High temperature superconductors materials with composition Bi1.6-xSbxPb0.4Sr2Ca2-yCdyCu3OZ (x = 0, 0.1, 0.2 and 0.3) and (y = 0.01 and 0.02), were prepared by using the chemical reaction in solid-state ways, and test influence of partial replacement of Bi and Ca with Sb and Cd respectively on the superconducting properties, all samples were sintered at the same temperature (850 oC) and for the same time (195 h). The structural analysis of the prepared samples was carried out using X-ray diffraction (XRD) measurements performed at room temperature, scanning electron microscope (SEM) and dc electrical resistivity was measured as a function of temperature. It was found that the sample prepared by partial substitution of Sb at ratio (x= 0.2

This study investigates the ionic conduction dependence on the size of alkaline cations in gel polymer electrolytes based on double iodide can enhance by incorporating a salt having a bulky cation.

This study was conducted according to contract with the North Refineries Company-Baiji and deals with the hydrodesulphurization of vacuum gas oil of Kirkuk crude oil, boiling range 611-833 K. A trickle bed reactor packed with a commercial cobalt-molybdenum on alumina catalyst was used. The operating conditions were: temperature range 583-643 K, liquid hourly space velocity range 1.50-3.75 1/h, hydrogen to oil ratio about 250 l/l and pressure kept constant at 3.5MPa.
The results showed that the aromatic content decreased and sulfur removal increased with increasing temperature and decreasing space velocity. The properties (viscosity, density, flash point and carbon residue) of the products decrease with temperature increasing, but the

To assess the effects of dietary oil sources on productive and reproductive traits, sunflower oil, flax oil, corn oil, or fish oil were induced in quail diets. One hundred and sixty-eight 7-week-old Japanese quail were randomly assigned to 4 groups (12 males and 30 females each) with 3 replicates per group containing 4 males and 10 females each and fed for 13 weeks (including one week as an adaptation period) on a commercial diet supplemented with 3% of sunflower oil (T1), flax oil (T2), corn oil (T3), or fish oil (T4). The birds received water and were fed ad libitum during the study. The results of the experiment revealed that dietary supplementation with different sources of oil had no significant effect on male body weight, female body

Abstract: This paper presents the results of the structural and optical analysis of CdS thin films prepared by Spray of Pyrolysis (SP) technique. The deposited CdS films were characterized using spectrophotometer and the effect of Sulfide on the structural properties of the films was investigated through the analysis of X-ray diffraction pattern (XRD). The growth of crystal became stronger and more oriented as seen in the X-ray diffraction pattern. The studying of X-ray diffraction showed that; all the films have the hexagonal structure with lattice constants a=b=4.1358 and c=6.7156A°, the crystallite size of the CdS thin films increases and strain (ε) as well as the dislocation density (δ) decreases. Also, the optical properties of the

The present study aimed to investigate effect of Pregabalin (PGB) on ovary tissue and number of follicles in female albino rats. Three groups of healthy adult female albino rats, fifteen rats in each group were used in current study. The rats of groups, G2 and G3 were administered orally with two doses 150 mg and 300mg/kg b.wt/day of pregabalin, respectively. The doses were given daily for 1 month, 2 months, and 3 months. Animals of group G1 (Control) were given saline alone. After the experimental periods, the rats were sacrificed and the isolated ovaries were histologically examined. The results of histological analysis of the ovaries in treated rats (G2, and G3) showed a significant (P≤0.05) decrease in the number of preantral, antral,

This work aim to study the effect of silver nanoparticles on fluorescence intensity of Coumarin 480 dye by using the sandwiches technique where AgNP layer had been separated from C480 layer by different type of materials such as silica, PMMA polymer and PVA polymer layer. Silver nanoparticles had been prepared by the chemical reduction method so the AgNP layer coating had been done by hot rotation liquid method. The optical properties of prepared samples had been tested by using UV-VIS absorption spectrophotometer and Fluorescence spectrophotometer. Morphology, average size and the structure of nanoparticles were estimated using AFM, SEM testes

Permanent magnets of different intensities were used to investigate the effect of a magnetic field in the process of preventing deposits of calcium carbonate. The magnets were fixed on the water line from the tap outside. Then heating a sample of this water in flasks and measuring the amount of sediment in a manner weighted differences. These experiments comprise to the change of the velocity of water flow, which amounted to (0.5, 0.75, 1) m/sec through the magnetic fields that are of magnetic strength (2200, 6000, 9250, 11000) Gauss, and conduct measurements, tests and compare them with those obtained from the use of ordinary water.The results showed the effectiveness of magnetic treatment in reducing the rate of deposition of calcium carb

Moisture induced damage can cause a progressive deterioration in the performance of asphalt pavement by the loss of adhesion between asphalt binder and aggregate surface and/or loss of cohesion within the binder in the presence of water. The objective of this paper is to improve the asphalt mixtures resistance to moisture by using hydrated lime as an anti-stripping additive. For this purpose, two types of asphalt binder were utilized; asphalt grades (40-50) and (60-70) with one type of aggregate of 19.0 mm aggregate nominal maximum size, and limestone dust as a mineral filler. Marshall method was adopted to find the optimum asphalt content. Essentially, two parameters were determined to evaluate the moisture susceptibili