In this work, a composite material was prepared from Low-density polyethylene (LDPE) with different weight percent of grain and calcinations kaolin at temperature of (850^oC) using single screw extruder and a mixing machine operated at a temperature between (190-200^oC). Some of mechanical and physical properties such as tensile strength, tensile strength at break, Young modulus, and elongation at break, shore hardness and water absorption were determined at different weight fraction of filler (0, 2, 7, 10 and 15%). It was found that the addition of filler increases the modulus of elasticity, elongation at break, shore hardness and impact strength; on other hand, it decreases the tensile strength and tensile strength

Denture bases are fabricated routinely using Poly(methyl methacrylate) (PMMA) acrylic resin. Yet, it is commonly known for its major drawbacks such as insufficient strength and ductility. The purpose of this study was to improve the performance of PMMA acrylic resin as a denture base material by reinforcement with surface treated lithium disilicate glass ceramic powder. The ceramic powder was prepared by grinding and sieving IPS e.max CAD MT blocks. Then, the powder was surface treated with an organosilane coupling agent (TMSPM) and added to PMMA in amount of 1%, 3%, 5% and 7% by weight. Characterizations of the powder was done by particle size analysis, XRD and FTIR. Transverse strength, Impact strength, Shore D hardness and surface roughn

Collaborative learning is a way that prepares students practically for real-world applications. Working together as teamwork to execute various writing skills is essential in most professions since it increases the level of experience. Thus, the current study aims to identify the role collaborative writing in developing students' level of performance in writing. It is qualitative in nature since the researcher depended on the extant literature in achieving the objective of the study. The researcher touched upon related theories that addressed Collaborative learning, categories, and problems .It concluded that collaborative writing increases the students’ self-confidence, self-esteem, creativity, and motivation through the interact

The increasing discharge of dye-containing wastewater has become a serious environmental problem, requiring efficient and sustainable treatment technologies. In this study, poultry litter–derived biochar (BC) was prepared via pyrolysis at 550 °C and subsequently modified with chitosan to produce a composite adsorbent (BC/CS) for the removal of Congo Red (CR) from aqueous solutions. The materials were characterized using SEM, BET, XRD, FTIR, and XPS analyses. BET results showed that chitosan modification slightly decreased the specific surface area from 8.28 to 8.18 m²/g and pore volume from 0.035 to 0.030 cm³ /g, while introducing abundant amine and hydroxyl functional groups on the surface. Maximum adsorption occurred at pH 3, w

To evaluate the bioactivity and the cytocompatibility of experimental Bioglass-reinforced polyethylene-based root-canal filling materials. The thermal properties of the experimental materials were also evaluated using differential scanning calorimetry, while their radiopacity was assessed using a grey-scale value (GSV) aluminium step wedge and a phosphor plate digital system. Bioglass 45S5 (BAG), polyethylene and Strontium oxide (SrO) were used to create tailored composite fibres. The filler distribution within the composites was assessed using SEM, while their bioactivity was evaluated through infrared spectroscopy (FTIR) after storage in simulated body fluid (SBF). The radiopacity of the composite fibres and their thermal properties were

In this work, functionally graded materials were synthesized by centrifugal technique at different
volume fractions 0.5, 1, 1.5, and 2% Vf with a rotation speed of 1200 rpm and a constant rotation time, T
= 6 min . The mechanical properties were characterized to study the graded and non-graded nanocomposites
and the pure epoxy material. The mechanical tests showed that graded and non-graded added alumina
(Al2O3) nanoparticles enhanced the effect more than pure epoxy. The maximum difference in impact strength
occurred at (FGM), which was loaded from the rich side of the nano-alumina where the maximum value was
at 1% Vf by 133.33% of the sample epoxy side. The flexural strength and Young modulus of the fu