Eight soil samples were selected around Najaf governorate at depth levels 40-50 cm. X-Ray Fluorescence (XRF) was used to determine the concentrations of major and trace elements. Liner and mass attenuation coefficient (µ, µ_ρ) have been determined at gamma energies (662, 1172,1332) keV using NaI (Tl) detector. The range of linear attenuation coefficients for calculated samples were (0.553-1.163) cm^-1, (0.122-0.178) cm^-1 and (0.049-0.105) cm^-1 at (662, 1172,1332) keV respectively. The range of mass attenuation coefficients obtained (0.39-0.76) cm²/gm, (0.087-0.117) cm²/gm and (0.0336-0.074) cm²/gm at (662, 1172,1332) keV respectively. The result

The deprivation Some of the children to exercise some fine motor activities a big problem , as a consequence, this problem plays of the delay in motor development during early childhood , Usually it happens to be the reasons for the lack of the right place to play , and the lack of the presence of the tools needed to play motor, or fear excessive protection by parents for their children as a result of lack of awareness of the importance of physical activity for the child to use his fingertips and fine his muscles . In addition to that small percentage of children spend most of their time in the daily activities and skills of non-motor , Such aswatching television, or play video games or they tend to play computer and mobile but they are

The -mixing of  - transition in Er 168 populated in  Er(n,n ) Er 168 168  reaction is calculated in the present work by using a2- ratio method. This method has used in previou studies [4, 5, 6, 7] in case that the second transition is pure or for that transition which can be considered as pure only, but in one work we applied this method for two cases, in the first one for pure transition and in the 2nd one for non pure transitions. We take into accunt the experimental a2- coefficient for previous works and -values for one transition only [1]. The results obtained are, in general, in agood agreement within associated errors, with those reported previously [1], the discrepancies that occur are due to in

Background: Ameloblastoma is the most common clinically significant odontogenic tumor, known for its locally invasive potential and frequent recurrences unless treated radically. Endocan is a soluble proteoglycan which is reported to have prognostic implications in multiple human diseases and tumors. This study aims to describe the expression of endocan in ameloblastoma. Materials and methods: With immunoperoxidase method; tissue sections of formalin fixed- paraffin embedded blocks for ameloblastomas were stained with monoclonal antibodies to endocan, the localization of the endocan expression was examined and the resulting scores of the tissue sections were analyzed according to age, sex, site and tumor subtype. Results: endocan was found

The isomerization of n-hexane on platinum loaded acidic zeolite was studied at atmospheric pressure, H2/nC6 molar ratios of 1-4 and temperature range of 240-270ºC. The measured kinetic data were fitted to an equation based on the bifunctional mechanism and by using independently obtained dehydrogenation and adsorption data. The activation energies of protonation (ΔHpro) and the elementary isomerization step (Eact,iso) and as well as the corresponding preexponential factor were simultaneously determined. The observed values of both ΔHpro and Eact,iso are in agreement with the results of quantum-chemical calculations.

0

The corrosion inhibition of aluminum alloy 5083 by an environment friendly compound called (8- Hydroxyquinoline) in
acidic and alkaline solutions of pH (2 and 12) respectively were studied using weight loss and polarization techniques.
Also to examine the main and combined effects of the inhibitor concentration, pH, and contact time using factorial
experimental design. Results show that corrosion rate decreased with increasing both inhibitor concentration and
contact time and increased with increasing pH value. The polarization curves show that 8-hydroxyquinoline is a
cathodic inhibitor

GaN thin films were deposited by thermal evaporation onto
glass substrates at substrate temperature of 403 K and a thickness of
385 nm . GaN films have amorphous structure as shown in X-ray
diffraction pattern . From absorbance data within the range ( 200-
900 ) nm direct optical energy gap was calculated . Also the others
optical parameters like transmittance T, reflectance R , refractive
index n , extinction coefficient k , real dielectric constant 1 Î , and
imaginary dielectric constant 2 Î were determined . GaN films
have good absorbance and minimum transmittance in the region of
the visible light .