The varied applications of polystyrene in various fields of life led to examining the cause of radiation influence on some rheological behavior of commercial Polystyrene (PS) solution in the chloroform (CHCl3) solvent. Polystyrene grains shape samples were irradiated using the radioactive element Cesium- 137 with (9 µci) activity for 10, 20, and 30 minutes. The viscosity of the polymer solution depends on the concentration and size (i.e. molecular weight) of the dissolved polymer. Experimental data showed that the radiation dose affected the value of viscosity (shear, relative, specific, and reduced). The viscosity value significantly reduced at 10 min radiation dose and when increasing the dose, the viscosity value increased

In this study three inorganic nano additives, namely; CaCO3, Al2O3 and SiO2 were used to prepare nanocomposites of unsaturated polyester in order to modify their mechanical properties, i.e. tensile strength, elongation, impact and hardness. The results indicated that all the three additives were effective to improve the mechanical properties up to 4% by weight. The effectiveness of them follows the order : CaCO3 > Al2O3 > SiO2 This is due to their particle size in which CaCO3 (13nm), Al2O3 (20-30nm) and SiO2 (15-20nm).

The increase globally fossil fuel consumption as it represents the main source of energy around the world, and the sources of heavy oil more than light, different techniques were used to reduce the viscosity and increase mobility of heavy crude oil. this study focusing on the experimental tests  and modeling with Back Feed Forward Artificial Neural Network (BFF-ANN) of the dilution technique to reduce a  heavy oil viscosity that was collected from the south- Iraq oil fields using organic solvents, organic diluents with different weight percentage  (5, 10 and  20 wt.% )  of  (n-heptane, toluene, and a mixture of  different ratio

Densities ρ and viscosities η for several concentrations of amino acids (Serine, Cysteine and Threonine) at different temperatures (298.15, 303.15 and 308.15K) have been measured. On the basis of these data, the apparent molal volumes v , partial molal volumes at infinite dilution v , slope Sv , Gibbs free energy of activation for viscous flow of solution ∆G1,2 and Jones – Dole Bcoefficients were calculated the nature of solute-solvent and solute-solute interactions have been discussed in terms of the values of v , v , Sv and B-coefficents

A series of overbased magnesium fatty acids such as caprylate, caprate, laurate, myristate, palmitate, stearate and oleate) were synthesized by the reaction of the fatty acids with active – 60 magnesium oxide and carbon dioxide (CO2) gas at 60 oC in the presence of ammonia solution as catalyst, toluene / ethanol solvent mixture (9:1vol/vol) was added.
The prepared detergent additives were characterized by FTIR, 1HNMR and evaluated by blending each additive in various concentrations with medium lubricant oil fraction (60 stock) supplied by Iraqi Midland Refineries Company. The total base number (TBN, mg of KOH/g) was determined, and the results of TBN were treated by using two-way analysis of variance (ANOVA) test. It was found that

Increasing the variety of products that are being designed with sculptured surfaces, efficient machining of these surfaces has become more important in many manufacturing industries. The objective of the present work is the investigation of milling parameters for the sculptured surfacesthat effecting of surface roughness during machining of Al-alloy. The machining operation implemented on C-TEK CNC milling machine. The influence of the selected variables on the chosen characteristics have been accomplished using Taguchi design approach, also ANOVA had been utilized to evaluate the contributionsof each parameter on proc

A hand lay-up method was used to prepare Epoxy/ metal composites. Epoxy resin (EP) was used as a matrix with metal particles (Al, Cu, and Fe) as fillers.
The preparation method includes preparing square panels of composites with different weight percentage of fillers (10, 20, 30, 40, and 50%). Standard specimens (88mm in diameter) for thermal conductivity tests were prepared to measure thermal conductivity kexp.The result of experimental thermal conductivity kexp, for EP/metal composites show that, kexp increase with increasing weight percentage, For EP/ Al and EP/Cu composites, and it have have maximum values of 0.33 and 0.35 W/m.K, respectively. While kexp for EP/ Fe composite show slight increase with maximum value of 0.186 W/m.K.

EP/ metal composites were prepared as adhesives between two steel rods. Epoxy resin (EP) was used as a matrix with metal as fillers (Al, Cu, Fe,).
The preparation method for tensile adhesion tests includes two steel rods with adhesive composites between the rods to measure adhesion strength Sad and adhesion toughness Gad.
Results of tensile adhesion tests show that EP/ metals composite have maximum strength Sad for certain weight percentage of metals 2.95 and 9MPa at 10% for EP/Al and EP/Cu composite and 8.2MPa at 40% for EP/Fe composites