The investigation of the effect of tempering on thermal analysis of
Al-Ti-Si alloy and its composites with MgO and SiC particles was
performed. Thermal analysis was performed before and after
tempering by DSC scan. Optical microscopy was used to identify the
phases and precipitations that may be formed in base alloy and
composites. X-ray diffraction test indicated that the Al3Ti is the main
phase in Al-Ti-Si alloy in addition to form Al5Ti7Si12 phase. Some
chemical reactions can be occurred between reinforcements and
matrix such as MgO.Al2O3 in Al-Ti/MgO, and Al4C3 and Al(OH)3 in
Al-Ti/SiC composite. X-ray florescence technique is used to
investigate the chemical composition of the fabricated specimens.
H

Purpose of research: The purpose of the article is to conduct a comparative analysis of the concept and types of puns in the Russian and Arabic languages. The main focus is on identifying similarities and differences in the definition of a pun, as well as analyzing its various types in both languages. The purpose of the study is to understand how puns are used to achieve comic or semantic effect in different cultural contexts.

Methods: The study includes an analysis of literature providing information about puns in Russian and Arabic. For comparative analysis, methods were used to compare concepts, definitions and types of puns in both languages. The phonetic, semantic and syntactic aspects of the pun are considered,

     Hyperbole is an obvious and intentional exaggeration in the sense that it takes things to such an extreme that the audience goes too far and then pulls itself back to a more reasonable position, i.e. it is an extravagant statement or figure of speech not intended to be taken literally. This paper focuses on the formal and functional perspectives in the analysis of hyperbole which American candidates produce in their speeches in electoral campaigns, for it is hypothesized that candidates in their electoral campaigns use hyperbolic expressions excessively to persuade voters of the objectives of their electoral campaign programs. Hence, it aims to analyze hyperbole in context to determine the range of pragmatic func

This paper investigates the experimental response of composite reinforced concrete with GFRP and steel I-sections under limited cycles of repeated load. The practical work included testing four beams. A reference beam, two composite beams with pultruded GFRP I-sections, and a composite beam with a steel I-beam were subjected to repeated loading. The repeated loading test started by loading gradually up to a maximum of 75% of the ultimate static failure load for five loading and unloading cycles. After that, the specimens were reloaded gradually until failure. All test specimens were tested under a three-point load. Experimental results showed that the ductility index increased for the composite beams relative to the reference specim

An experimental program was conducted to determine the residual of composite Steel Beams-Reinforced Concrete (SB-RC) deck floors fabricated from a rolled steel beam topped with a reinforced concrete slab, exposed to high temperatures (fire flame) of 300, 500, and 700ºC for 1 hour, and then allowed to cool down by leaving them in the lab condition to return to the ambient temperature. The burning results showed that, by exposing them to a fire flame of up to 300ºC, no serious permanent deflection occurred. It was also noticed that the specimen recovered 93% of 19.2 mm of the deflection caused by burning. The recovered deflection of burned composite SB-RC deck floor at 500ºC was 40% of 77.9 mm of the deflection caused by burning with a res

This paper investigates the experimental response of composite reinforced concrete with GFRP and steel I-sections under limited cycles of repeated load. The practical work included testing four beams. A reference beam, two composite beams with pultruded GFRP I-sections, and a composite beam with a steel I-beam were subjected to repeated loading. The repeated loading test started by loading gradually up to a maximum of 75% of the ultimate static failure load for five loading and unloading cycles. After that, the specimens were reloaded gradually until failure. All test specimens were tested under a three-point load. Experimental results showed that the ductility index increased for the composite beams relative to the refe