Self-compacted concrete (SCC) is a highly flowable concrete, with no segregation which can be spread into place by filling the structures framework and permeate the reinforcement without any compaction or mechanical consolidation ACI 237R-14. One of the most important problems faced by concrete industry in Iraq and Gulf Arab land is deterioration due to internal sulfate attack (ISA) that causes damage of concrete and consequently reduces its compressive strength, increases expansion and may lead to its cracking and destruction. The experimental program was focused to study two ordinary Portland cements with different chemical composition with (5, 10 and 15) % percentage of high reactivity metakaoline (HRM) as a cement replacement and with W/Cm ratio 0.35. The SCC mixes with AL Shemalia OPC cement that produced in Saudi Arabia (C3 A=7.02%) shows higher resistance to ISA than mixes with Tasluja OPC cement that is produced in Iraq (C3 A=4.13%). The results indicate that the SCC mixes containing 15% HRM shows higher opposition to ISA. A good correlation was obtained between concrete splitting tensile strength and compressive strength from the results of this study.
The aim of the current research is to identify the self-control of kindergarten teachers as well as to identify the significance of the differences according to a variable (years of service, academic achievement, specialization). Its final paragraphs consist of (35) paragraphs, and its psychometric properties were verified and the tool was applied to a sample of (400) teachers chosen randomly from kindergarten teachers affiliated to the General Directorates of Education in Baghdad, Rusafa, and Karkh for the academic year 2019-2020
In light of the objectives of the current research, the following results were reached
- The current research sample is from kindergarten teachers with self-contro
- There are diffe
Indium Antimonide (InSb) thin films were grown onto well cleaned glass substrates at substrate temperatures (473 K) by flash evaporation. X-ray diffraction studies confirm the polycrystalline of the films and the films show preferential orientation along the (111) plane .The particle size increases with the increase of annealing time .The transmission spectra of prepared samples were found to be in the range (400-5000 cm-1 ) from FTIR study . This indicates that the crystallinity is improved in the films deposited at higher annealing time.
The current study designed to determine the effect of Glucosamine sulfate on the liver tissue of Albino mice .the study included (40)mice divided in to 4 groups(control group had distilled water orally ).The other groups treated with(1000,2000,3000)ml/k .respectively for 8 week .the liver have been taken from dissected animal for microscopic preparation to study the histological changes .Frequently histopathologicale changes appeared in the liver tissue of the exposure groups during (4-8)week .This changes depends on (Dose and Time ). The effects were Congestion ,Infiltration ,Swelling ,Vaculation ,Hyalinization , Amyloid and Necrosis.
The current study designed to determine the effect of Glucosamine sulfate on the liver tissue of Albino mice .the study included (40)mice divided in to 4 groups(control group had distilled water orally ).The other groups treated with(1000,2000,3000)ml/k .respectively for 8 week .the liver have been taken from dissected animal for microscopic preparation to study the histological changes .Frequently histopathologicale changes appeared in the liver tissue of the exposure groups during (4-8)week .This changes depends on (Dose and Time ). The effects were Congestion ,Infiltration ,Swelling ,Vaculation ,Hyalinization , Amyloid and Necrosis.
This paper reports on the experimental study, which conducted a series of triaxial tests for the asphalt concrete using hydrated lime as a mineral additive. Three HMA mixes, prepared by the specification for wearing, levelling and base layers, were studied under three different temperatures. The test results have demonstrated that, compared with the control mixes excluding HL, the permanent deformation resistance of the HL modified mixes has significant improvement. The deformation has been reduced at the same load repetition number, meanwhile the flow number has been considerably increased. The degree of improvement in permanent deformation resistance using HL is more pronounced at high stress deviation states and high temperature.
... Show More
(11)
(11)
Bendable concrete, also known as Engineered Cementitious Composite (ECC) is a type of ultra-ductile cementitious composites reinforced with fibres to control the width of cracks. It has the ability to enhance concrete flexibility by withstanding strains of 3% and higher. The properties of bendable concrete mixes (compressive strength, flexural strength, and drying shrinkage) are here assessed after the incorporation of supplementary cementitious materials, silica fume, polymer fibres, and the use of ordinary Portland cement (O.P.C) and Portland limestone cement (IL). Mixes with Portland limestone cement show lower drying shrinkage and lower compressive and flexural strength than mixes with ordinary Portland cement, due to the ratio o
... Show MoreNatural fibers and particles reinforced composites are being broadly used due to their bio and specific properties such as low density and easy to machine and production with low cost. In this work, water absorption and mechanical properties such as tensile strength, flexural strength and impact strength of recycled jute fibers reinforced epoxy resin were enhanced by treating these fibers with alkaline solution. The recycled jute fibers were treated with different concentration of (NaOH) solution at (25 0C) for a period of (24) hours. From the obtained results, it was found that all these properties are improved when fibers treated with (7.5wt% NaOH) related to untreated fibers. Conversely, the mentioned properties of composit
... Show More
This study investigates the possibility of using waste plastic as one of the components of expired lead-acid batteries to produce lightweight concrete. Different percentages of lead-acid battery plastic were used in the production of lightweight concrete. The replacements were (70, 80 and 100%) by volume of the fine and coarse aggregate. Results demonstrated that a reduction of approximately 23.6% to 35% in the wet density was observed when replacement of 70% to 100% of the natural aggregate by lead-acid battery plastic. Also, the compressive strength decreased slightly with the increase in plastic content at different curing ages of 7, 28, 60, 90, 120 days. The lowest value of compressive strength was (20.7 MPa) for (wa
... Show More
(1)
Low bearing capacity of weak soil under shallow footings represents one of construction problems.
Kaolin with water content converges to liquid limit used to represent the weak soil under shallow
footing prototype. On the other hand, fly ash, which can be defined as undesirable industrial waste
material, was used to improve the bearing capacity of the soft soil considered in this research. The soft
soil was prepared in steel box (36×36×25) cm and shallow square footing prototype (6×6) cm were
used .Group of physical and chemical tests were conducted on kaolin and fly ash. The soft soil was
improved by a bed of compacted fly ash placed under the footing with dimensions equal to that of