors

The adequacy of diagnostic tests, together with trichomoniasis associated clinical symptoms, were investigated in females suffering vaginitis, and they were referred to the Gynecology Department, Al-Yarmouk Teaching Hospital during the period December 2004 – June 2005. The total number of patients was 250 cases (age range: 18 - 52 years), and each patient was examined using a sterile speculum to obtain vaginal swabs for examination. The diagnosis with T. vaginalis was done in many methods. The direct methods included wet and stained (Leishman's stain) examinations and cultivation in different culture media (Kupferberg Trichomonas Broth Base;, Trichomonas Agar Base; TAB and Trichomonas Modified CPLM), while the indirect methods were serol

... Show More
View Publication Preview PDF
Crossref (1)
Crossref
Publication Date
Wed Feb 29 2012
Journal Name
Al-khwarizmi Engineering Journal
Effect of Fuel Cetane Number on Multi-Cylinders Direct Injection Diesel Engine Performance and Exhaust Emissions
...Show More Authors

Due to the energy crisis and the stringent environmental regulations, diesel engines are offering good hope for automotive vehicles. However, a lot of work is needed to reduce the diesel exhaust emissions and give the way for full utilization of the diesel fuel’s excellent characteristics.

A kind of cetane number improver has been proposed and tested to be used with diesel fuel as                 ameans of reducing exhaust emissions. The addition of (2-ethylhexyl nitrate) was designed to raise fuel cetane number to three stages, 50, 52 and 55 compared to the used conventional diesel fuel whose CN was 48.5. The addition of CN improver results in the decre

... Show More
View Publication Preview PDF
Publication Date
Sat Sep 28 2024
Journal Name
Journal Of International Dental And Medical Research
Effect of Air–Particle Abrasion of Dentin Surface on Shear Bond Strength of Lithium Disilicate to Dentin Using Three Different Cements
...Show More Authors

This study aims to evaluate the influence of the air abrasion of dentin on the shear bond strength of lithium disilicate using three different types of luting cements. Sixty cylindrical specimens were milled from lithium disilicate CAD/CAM blocks (IPSe.max CAD). Sixty sound human maxillary premolar teeth were decoronated to the level of peripheral dentin, then randomly divided into three groups according to the type of luting cement used for the cementation of the lithium disilicate specimens (n = 20); Group A: Glass ionomer cement (Riva Self- Cure); Group B: Adhesive resin cement (Rely X Ultimate); Group C: Self-adhesive resin cement (Rely X U200). Each group was then further subdivided into two subgroups (n=10); Subgroups AI, BI, and CI,

... Show More
Preview PDF
Scopus
Publication Date
Thu Dec 01 2011
Journal Name
Journal Of Engineering
MECHANISTIC EVALUATION OF LIME-MODIFIED ASPHALT CONCRETE MIXTURES
...Show More Authors

Frequently, Load associated mode of failure (rutting and fatigue) as well as, occasionally, moisture damage in some sections poorly drained are the main failure types found in some of the newly constructed road within Baghdad as well as other cities in Iraq. The use of hydrated lime in pavement construction could be one of the possible steps taken in the direction of improving pavement performance and meeting the required standards. In this study, the mechanistic properties of asphalt concrete mixes modified with hydrated lime as a partial replacement of limestone dust mineral filler were evaluated. Seven replacement rates were used; 0,0.5, 1, 1.5, 2, 2.5 and 3 percent by weight of aggregate. Asphalt concrete mixes were prepared at their

... Show More
View Publication Preview PDF
Crossref
Publication Date
Mon Jun 01 2020
Journal Name
Journal Of Engineering
Effect of Biopolymer Alginate on some properties of concrete
...Show More Authors

Alginate from Large brown seaweeds act as natural polymer has been investigated as polymer and has been added to concrete in different percentages ( 0% , 0.5% , 1% and 1.5% ) by the cement weight and the study show the effect of using alginate biopolymer admixtures on  some of the fresh properties of the concrete (slump &  the density  fresh) also in the hardened state (  Compressive strength , Splitting tensile strength  and Flexural strength ) at 28 days. The mix proportion was (1:2.26:2.26) (cement: sand: gravel) respectively and at constant w/c equal to 0.47. The results indicate that the use of alginate as a percent of the cement weight possess a positive effect on fresh properties of co

... Show More
View Publication Preview PDF
Crossref (7)
Crossref