The cost-effective carbon cross-linked Y zeolite nanocrystals composite (NYC) was prepared using an eco-friendly substrate prepared from bio-waste and organic adhesive at intermediate conditions. The green synthesis method dependent in this study assures using chemically harmless compounds to ensure homogeneous distribution of zeolite over porous carbon. The greenly prepared cross-linked composite was extensively characterized using Fourier transform infrared, nitrogen adsorption/desorption, Field emission scanning electron microscope, Dispersive analysis by X-ray, Thermogravimetric analysis, and X-ray diffraction. NYC had a surface area of 176.44 m2/g, and a pore volume of 0.0573 cm3/g. NYC had a multi-function nature, sustained at a long-

Fabrication of porous clay refractory insulating specimens from Iraqi kaolin with different percentage of Expanded Polystyrene (EPS) waste crumbs additions were investigated. After mixing and forming by hand molding, the specimens was dried and fired at 1300 oC. The structural, physical, mechanical and thermal properties of the refractory insulating products were measured. Maximum addition of EPS (1.25 wt%) lead to reduce the linear shrinkage to less than 1.7% and increased apparent porosity up to 50 %. As well as, the density, Modulus of rupture and thermal conductivity were reduced to 1.39 g/cm3, 4.1 MPa and 0.21 W/m.K, respectively. The final outcome, addition of EPS showed good results in the formation of pores without distorting the

This study focuses on diagnosis of Candida species causing Vulvovaginal Candidiasis using phenotype and genotype analyzing methods, and frequencies of candida species also using Vulvovaginal Candidiasis patients. 130 samples (100 from patients and 30 from non infected women) were collected and cultured on biological media. Identifying the yeasts, initially some phenotypic experiments were carried out such as germ tube, from motion of pseudohyphae and clamydospores in CMA+TW80 medium, API20 candida and CHROMagar Candida. Genomic DNA of all species were extracted and analyzed with PCR and subsequent Polymerase Chain Reaction - Restriction Fragments Length Polymorphism (PCR-RFLP) methods. Frequency of C. albicans, C. krusei, C. tropicalis , C.

Bentonite is widely used in industrial applications. The present study reports the effect of adding different weights of ZnO to the Iraqi bentonite, on surface area, pore volume and real density. These surface properties were evaluated for pure and modified bentonite. The modification was made by adding different ZnO weights such as; ( 0.5%, 1%, 5%, 10% ). The effect of heat exposing for all modified clay samples at 500 ?C have been also evaluated. The results show that the addition of 0.5% ZnO leads to increase the surface area percentage about 36%, increase pore volume percentage about 5.48% and increase the real density percentage about 27.116%. When the samples exposed to 500 ?C, their surface area and pore volumes have been decreased a

The adsorption ability of Iraqi initiated calcined granulated montmorillonite to adsorb of 4-(4-Nitrobenzeneazo) 3-Aminobenzoic Acid from aqueous solutions has been investigated through columnar method. The azo dye adsorption found to be dependent on adsorbent dosage, initial concentration and contact time. All columnar experiments were carried out at three different pH values (5.5, 7and 8) using buffer solutions at flow rate of (3 drops/ min.), at room temperature (25±2) °C. The experimental isotherm data were analyzed using Langmuir, Freundlich and Temkin equations. The monolayer adsorption capacity is 6.4066 mg Azo ligand per 1g calcined Montmorillonite. The experiments showed that highest removal rate 90.5 % for azo dye at pH 5.5.The

Electrochemical oxidation in the presence of sodium chloride used for removal of phenol and any other organic by products formed during the electrolysis by using MnO2/graphite electrode. The performance of the electrode was evaluated in terms fraction of phenol and the formed organic by products removed during the electrolysis process. The results showed that the electrochemical oxidation process was very effective in the removal of phenol and the other organics, where the removal percentage of phenol was 97.33%, and the final value of TOC was 6.985 ppm after 4 hours and by using a speed of rotation of the MnO2 electrode equal to 200 rpm.

The present study provides a new insight into valuable information on the diverse structure of the Anisakid population and discusses the limited species richness in the Nemipterus japonicus (Bloch,1791) (Perciformes, Nemiperidae). The fishing area consists of various locations in the Arabian Gulf (29°58 0 33 00 N48°28 0 20 E). A total of 315 marine fish were examined, (n=287) were infected. Larval stages (n= 763) encysted within the mesenteries peritoneum and viscera of fish organs were isolated, with a prevalence of 91.11% of infection and, the intensity was 2.65. Molecular analysis was carried out on thirty individuals who have examined the morphology and showed some appearance differences, by amplifying internal transcribed spacers

Natural bentonite (B) mineral clay was modified by anionic surfactant sodium dodecyl sulfate (SDS) and characterized using different techniques such as: FTIR spectroscopy, scanning electron microscopy (SEM) and X-Ray diffraction (XRD). The bentonite and modified bentonite were used as adsorbents for the adsorption of methyl violet (MV) from aqueous solutions. The adsorption study was carried out at different conditions such as: contact time, pH value and adsorbent weight. The adsorption kinetic described by pseudo– first order and pseudo – second order equilibrium experimental data described by Langmuir, Freundlich and Temkin isotherm models. The thermodynamic parameters standard free energy ( ), standard entropy ( ) standa

Cement-based adhesive (CBA) is used as a bonding agent in Carbon Fibre Reinforced Polymer (CFRP) applications as an alternative to epoxy-based adhesive due to the drawbacks of the epoxy system under severe service conditions which negatively affect the bond between the CFRP and strengthened elements. This paper reports the results of, an investigation carried out to develop two types of CBA using magnetized water (MW) for mixing and curing. Two magnetic devices (MD-I and MD-II), with different magnetic field strengths (9000 and 6000 Gauss) respectively, were employed for water magnetization. Different water flows with different water circulation times in the magnetizer were used for each device. Compressive and splitting tensile strength te