In this work, PAni nanofibers (NFs) are successfully synthesized via hydrothermal method. The structural, surface morphological, optical, electrical and H2S gas sensing properties have been investigated for PAni thin films deposited by spin coating technique. The XRD pattern reveals crystalline nature of PAni NFs with crystallite size of 9.2 nm. The SEM image of Polyaniline clearly indicates that the polymer possesses nanofiber like structure. The optical properties show that the optical energy gap follows allowed direct electronic transition calculated using Tauc’s equation. Intense hotoluminescence (PL) peaks at 309, 340 and 605 nm are observed. The electrical properties such as D.C. conductivity and Hall effect have been studied wher

New microphotometer was constructed in our Laboratory Which deals with the determination of Molybdenum (VI) through its Catalysis effect on Hydrogen peroxide and potasum iodide Reaction in acid medium H2SO4 0.01 mM. Linearity of 97.3% for the range 5- 100 ppm. The repeatability of result was better than 0.8 % 0.5 ppm was obtanined as L.U. (The method applied for the determination of Molybdenum (VI) in medicinal Sample (centrum). The determination was compared well with the developed method the conventional method.

     Pumpkin waste powder was used as a coloring and strengthening filler in epoxy to prepare a natural gelcoat . The Pumpkin powder was mixed with different weight ratios (1, 2, 3, 4, 5, 6, 7, and 8%) to the epoxy matrix to select the best value of powder addition. The effect of the pumpkin particle size on the mechanical properties (impact, flexural, hardness, and wear loss) using two different sizes (2.5 and 1.25 microns) was studied. The impact strength increased from (10.09 KJ/ m²) for neat epoxy to (14.79 KJ/ m²) for epoxy with  1% of micron pumpkin fibers ( MPF) with particle size 2.5 micrometer and (14.21 KJ/ m²) for epoxy with 4% (1.25 MPF), flexural strength increased from (41.94 MPa) for n

The dialogue considers a method and life curriculum help to solve many problems as well as the best way to build a healthy family setting supports the growth of children and leads to the formation sound, strong and positive character. It also supports the family relationship. many of family members needs may achieve through what prevails among them such as continuing a comprehensive and deep combines word, deed and feeling it enters the body and soul . So each part strengthens by the other part and exchanges effect The deep domestic dialogue opens hearts between parents and children  Family increases more loving , intimacy , honesty and happiness. So the domestic dialogue became an urgent necessity in the light of many socia

Two simple, rapid, and useful spectrophotometric methods were suggest or the determination of sulphadimidine sodium (SDMS) with and without using cloud point extraction technique in pure form and pharmaceutical preparation. The first  method was based on  diazotization of the Sulphdimidine Sodium drug by sodium nitrite at 5 ºC, followed by coupling with α –Naphthol in basic medium to form an orange colored product . The product was stabilized and its absorption was measured at 473 nm. Beer’s law was obeyed in the concentration range of (1-12) μg∙ml^-1. Sandell’s sensitivity was 0.03012 μg∙cm^-1, the detection limit was 0.0277 μg∙ml^-1, and the limit of Quantitation was 0.03605μg

   For extraction chloro anion complexes of Cd2+ and Hg2+ used many organic agents as extractant according to liquid ion exchange method such as α-Naphthyl amine (α-NA), 4-Amino benzoic acid (4-ABA), 2-[(4-Carboxy methyl phenyl) azo]-4,5-diphenyl imidazole (4CMePADPI) and Cryptand (C222). This study includes definition hydrochloric acid concentration in aqueous phase and shaking with organic phase necessary for extraction as well as shaking time, organic solvent effect, interferences and alkaline salt effect. Thermodynamic showed the ion exchange reaction was exothermic for α-NA, C222 and endothermic for 4-ABA, 4-CMePADPI for extraction CdCl4=, but for extraction HgCl4= was exothermic with 4-ABA, 4CMePADPI and C222 but

During the last two decades, nanomaterial application has gained a significant attraction into asphalt technology due to their effect in enhancing asphalt binder improving the asphaltic mixture. This study will modify the asphalt binder with two different nano types, nano SiO2 and CaCO3, at levels ranging from 1% to 7%. The resulting optimum nano-modified Asphalt will be subject to a series of rheological tests, including dynamic shear rheometer (DSR), Viscosity, and bending beam rheometer (BBR) to determine asphalt binder sensitivity towards low-medium-high temperature range. Results indicate that both nano types improved the physical characteristics of Asphalt, and 5% by weight of Asphalt was suggested as a reasonable dosage of nano-SiO2

Model birefringence was measured for elliptical-core fibers with low ellipticities, note the birefringence depends strongly on the frequency, especially when fiber is being operated near the higher mode cutoff where ν  for circular fiber of the single-mode type that correspond to the birefringence maximum. When ν  this also correspond to the birefringence maximum that can be introduced in an elliptical core fiber while still operating in the single-mode regime near the higher mode cutoff. Also the birefringence is proportional to the fiber core ellipticity when core ellipticity is much less than unity, but this birefringence deviates from the linear for the large core ellipticities.

In this work, electrochemical process was presented to polymerized eugenol on Gr.2 and Gr.5 titanium alloys before and after treated by Micro Arc Oxidation (MAO), where Gr.2 is commercial pure titanium and Gr.5 is Ti-6Al-4V dental alloys. The deposited layers were characterized by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FTIR). The adhesion strength of polymeric thin-film was estimation by using pull-off adhesion test and the result was the adhesion strength of PE was (1.23 MPa) on Gr.2 before MAO and increase to (1.98 MPa) on Gr.2 after MAO treatment. The corrosion behavior of Gr.2 and Gr.5 alloy in artificial saliva environment at

This research has presented a solution to the problem faced by alloys: the corrosion problem, by reducing corrosion and enhancing protection by using an inhibitor (Schiff base). The inhibitor (Schiff base) was synthesized by reacting of the substrates materials (4-dimethylaminobenzaldehyde and 4-aminoantipyrine). It was diagnosed by infrared technology IR, where the IR spectrum and through the visible beams proved that the Schiff base was well formed and with high purity. The corrosion behavior of carbon steel and stainless steel in a saline medium (artificial seawater 3.5%NaCl) before and after using the inhibitor at four temperatures: 20, 30, 40, and 50 C° was studied by using thr